Cutting steel wire, steel material for cutting steel wire and production method thereof

A technology for cutting steel wire and production method, applied in the field of steel for cutting steel wire and cutting steel wire, can solve the problems of large inclusion size, high number density of inclusions, low tensile strength and the like

Active Publication Date: 2020-05-22
INST OF RES OF IRON & STEEL JIANGSU PROVINCE +2
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In view of the fact that the steel for cutting steel wire prepared by the current production process in this technical field has problems such as large inclusion size, high number density of inclusions, and low tensile strength, the performance of the existing cutting steel wire cannot meet market demand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cutting steel wire, steel material for cutting steel wire and production method thereof
  • Cutting steel wire, steel material for cutting steel wire and production method thereof
  • Cutting steel wire, steel material for cutting steel wire and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] In this embodiment, five test examples with serial numbers A, B, C, D, and E are illustrated, and the specific details of this embodiment will be introduced below.

[0069] (1) Pretreatment

[0070] Take blast furnace molten iron for desulfurization in KR desulfurization device. The temperature, weight, Si content, S content of blast furnace molten iron and the S content in molten iron after desulfurization are shown in Table 1.

[0071] [Table 1]

[0072]

[0073] (2) Electric furnace blowing

[0074] Add steel scrap and pretreated molten iron into a 100t electric furnace, and mix the two into molten steel with a total weight of 110±2t; add the first batch of slagging agent to the molten steel and then perform desiliconization and dephosphorization; The second batch of slagging agent is added to the molten steel after silicon and dephosphorization; after that, the molten steel is subjected to oxygen blowing decarburization, and during the oxygen blowing decarburiz...

Embodiment 2

[0100] In this embodiment, five test examples with serial numbers H, I, J, K, and L are illustrated, and the specific details of this embodiment will be introduced below.

[0101] (1) Pretreatment

[0102] Take blast furnace molten iron for desulfurization in KR desulfurization device. The temperature, weight, Si content, S content of blast furnace molten iron and the S content in molten iron after desulfurization are shown in Table 8.

[0103] [Table 8]

[0104]

[0105] (2) Converter blowing

[0106] Add steel scrap and pretreated molten iron into a 120t converter, and mix the two into molten steel with a total weight of 130±2t; add the first batch of slagging agent to the molten steel and then perform desiliconization and dephosphorization; The second batch of slagging agent is added to the molten steel after silicon and dephosphorization; after that, the molten steel is subjected to oxygen blowing decarburization, and during the oxygen blowing decarburization process ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a sawing wire, steel for the sawing wire, and a production method thereof. The production method comprises the steps of desulfurizing molten iron till S in the molten iron is no more than 0.002%; mixing the desulfurized molten iron and steel scrap into molten steel, and desiliconizing and dephosphorizing the molten steel at 1330 DEG C-1380 DEG C; then, decarburizing the molten steel by blowing oxygen, and obtaining the molten steel comprising no less than 0.3% of C, no more than 0.01% of P and no more than 0.01% of S, wherein the temperature of the molten steel is no lower than 1650 DEG C; adding desoxidants and slagging media to the molten steel for deoxidation alloying; then, refining the molten steel for regulating chemical components and inclusions, wherein thecomponents of the inclusions comprise no more than 10% of Al2O3 and no more than 30% of CaO; degassing the refined molten steel and removing the inclusions to obtain the molten steel, wherein the sizeof the inclusions of the molten steel is no more than 10 [mu]m, and the number density of the inclusions is no more than 0.5 g / m<3>; and casting the molten steel into steel billets. The steel, prepared with the production method, for the sawing wire can be used as base metal for producing the sawing wire with the diameter of no more than 100 <mu>m and the tensile strength of no lower than 4600 MPa; and the length of the continuous wire in the process of manufacturing the sawing wire is no less than 200 km.

Description

technical field [0001] The invention belongs to the technical field of iron and steel smelting, and relates to a production method of steel for cutting steel wire, and also relates to a steel for cutting steel wire prepared by the production method, and a cutting steel wire further processed from the steel for cutting steel wire . Background technique [0002] Cutting wire, also known as cutting wire, cutting steel wire, and cutting wire, is a special wire used for cutting, and it is also a special steel wire with a diameter of less than 0.20mm and a galvanized copper surface. It is widely used as a consumable material In the fields of energy, aviation, equipment and public facilities, such as cutting and forming of solar silicon wafers, quartz materials, monocrystalline silicon, and polycrystalline silicon. It is even possible to inlay tiny diamond particles on the cutting wire to make a diamond cutting wire, or diamond wire, diamond cutting wire, or diamond wire. [0003...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C33/04C22C38/02C22C38/04C22C38/06C22C38/18C22C38/28C22C38/14C21C1/02C21C5/28C21C5/52C21C7/06C21C7/10
CPCC21C1/02C21C5/28C21C5/52C21C7/06C21C7/10C22C33/04C22C38/02C22C38/04C22C38/06C22C38/14C22C38/18C22C38/28Y02P10/20
Inventor 邹长东赵家七胡显军麻晗
Owner INST OF RES OF IRON & STEEL JIANGSU PROVINCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products