Preparation method for self-adhesive PVC floor

A self-adhesive, floor technology, used in adhesives, non-polymer adhesive additives, non-polymer organic compound adhesives, etc., can solve the problem of low initial viscosity, low bonding strength, poor adhesion of PVC floors, etc. problems, to achieve the effect of improving oil resistance, high bonding strength and increasing service life

Inactive Publication Date: 2019-11-29
黄山市润亿建筑装饰材料有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, emulsion-type PVC floor adhesives generally have problems such as low initial viscosity, low bonding strength, and poor adhesion to PVC floors.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for self-adhesive PVC floor
  • Preparation method for self-adhesive PVC floor
  • Preparation method for self-adhesive PVC floor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method for a self-adhesive PVC floor, said self-adhesive PVC floor comprising a PVC substrate layer, a UV treatment layer, an adhesive layer and a protective paper layer, comprising the following steps:

[0031] S1 prepares PVC substrate layer: choose the PVC raw material that is 100 parts by weight, the filler of 350 parts and the auxiliary agent of 100 parts, wherein filler is calcium carbonate and kaolin, the parts by weight of kaolin is 50 parts by weight, the parts by weight of calcium carbonate 300 parts, the additives are 70 parts of plasticizer, 25 parts of lubricant, 2 parts of stabilizer and 3 parts of defoamer, slowly add PVC raw materials, fillers and additives into the high-speed mixer, stir and mix for 2-3 minutes Finally, unload the material into the tray of the mixer. If the raw materials are not mixed uniformly, it is necessary to prolong the mixing for 0.5-1min, then pressurize and release the pressure repeatedly for 2-3 times, the total t...

Embodiment 2

[0037] A preparation method for a self-adhesive PVC floor, said self-adhesive PVC floor comprising a PVC substrate layer, a UV treatment layer, an adhesive layer and a protective paper layer, comprising the following steps:

[0038] S1 prepares PVC substrate layer: choose the PVC raw material that is 100 parts by weight, the filler of 350 parts and the auxiliary agent of 100 parts, wherein filler is calcium carbonate and kaolin, the parts by weight of kaolin is 50 parts by weight, the parts by weight of calcium carbonate 300 parts, the additives are 70 parts of plasticizer, 25 parts of lubricant, 2 parts of stabilizer and 3 parts of defoamer, slowly add PVC raw materials, fillers and additives into the high-speed mixer, stir and mix for 2-3 minutes Finally, unload the material into the tray of the mixer. If the raw materials are not mixed uniformly, it is necessary to prolong the mixing for 0.5-1min, then pressurize and release the pressure repeatedly for 2-3 times, the total t...

Embodiment 3

[0044] A preparation method for a self-adhesive PVC floor, said self-adhesive PVC floor comprising a PVC substrate layer, a UV treatment layer, an adhesive layer and a protective paper layer, comprising the following steps:

[0045] S1 prepares PVC substrate layer: choose the PVC raw material that is 100 parts by weight, the filler of 350 parts and the auxiliary agent of 100 parts, wherein filler is calcium carbonate and kaolin, the parts by weight of kaolin is 50 parts by weight, the parts by weight of calcium carbonate 300 parts, the additives are 70 parts of plasticizer, 25 parts of lubricant, 2 parts of stabilizer and 3 parts of defoamer, slowly add PVC raw materials, fillers and additives into the high-speed mixer, stir and mix for 2-3 minutes Finally, unload the material into the tray of the mixer. If the raw materials are not mixed uniformly, it is necessary to prolong the mixing for 0.5-1min, then pressurize and release the pressure repeatedly for 2-3 times, the total t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method for a self-adhesive PVC floor. The self-adhesive PVC floor comprises a PVC substrate layer, a UV treatment layer, an adhesive layer and a protective paper layer. The preparation method comprises the following steps: S1, preparation of the PVC substrate layer; S2, preparation of the UV treatment layer; S3, preparation of a rough friction surface; S4, preparation of protective paper; and S5, preparation of the adhesive layer. According to the invention, an acrylate emulsion is polymerized by adopting acrylic acid and methacrylic acid with a mass fraction of 2% to 5%, so oil resistance, solvent resistance and adhesive strength of the acrylate emulsion are significantly improved; freeze-thaw stability of the emulsion and wettability of the emulsion to a pigment filler can be improved; the polymerized emulsion can be endowed with the characteristic of thickening; meanwhile, through addition of different varieties of filling materials with different parts by mass and various auxiliary agents with different parts by mass, a floor adhesive is optimized; a PVC floor adhesive with good initial viscosity and high bonding strength is prepared; and the service life of a PVC floor is prolonged.

Description

technical field [0001] The invention relates to the technical field of floor technology design and application, in particular to a preparation method of a self-adhesive PVC floor. Background technique [0002] With the progress of society and the development of science and technology, people have higher and higher requirements for the living environment, especially the building and decoration materials used in residential places.” There are many new energy-saving and environmentally friendly building materials on the market, among which polyvinyl chloride (PVC) Plastic flooring is currently the most novel high-tech flooring material in the world's building materials industry. It has entered the Chinese market since the early 1980s and has been widely recognized in large and medium-sized cities in China. It is widely used, such as indoor homes and hospitals. , schools, office buildings, factories, public places, supermarkets, stadiums and other places. [0003] However, the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K3/26C08K3/34C08J5/18C09J4/00C09J4/02C09J11/04E04F15/02
CPCC08J5/18C08J2327/06C08K3/346C08K2003/265C09J4/00C09J11/04E04F15/02
Inventor 不公告发明人
Owner 黄山市润亿建筑装饰材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com