Algae fiber facial mask base fabric and preparation method thereof

A technology of seaweed fiber and calcium alginate fiber, which is applied in fiber treatment, plant fiber, non-woven fabrics, etc., can solve the problems of cumbersome and complicated processes, improve subcutaneous tissue damage, repair skin damage, and moisturize and not greasy skin Effect

Inactive Publication Date: 2019-04-05
广州市洁宝无纺制品有限公司
View PDF6 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the seaweed fiber used for facial masks currently on the market is only processed into a spunlace mask substrate through the production process of spunlace non-woven fabrics. For example, in patent CN105401337A, calcium alginate and plant mixed fibers are used as raw materials. Seaweed fiber spunlace nonwovens are made through the production process of spunlace nonwovens. Another example is patent CN107898706A which discloses a seaweed fiber nonwoven mask, which is obtained by esterifying calcium alginate fiber nonwovens twice. Calcium alginate fiber mask base fabric; however, when these calcium alginate fiber mask base fabrics are used in the finished mask, in order to achieve the gel effect, ingredients containing potassium ions or sodium ions must be added to the essence, which makes the process cumbersome and complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Algae fiber facial mask base fabric and preparation method thereof
  • Algae fiber facial mask base fabric and preparation method thereof
  • Algae fiber facial mask base fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] The seaweed fiber facial mask base cloth is composed of the following components according to mass percentage: 80% carboxymethyl cellulose fiber, 15% calcium alginate fiber and 5% sodium alginate.

[0035] The preparation steps of above-mentioned seaweed fiber mask base cloth are as follows:

[0036] (1) Weigh the raw materials in proportion for later use. Carboxymethyl cellulose fibers and calcium alginate fibers are preliminarily opened and mixed by hand, and then opened with an opener to open the fibers from the original compacted state. Relaxed state;

[0037] (2) mixing the carboxymethyl cellulose fiber and the calcium alginate fiber through step (1), and further opening after mixing;

[0038] (3) Comb the mixed fibers obtained in step (2) into a web, and then perform hydroentanglement processing with a hydroentanglement machine, and spray high-pressure fine water flow onto the fiber web, and the fibers will entangle with each other during the process, so that the...

Embodiment 2

[0042] The seaweed fiber facial mask base cloth is composed of the following components according to mass percentage: 75% carboxymethyl cellulose fiber, 15% calcium alginate fiber and 10% sodium alginate.

[0043] The preparation method of above-mentioned seaweed fiber mask base cloth, concrete steps are as follows:

[0044] (1) Weigh the raw materials in proportion for later use. Carboxymethyl cellulose fibers and calcium alginate fibers are preliminarily opened and mixed by hand, and then opened with an opener to open the fibers from the original compacted state. Relaxed state;

[0045] (2) mixing the carboxymethyl cellulose fiber and the calcium alginate fiber through step (1), and further opening after mixing;

[0046](3) Comb the mixed fibers obtained in step (2) into a web, and then perform hydroentanglement processing with a hydroentanglement machine, and spray high-pressure fine water flow onto the fiber web, and the fibers will entangle with each other during the pro...

Embodiment 3

[0050] The seaweed fiber facial mask base cloth is composed of the following components by mass percentage: 77% carboxymethyl cellulose fiber, 17% calcium alginate fiber and 6% sodium alginate.

[0051] The preparation method of above-mentioned seaweed fiber mask base cloth, concrete steps are as follows:

[0052] (1) Weigh the raw materials in proportion for later use. Carboxymethyl cellulose fibers and calcium alginate fibers are preliminarily opened and mixed by hand, and then opened with an opener to open the fibers from the original compacted state. Relaxed state;

[0053] (2) mixing the carboxymethyl cellulose fiber and the calcium alginate fiber through step (1), and further opening after mixing;

[0054] (3) Comb the mixed fibers obtained in step (2) into a web, and then perform hydroentanglement processing with a hydroentanglement machine, and spray high-pressure fine water flow onto the fiber web, and the fibers will entangle with each other during the process, so t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of skin care products, and particularly relates to an algae fiber facial mask base fabric which consists of carboxymethyl cellulose fibers, calcium alginate fibers and sodium alginate. The preparation method of the algae fiber facial mask base fabric is provided. The algae fiber facial mask base cloth can realize gelation without adding a component containing potassium ions or sodium ions into the essence, gelation of the seaweed facial mask can be realized as long as liquid exists, no requirement on the essence component and the packaging mode of the facial mask bag is proposed, and is convenient to use. In addition, the algae fiber facial mask base fabric has the advantages of good skin sticking property, good moisture retention property, fresh skin feeling, no tightness, and no greasy skin. The alginate can form a fibrous hydrogel with wound exudate to accelerate wound hemostasis, has no toxicity, no sensitization and no irritation, and has obvious improvement effect on enlarged acne scar, intradermal or subcutaneous tissue damage.

Description

technical field [0001] The invention belongs to the technical field of skin care products, and in particular relates to a seaweed fiber facial mask base cloth and a preparation method thereof. Background technique [0002] At present, a more common method of facial beauty maintenance is to absorb the prepared high-concentration maintenance essence on the mask cloth to prolong the time that the essence stays on the skin, improve the penetration amount and penetration depth of skin care ingredients into the skin, and Rapidly changes skin moisture levels. In essence, the beauty care process of the skin is the water absorption and moisturizing process of the skin, and the key is to look at the water replenishment and moisturizing properties of the mask material. [0003] There are many types of mask materials. 70% of the masks on the market are spunlace non-woven fabrics. Tencel fibers, viscose fibers, cotton fibers, and silk fibers are commonly used. However, the tencel fiber...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/13A61K8/02A61K8/73A61Q19/00D04H1/4382D04H1/492D06M101/04D06M101/06
CPCA61K8/0212A61K8/731A61K8/733A61Q19/00D04H1/4382D04H1/492D06M15/13D06M2101/04D06M2101/06
Inventor 邓喜艳
Owner 广州市洁宝无纺制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com