Low-temperature solidified powder production line system and production process thereof

A technology of production process and production line, which is applied in the field of low-temperature curing powder production line system and its production process, and can solve problems such as production interruption, reduced production efficiency, and inability to realize continuous production

Pending Publication Date: 2020-06-12
烟台凌宇粉末机械有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As a result, production is interrupted, continuous production cannot be realized, time-consuming and labor-intensive, and production efficiency is greatly reduced.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature solidified powder production line system and production process thereof
  • Low-temperature solidified powder production line system and production process thereof
  • Low-temperature solidified powder production line system and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The low-temperature solidified powder production line system includes a mixer 1, a screw extruder 2, a roller tablet press 3, a cyclone separator 4 and a stirring tank 5 configured in sequence according to the production process route, wherein the mixer 1 has a mixing tank with ice The interlayer of the material tank connected to the water machine, the interlayer of the material tank is fed with ice water to control the mixing and stirring of the materials inside the material tank under the predetermined low temperature condition; the mixer 1 is sequentially connected to the screw extruder 2, and the screw extruder The outer screw sleeve and the inner mandrel of the extruder 2 are all connected to the ice water machine, and the ice water is fed to extrude the material at a low temperature. The screw length-to-diameter ratio of the screw extruder 2 is set to 30:1; The lower part of the discharge port of the screw extruder 2 is provided with a roller tablet press 3, and th...

Embodiment 2

[0036] A production process for low-temperature solidified powder, which is implemented based on the production line system of Embodiment 1, includes the following specific steps:

[0037] S1, low temperature mixing

[0038] Put the material into the material tank of the mixer for pre-mixing, pass ice water into the interlayer of the material tank through the ice water machine, set the outlet water temperature of the ice water machine to 14 degrees, and the ice water in the material tank interlayer ensures that the materials in the tank are kept in the mixer Internal low-temperature mixing to reduce the frictional heat generated during the premixing process, the premixing time is controlled at 6 minutes, and the temperature of the material in the tank is 30-35 degrees at this time;

[0039] S2, low temperature extrusion

[0040] The premixed material enters the screw extruder, the screw length-to-diameter ratio of the screw extruder is 30:1, the extrusion speed is 380r / min, t...

Embodiment 3

[0052] A production process for low-temperature solidified powder, which is implemented based on the production line system of Embodiment 1, includes the following specific steps:

[0053] S1, low temperature mixing

[0054] Put the material into the material tank of the mixer for pre-mixing, pass ice water into the interlayer of the material tank through the ice water machine, set the outlet water temperature of the ice water machine to 12 degrees, and the ice water in the material tank interlayer ensures that the materials in the tank are kept in the mixer Internal low-temperature mixing to reduce the frictional heat generated during the premixing process, the premixing time is controlled at 8 minutes, and the temperature of the material in the tank is 28-32 degrees at this time;

[0055] S2, low temperature extrusion

[0056] The premixed material enters the screw extruder, the screw length-to-diameter ratio of the screw extruder is 30:1, the extrusion speed is 360r / min, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a low-temperature solidified powder production line system and a production process thereof. The production line system comprises a mixer, an extruder, a roller type tablet press, a cyclone separator and a stirring tank which are sequentially arranged according to a production process route. The production process comprises the following steps: S1, low-temperature mixing;S2, low-temperature extrusion; S3, tabletting at low temperature; S4, separation; S5, stirring; and S6, low-temperature grinding. Transformation is carried out on the basis of existing powder coatingproduction line equipment, so that the material temperature in each process node is controllable and adjustable, and the powder coating production line equipment can be suitable for the production characteristic of low-temperature solidified powder. In the technological process, different temperature parameters are set for mixing, extrusion and tabletting respectively, so that the materials alwayskeep good properties on the technological route, and finally, the materials meet the grinding requirements through the quenching process of heating and cooling in sequence in the stirring tank.

Description

technical field [0001] The invention relates to the technical field of powder coating production, in particular to a low-temperature curing powder production line system and a production process thereof. Background technique [0002] Powder coating is widely used in modern industrial production due to its advantages of economy, environmental protection, high efficiency and excellent performance, but some of its weaknesses are also obvious. If the curing conditions are relatively harsh, the curing temperature is generally between 180 and 200 °C. If the curing temperature can be reduced, energy consumption can be reduced, which is the need for environmental protection, energy saving and emission reduction. [0003] The high curing temperature not only leads to high energy consumption, but also restricts the coating of some substrates that cannot withstand high temperatures, such as plastics and wood, which greatly affects the expansion of the application field of powder coa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01F13/10B01F3/00B01F3/18B01F3/20B01F3/22B01F15/06B01J2/00C09D5/03B01F23/00B01F23/70B01F23/80
CPCB01J2/00C09D5/03B01F23/00B01F23/69B01F23/81B01F23/70B01F33/83B01F33/83612B01F33/83613B01F2035/98B01F2035/99B01F35/92B01F2101/30
Inventor 高奎坤
Owner 烟台凌宇粉末机械有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap