Wear-resistant sole material and preparation method thereof

A technology for sole materials and composite materials, applied in soles, footwear, clothing, etc., can solve problems such as poor compatibility, and achieve excellent wear resistance and corrosion resistance

Inactive Publication Date: 2021-02-19
台州市路桥区静荷纺织有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In the present invention, under the action of dibutyltin dilaurate as a catalyst, the second intermediate is mixed with the dissolved methyl phenyl silicone rubber, and the p-phenyl silicone rubber is modified, through the active siloxy group and active hydrogen A ring-opening reaction occurs, and product two is grafted on methylphenyl silicon, which solves the technical problem of poor compatibility between product one and methylphenyl silicone rubber, and can endow the prepared shoe sole material with excellent corrosion resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant sole material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A wear-resistant sole material, comprising the following raw materials in parts by weight: 30 parts of natural rubber, 20 parts of corrosion-resistant rubber, 30 parts of ethylene-vinyl acetate copolymer, 10 parts of wear-resistant composite materials, 10 parts of phthalates Plasticizer, 1 part lead sulfate tribasic;

[0030] This wear-resistant sole material is made by following method:

[0031]The first step, add natural rubber, corrosion-resistant rubber, ethylene-vinyl acetate copolymer, wear-resistant composite material, phthalate plasticizer and tribasic lead sulfate into the kneader and knead at 100 ° C for 2 hours , to obtain the mixture, and then add the mixture to the masticator to masticate the pull sheet, and control the temperature of mastication to be 120°C to obtain the first sheet material;

[0032] The second step is to add the prepared primary sheet into a hot press to heat and plasticize, foam, shape, and demould to obtain a billet, and then heat and...

Embodiment 2

[0040] A wear-resistant shoe sole material, comprising the following raw materials in parts by weight: 32 parts of natural rubber, 22 parts of corrosion-resistant rubber, 35 parts of ethylene-vinyl acetate copolymer, 14 parts of wear-resistant composite materials, 12 parts of phthalates Plasticizer, 2 parts lead sulfate tribasic;

[0041] This wear-resistant sole material is made by following method:

[0042] The first step, add natural rubber, corrosion-resistant rubber, ethylene-vinyl acetate copolymer, wear-resistant composite material, phthalate plasticizer and tribasic lead sulfate into the kneader and knead at 100 ° C for 2 hours , to obtain the mixture, and then add the mixture to the masticator to masticate the pull sheet, and control the temperature of mastication to be 120°C to obtain the first sheet material;

[0043] The second step is to add the prepared primary sheet into a hot press to heat and plasticize, foam, shape, and demould to obtain a billet, and then h...

Embodiment 3

[0051] A wear-resistant shoe sole material, comprising the following raw materials in parts by weight: 38 parts of natural rubber, 28 parts of corrosion-resistant rubber, 45 parts of ethylene-vinyl acetate copolymer, 18 parts of wear-resistant composite materials, 14 parts of phthalates Plasticizer, 2 parts lead sulfate tribasic;

[0052] This wear-resistant sole material is made by following method:

[0053] The first step, add natural rubber, corrosion-resistant rubber, ethylene-vinyl acetate copolymer, wear-resistant composite material, phthalate plasticizer and tribasic lead sulfate into the kneader and knead at 100 ° C for 2 hours , to obtain the mixture, and then add the mixture to the masticator to masticate the pull sheet, and control the temperature of mastication to be 120°C to obtain the first sheet material;

[0054] The second step is to add the prepared primary sheet into a hot press to heat and plasticize, foam, shape, and demould to obtain a billet, and then h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a wear-resistant sole material and a preparation method thereof. The wear-resistant sole material comprises the following raw materials in parts by weight: 30-40 parts of natural rubber, 20-30 parts of corrosion-resistant rubber, 30-50 parts of an ethylene-vinyl acetate copolymer, 10-20 parts of a wear-resistant composite material, 10-15 parts of a plasticizer and 1-3 partsof a stabilizer. The preparation method comprises the following steps: adding the natural rubber, the corrosion-resistant rubber, the ethylene-vinyl acetate copolymer, the wear-resistant composite material, the plasticizer and the stabilizer into a kneading machine, kneading for 2 hours at the temperature of 80-100 DEG C to prepare a mixture, adding the mixture into a plasticator, plastifying andpulling sheets, and controlling the plastifying temperature to be 100-120 DEG C to prepare a primary sheet material; the active silica group and the active hydrogen are subjected to the ring-openingreaction, and the product 2 is grafted on the methyl phenyl silicon so that the technical problem of poor compatibility between the product 1 and the methyl phenyl silicon rubber is solved, and the prepared sole material can be endowed with excellent corrosion resistance.

Description

technical field [0001] The invention belongs to the technical field of shoe sole material preparation, in particular to a wear-resistant shoe sole material and a preparation method thereof. Background technique [0002] Compared with other foaming materials, PVC foaming materials have the advantages of good mechanical properties, good adhesion, convenient processing, and low cost. With the rising price of raw materials, PVC foam sole materials are becoming more and more popular. Ethylene-vinyl acetate copolymer (EVA) has good plasticity, elasticity and processability, and the foamed material has the advantages of low density, good mechanical properties, and easy coloring. It is widely used in shoe sole materials, but EVA materials It has the disadvantage that the wear resistance is not as good as that of rubber shoe materials, which limits its partial application. However, although the ordinary PVC foam sole material is lighter, it loses wear resistance and affects the serv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L23/08C08L29/04C08L83/10C08K13/02C08K5/053C08K3/30C08K5/12A43B13/04
CPCC08L7/00C08L23/0853A43B13/04C08L2205/035C08K2201/011C08K2003/3045C08L29/04C08L83/10C08K13/02C08K5/053C08K3/30C08K5/12
Inventor 程同恩
Owner 台州市路桥区静荷纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products