Novel polyurethane composite material for wall decoration and preparation method thereof

A polyurethane composite material and wall technology, which is applied in the field of polyurethane synthetic materials, can solve the problems of resource waste, high cost, and insufficient strength, and achieve the effects of low VOC, appropriate performance, and improved bearing capacity

Inactive Publication Date: 2020-04-28
SHANDONG INOV NEW MATERIALS CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, most of the wall interior materials commonly used in the market are high-resilience products. The strength of such products is not high enough, and external auxiliary materials are needed to provide certain support. At the same time, the cost of this product is relatively high, resulting in a certain waste of resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel polyurethane composite material for wall decoration and preparation method thereof
  • Novel polyurethane composite material for wall decoration and preparation method thereof
  • Novel polyurethane composite material for wall decoration and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] (1) Prepare 100Kg of component A material, respectively weigh polyether polyol a (F330N, Novel) 19.2Kg, polyether polyol b (C3050A, Novel) 52.9Kg, polyether polyol c (F628 , a Novel) 23.8Kg, water 3.2Kg, cell opener a (O-501,) 0.3Kg, catalyst a (bis(dimethylaminoethyl) ether) 0.1Kg, catalyst b (N,N-dimethyl Cyclohexylamine) 0.5Kg, put the weighed polyether polyol and water into the mixing tank and stir, then add the weighed cell opener and catalyst, add them to the reactor in turn, stir evenly at room temperature, and take samples After passing the test, it can be loaded into barrels.

[0036] (2) Prepare 100Kg of component B material, accurately measure polymethylene polyphenyl polyisocyanate 44V20L (Byer) 75Kg, plasticizer (dioctyl phthalate) 25Kg, put into the reaction kettle in order, stir and mix for 1 Hours, after the sampling test is qualified, the material is discharged, and the nitrogen is replaced with a sealed package.

[0037] Mix A and B components accord...

Embodiment 2

[0039] The novel wall interior material is prepared from the following components according to the following steps:

[0040] (1) Prepare 100Kg of component A material, weigh polyether polyol a (F330N, Novel) 23.8Kg, polyether polyol b (C3050A, Novel) 46.9Kg, polyether polyol c (F628 , Novel) 23.8Kg, water 3.2Kg, foam stabilizer a (F8001A, Novel) 1Kg, foam stabilizer b (L-580, Momentive) 1Kg, catalyst a (bis(dimethylaminoethyl) ether) 0.1Kg, catalyst b (bismuth isooctanoate) 0.2Kg, put the weighed polyether polyol and water into the mixing kettle and stir, then add the weighed foam stabilizer and catalyst, and add them in the reaction kettle successively, Stir evenly at room temperature, and after sampling and testing pass, it can be filled into barrels.

[0041] (2) Prepare 100Kg of component B materials, accurately measure 75Kg of polymethylene polyphenyl polyisocyanate M20S (BASFSE), and 25Kg of plasticizer (chlorinated paraffin), put them into the reaction kettle in order,...

Embodiment 3

[0044] The novel wall interior material is prepared from the following components according to the following steps:

[0045] (1) Prepare 100Kg of component A material, weigh polyether polyol a (F330N, Novel) 24.3Kg, polyether polyol b (C3050A, Novel) 47.5Kg, polyether polyol c (F628 , a Novel) 24.1Kg, water 3.2Kg, cell opener a (O-501) 0.3Kg, catalyst a (bis(dimethylaminoethyl) ether) 0.1Kg, catalyst b (C1) 0.5Kg, will weigh Put the measured polyether polyol and water into the mixing tank and stir, then add the weighed cell opening agent and catalyst, add them to the reaction tank in turn, stir evenly at room temperature, and fill the tank after sampling and testing pass.

[0046] (2) Prepare 100Kg of component B material, accurately measure 75Kg of polymethylene polyphenyl polyisocyanate PM200 (Yantai Wanhua), and 25Kg of plasticizer (dioctyl phthalate) into the reaction kettle in order, stir and mix After 1 hour, after the sampling test is qualified, the material is dischar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Functional group degreeaaaaaaaaaa
Functional group degreeaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of polyurethane synthetic materials, and particularly relates to a novel polyurethane composite material for wall decoration and a preparation method thereof. The novel polyurethane composite material for wall decoration comprises a component A and a component B. The component A is prepared from the following raw materials in percentage by mass: 10-40 percent of polyether polyol a, 40-70 percent of polyether polyol b, 0-40 percent of polyether polyol c, 0.2-2.0 percent of auxiliary agent, 0.2-1.0 percent of catalyst and 2.5-3.5 percent of water; andthe component B comprises the following raw materials in percentage by mass: 60-100% of polyisocyanate and 0-40% of a plasticizer. The polyurethane material prepared by the invention has higher bearing property and low raw material cost and is energy-saving and consumption-reducing. The invention also provides a simple and feasible preparation method.

Description

technical field [0001] The invention belongs to the technical field of polyurethane synthetic materials, and in particular relates to a novel polyurethane composite material for wall decoration and a preparation method thereof. Background technique [0002] As polyurethane gradually enters people's lives, its use is becoming more and more extensive. For some entertainment places such as KTV, bars and other places, in order to achieve sound absorption and safety protection, some polyurethane products with higher rebound effect are usually used. Good product for interior wall decoration. [0003] At present, most of the wall interior materials commonly used in the market are high-resilience products, which are not strong enough, and require a certain amount of support from the outer layer of auxiliary materials; at the same time, the cost of this product is relatively high, resulting in a certain waste of resources. Contents of the invention [0004] Aiming at the deficienc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/79C08G18/76C08G18/48C08K5/12C08L75/08C08L91/06C08J9/08
CPCC08G18/4816C08G18/7664C08G18/79C08G18/797C08J9/0023C08J9/0061C08J2205/05C08J2375/08C08J2491/06C08G2110/0058C08G2110/0083
Inventor 徐军李宗儒郝德开刘玄
Owner SHANDONG INOV NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap