A kind of hardenability measurement component and measurement method of medium and low hardenability steel

A measuring method and technology for measuring components, which are applied to measuring devices, analyzing materials, testing crystals, etc., can solve the problems of difficulty in ensuring consistent sample quenching conditions and large sample size, and reduce time and material costs, and achieve consistent quenching conditions. Effect

Active Publication Date: 2021-08-24
内蒙古中盛工程技术有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problem that the critical hardening diameter method in the prior art has a large sample size and it is difficult to ensure that the quenching conditions of each sample are consistent, the present invention provides a medium-low hardenability steel hardenability measurement component and a measurement method. The present invention Set the test sample as a unequal diameter cone structure to solve the technical problem of large sample size, and conduct the same experiment in the same hardenability measurement device for medium and low hardenability steel to ensure the quenching conditions of the sample unanimous

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hardenability measurement component and measurement method of medium and low hardenability steel
  • A kind of hardenability measurement component and measurement method of medium and low hardenability steel
  • A kind of hardenability measurement component and measurement method of medium and low hardenability steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Example 1: from Figure 1~3 As shown, a medium-low hardenability steel hardenability measurement component includes a base 1, a bracket 2, a liquid inlet pipe 3, a liquid inlet valve 4, a liquid storage tank 5, a test sample 6, a quenching liquid 7, and a drain Pipe 8, drain valve 9,

[0037] The liquid storage tank 5 is fixedly arranged on the base 1, and the top side end of the liquid storage tank 5 is provided with a liquid inlet pipe 3 communicating with the cavity of the liquid storage tank 5, and the quenching liquid 7 is arranged in the liquid storage tank 5, and the liquid storage tank 5 The bottom end of the bottom is provided with a liquid discharge pipe 8 communicating with the cavity of the liquid storage tank 5, the liquid discharge pipe 8 is provided with a liquid discharge valve 9, and the bracket 2 is fixed horizontally on the inner wall of the lower part of the liquid storage tank 5;

[0038] The test sample 6 is set on the support 2;

[0039] Test sa...

Embodiment 2

[0051] Embodiment 2: This embodiment adopts the method for measuring the hardenability of the medium and low hardenability steel by the low hardenability steel hardenability measuring member in Embodiment 1, and the specific steps are as follows:

[0052] (1) The test sample of SA508-3 steel, which is a large nuclear power forging, is processed into an unequal diameter cone structure (see image 3 ), where the major diameter is Φ30mm, the minor diameter is Φ20mm, and the length is 100mm;

[0053] (2) Put the SA508-3 steel test sample with unequal diameter cone structure into a heat treatment furnace and heat it up to 900°C for 30 minutes, and keep it at 900°C for 30 minutes to make the sample completely austenitized. The heating process is as follows: Figure 5 shown;

[0054] (3) Fix the bracket horizontally on the inner wall of the liquid storage tank, open the liquid inlet valve of the liquid inlet pipe, and add the quenching liquid (water) into the liquid storage tank unt...

Embodiment 3

[0061] Embodiment 3: This embodiment adopts the method for measuring the hardenability of the medium and low hardenability steel by the low hardenability steel hardenability measuring member in Embodiment 1, and the specific steps are as follows:

[0062] (1) The test sample of SA508-3 steel, which is a large nuclear power forging, is processed into an unequal diameter cone structure (see image 3 ), where the major diameter is Φ30mm, the minor diameter is Φ20mm, and the length is 100mm;

[0063] (2) Put the SA508-3 steel test sample with unequal diameter cone structure into a heat treatment furnace and heat it up to 900°C for 30 minutes, and keep it at 900°C for 30 minutes to make the sample completely austenitized. The heating process is as follows: Figure 5 shown;

[0064] (3) Fix the bracket horizontally on the inner wall of the liquid storage tank, open the liquid inlet valve of the liquid inlet pipe, and add the quenching liquid (oil) into the liquid storage tank until...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a measuring component and a measuring method for the hardenability of steel with medium and low hardenability, and belongs to the technical field of hardenability testing of metal materials. In the present invention, the hardenability measurement component of low hardenability steel includes a base, a bracket, a liquid inlet pipe, a liquid inlet valve, a liquid storage tank, a test sample, a quenching liquid, a liquid discharge pipe, a liquid discharge valve, and the liquid storage tank is fixedly arranged. On the base, the top side end of the liquid storage tank is provided with a liquid inlet pipe communicating with the cavity of the liquid storage tank, the quenching liquid is arranged in the liquid storage tank, and the bottom end of the liquid storage tank is provided with a pipe connected with the cavity of the liquid storage tank. The liquid discharge pipe is provided with a liquid discharge valve, and the support is fixed horizontally on the inner wall of the lower part of the liquid storage tank; the test sample is arranged on the support; the test sample is a unequal diameter cone structure. The present invention solves the technical problem of a large amount of samples by setting the test sample as an unequal-diameter cone structure, and conducts the same experiment in the same hardenability measuring device for medium and low hardenability steel to ensure that the sample The quenching conditions are the same.

Description

technical field [0001] The invention relates to a measuring component and a measuring method for the hardenability of medium and low hardenability steel materials, and belongs to the technical field of hardenability testing of metal materials. Background technique [0002] The hardenability of steel refers to the ability of the steel to obtain an effective hardening depth after austenitization. Generally, the depth from the quenching end to the semi-martensitic zone is defined as the depth of the effective hardening layer. Understanding the hardenability of steel is of great significance for selecting the appropriate steel for the workpiece and determining a reasonable heat treatment process for the part. [0003] The critical hardening diameter method is a method for measuring the hardenability of materials. The critical hardening diameter method refers to the maximum diameter of the round bar sample quenched in a quenching liquid, and the center of the cross section is que...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G01N21/84G01N1/28G01N1/42G01N1/44
CPCG01N1/28G01N1/42G01N1/44G01N21/84G01N2021/8477
Inventor 李萌蘖徐大成郑善举
Owner 内蒙古中盛工程技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap