A kind of organic optoelectronic material and its application

An organic optoelectronic material, phenanthroimidazole technology, applied in luminescent materials, organic chemistry, circuits, etc., to achieve the effects of reducing the singlet-triplet energy gap, high luminous brightness, and reducing overlap

Active Publication Date: 2020-10-09
WUHAN SUNSHINE OPTOELECTRONICS TECH CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The quantum efficiency of thermally induced delayed fluorescent materials has greatly broken through the theoretical limit of traditional fluorescent devices, but in fact it faces the following three problems: (1) How to adjust the fine structure of the designed molecules so that the spin coupling parameters of the materials are consistent with The singlet-triplet energy level difference, and the radiative transition constant (k f ) can effectively cooperate, so that the material has both high exciton utilization rate and high fluorescence radiation efficiency; (2) how to improve the radiative transition constant (k f ), avoiding non-radiative transitions so that the singlet radiative transition constant (k f ) is greater than the transition constant (k isc ), improving device efficiency roll-off from the perspective of regulating exciton lifetime; (3) on the basis of high-efficiency thermally induced delayed fluorescence materials, how to match functional materials of different energy levels to improve device performance from the perspective of device structure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of organic optoelectronic material and its application
  • A kind of organic optoelectronic material and its application
  • A kind of organic optoelectronic material and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Compound 3 provided by the present invention can be synthesized by the following method.

[0049]

[0050] (1) In a 500ml three-necked flask, add 4,6-dichloro-1,3,5-triazin-2-amine (16.50g, 100mmol), 4-tert-butylphenylboronic acid (35.60g, 200mmol), Potassium carbonate (27.64g, 200mmol), toluene 150mL, ethanol 75mL, water 75mL, in N 2 Tetrakis(triphenylphosphine)palladium (0.35 g, 3 mmol) was added under protection, the reaction was controlled at 85° C., and the reaction was carried out for 12 h, and the reaction was completed by liquid phase monitoring. Cool to room temperature, wash twice with water, add activated carbon for decolorization, filter, concentrate to obtain a light yellow solid, recrystallize twice from ethanol, and dry under vacuum to obtain 4,6-bis(4-tert-butylphenyl)-1,3, 32.44 g of 5-triazin-2-amine, yield 90%.

[0051] (2) In a 500ml three-necked flask, add phenanthrenequinone (10.41g, 50mmol), 4,6-di(4-tert-butylphenyl)-1,3,5-triazin-2-amine (2...

Embodiment 2

[0053] Compound 12 provided by the present invention can be synthesized by the following method.

[0054]

[0055] (1) In a 500ml three-necked flask, add 4,6-dichloro-1,3,5-triazin-2-amine (16.50g, 100mmol), (9,9-dimethyl-9H-fluorene-2 -base) boric acid (47.62g, 200mmol), potassium carbonate (27.64g, 200mmol), toluene 150mL, ethanol 75mL, water 75mL, in N 2 Tetrakis(triphenylphosphine)palladium (0.35 g, 3 mmol) was added under protection, the reaction was controlled at 85° C., and the reaction was carried out for 12 h, and the reaction was completed by liquid phase monitoring. Cool to room temperature, wash twice with water, add activated carbon for decolorization, filter, concentrate to obtain a light yellow solid, recrystallize twice from ethanol, and dry under vacuum to obtain 4,6-bis(9,9-methyl-9H-fluorene-2- base)-1,3,5-triazin-2-amine 42.29g, yield 88%.

[0056] (2) In a 500ml three-necked flask, add phenanthrenequinone (10.41g, 50mmol), 4,6-di(9,9-methyl-9H-fluoren...

Embodiment 3

[0058] Compound 21 provided by the present invention can be synthesized by the following method.

[0059]

[0060] (1) In a 500ml three-necked flask, add 4,6-dichloro-1,3,5-triazin-2-amine (16.50g, 100mmol), phenylboronic acid (24.39g, 200mmol), potassium carbonate (27.64g , 200mmol), toluene 150mL, ethanol 75mL, water 75mL, in N 2 Tetrakis(triphenylphosphine)palladium (0.35 g, 3 mmol) was added under protection, the reaction was controlled at 85° C., and the reaction was carried out for 12 h, and the reaction was completed by liquid phase monitoring. Cool to room temperature, wash twice with water, add activated carbon for decolorization, filter, concentrate to obtain a light yellow solid, recrystallize twice from ethanol, and dry under vacuum to obtain 4,6-diphenyl-1,3,5-triazine-2- Amine 22.35g, yield 90%.

[0061] (2) In a 500ml three-necked flask, add phenanthrenequinone (10.41g, 50mmol), 4,6-diphenyl-1,3,5-triazin-2-amine (14.89g, 60mmol), [1,1 '-Biphenyl]-4-formal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of photoelectric material application technology, and in particular relates to an organic photoelectric material and its application. The organic optoelectronic material provided by the present invention takes phenanthroimidazole and triazine as basic structural units to form a kind of thermally induced delayed fluorescent material, and the triazine group and imidazole group with strong electron donating properties have a large conjugated The bonding or condensing of the planar phenanthrene groups effectively improves the roll-down of the device. At the same time, the further modification of the functional groups with strong electron-withdrawing properties improves the exciton transport and luminescence performance of the device at high current densities. It is an ideal light-emitting layer material, electron transport material and light-extracting layer material in organic electroluminescent devices.

Description

technical field [0001] The invention belongs to the technical field of photoelectric material application technology, and in particular relates to an organic photoelectric material and its application. Background technique [0002] Organic Light-Emitting Diode (OLED), also known as organic electro-laser display and organic light-emitting semiconductor, was discovered in the laboratory by Chinese-American professor Ching W.Tang in 1979. The advantages of luminescence, wide viewing angle, almost infinitely high contrast, low power consumption, and extremely high response speed are widely used in mobile phones, digital cameras, notebook computers, car displays, TVs, and lighting. The continuous development of OLED materials and The improvement of the performance of organic light-emitting diodes has become a research hotspot in the field of optoelectronic technology. [0003] OLED materials can be divided into three generations based on differences in light-emitting mechanism a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07D403/04C07D405/14C07D409/14C07D403/14C09K11/06H01L51/50H01L51/54
CPCC07D403/04C07D405/14C07D409/14C07D403/14C09K11/06C09K2211/1029C09K2211/1044C09K2211/1059C09K2211/1088C09K2211/1092C09K2211/1007C09K2211/1011C09K2211/1014H10K85/615H10K85/631H10K85/654H10K85/6572H10K85/6574H10K85/6576H10K50/00
Inventor 穆广园庄少卿任春婷
Owner WUHAN SUNSHINE OPTOELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com