Manufacturing process of iron oxide red transmutation glazed porcelain

A production process and kiln changing glaze technology, which can be used in clay products, applications, household appliances, etc., and can solve the problems of harsh firing conditions, difficult commercial production, and narrow crystallization temperature range.

Inactive Publication Date: 2020-08-25
福建省德化县东盛陶瓷有限公司
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its appearance has attracted attention at home and abroad, but due to its narrow crystallization temperature range and harsh firing conditions, it has brought difficulties to commercial production and needs further improvement.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] An iron-red kiln-varnished glazed porcelain includes a body and iron-red glaze.

[0057] The green body includes the following raw materials in parts by weight: 20 parts of Dehua feldspar, 40 parts of Dehua quartz, 18 parts of Dehua kaolin, 18 parts of sillimanite, 8 parts of boronite, 5 parts of boronite, and 5 parts of sphalerite , 8 parts of zinc oxide, 3 parts of zirconia.

[0058] The iron red glaze includes the following raw materials in parts by weight: 10 parts of albite, 35 parts of Dehua quartz, 10 parts of calcite, 8 parts of chalk, 15 parts of magnetite, 15 parts of phosphorite, 25 parts of low-temperature frit, boron magnesium Stone 10 parts.

[0059] The chemical composition of the low temperature frit is as follows: SiO 2 : 52.4%, Al 2 o 3 : 11.7%, CaO: 14.8%, MgO: 6.8%, Li 2 O: 3.9%, ZnO: 5.3%, K 2 O: 2.8%, BaO: 1.2%, La 2 o 3 : 1.1%;

[0060] Its manufacturing process includes the following steps:

[0061] Step 1, weighing ingredients accordin...

Embodiment 2

[0077] An iron-red kiln-varnished glazed porcelain includes a body and iron-red glaze.

[0078] The green body includes the following raw materials in parts by weight: 25 parts of Dehua feldspar, 35 parts of Dehua quartz, 22 parts of Dehua kaolin, 12 parts of sillimanite, 12 parts of boronite, 3 parts of boronite, and 10 parts of sphalerite , 6 parts of zinc oxide, 4 parts of zirconia.

[0079] The iron red glaze includes the following raw materials in parts by weight: 15 parts of albite, 30 parts of Dehua quartz, 12 parts of calcite, 5 parts of chalk, 18 parts of magnetite, 10 parts of phosphorite, 30 parts of low-temperature frit, boron magnesium Stone 5 parts.

[0080] The chemical composition of the low temperature frit is as follows: SiO 2 : 46.3%, Al 2 o 3 : 16.5%, CaO: 10.3%, MgO: 9.6%, Li 2 O: 2.6%, ZnO: 7.2%, K 2 O: 3.7%, BaO: 3.2%, La 2 o 3 : 0.6%;

[0081] Its manufacturing process includes the following steps:

[0082] Step 1, weighing ingredients accordi...

Embodiment 3

[0098] An iron-red kiln-varnished glazed porcelain includes a body and iron-red glaze.

[0099] The green body includes the following raw materials in parts by weight: 22 parts of Dehua feldspar, 38 parts of Dehua quartz, 20 parts of Dehua kaolin, 15 parts of sillimanite, 10 parts of boronite, 4 parts of boronite, and 7 parts of sphalerite , 7 parts of zinc oxide, 3.5 parts of zirconia.

[0100] The iron red glaze includes the following raw materials in parts by weight: 12 parts of albite, 32 parts of Dehua quartz, 11 parts of calcite, 6 parts of chalk, 16 parts of magnetite, 12 parts of phosphorite, 27 parts of low-temperature frit, boron magnesium Stone 8 servings.

[0101] The chemical composition of the low temperature frit is as follows: SiO 2 : 49.5%, Al 2 o 3 : 13.2%, CaO: 13.1%, MgO: 8.1%, Li 2 O: 3.2%, ZnO: 6.4%, K 2 O: 3.3%, BaO: 2.4%, La 2 o 3 : 0.8%;

[0102] Its manufacturing process includes the following steps:

[0103] Step 1, weighing ingredients acc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing process of iron oxide red transmutation glazed porcelain. The iron oxide red transmutation glazed porcelain comprises a green body and an iron oxide red glaze,wherein the green body is prepared from the following raw materials: Dehua feldspar, Dehua quartz, Dehua kaolin, sillimanite, szaibelyite, boehmite, sphalerite, zinc oxide and zirconium oxide. By limiting the composition of the green body and improving the basic formula of the glaze, a plurality of orange plaques with the sizes of broad beans and peas are distributed on the glaze surface of the fired iron oxide red transmutation glazed porcelain.

Description

technical field [0001] The invention belongs to the field of porcelain preparation, and in particular relates to a manufacturing process of iron red kiln glazed porcelain. Background technique [0002] With the rapid development of the economy and society, people's quality of life is improving day by day, and the concept of consumption is also constantly changing, requiring that ceramic products should not only be practical, but also artistic and ornamental. The existing glaze color can be divided into high temperature glaze and low temperature glaze according to the firing temperature; according to the appearance characteristics, it can be divided into transparent glaze, opacity glaze, color glaze, glossy glaze, matte glaze, crackle glaze (open sheet), crystal glaze and so on. [0003] The iron-based crystalline glaze began to be fired in the Song Dynasty, and formed a characteristic tea set decoration. It was famous at that time. There were varieties such as oil drop, rabb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/16C04B33/10C04B33/24C04B33/34C03C8/14C03C8/04C04B41/86
CPCC04B33/131C04B33/16C04B33/10C04B33/24C04B33/34C03C8/14C03C8/04C04B41/86C04B41/009C04B41/5022C04B2235/3463C04B2235/3409C04B2235/446C04B2235/3284C04B2235/3244C04B2235/6562C04B2235/6584C04B41/4539C04B41/4543
Inventor 林东星
Owner 福建省德化县东盛陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com