Ceramic flash powder glaze and preparation method thereof

A technology of ceramics and flash powder, which is applied in the field of ceramic flash powder glaze and its preparation, and can solve problems such as not having a three-dimensional effect

Inactive Publication Date: 2019-02-05
HUNAN YINHE CERAMICS IND
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, in the porcelain industry, the shape of porcelain blanks is the basis of high-quality products. The deployment of glazes makes porcelain more colorful. Porcelain blanks of the same shape often have different effects on consumers' vision due to different glazes. , ceramics in the prior art generally do not have a three-dimensional effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A ceramic flash powder glaze, the components contained in the glaze used in it and the parts by mass of each component are as follows:

[0028] Water-based acrylic resin: 59.8 parts;

[0029] Water-based curing agent: 0.2 parts;

[0030] Color glitter powder: 30 parts;

[0031] Purified water: 10 parts.

[0032] The preparation method of the ceramic flash powder glaze, the steps of the method include:

[0033] S1: Prepare the glaze according to each component and the mass parts of each component;

[0034] S2: cleaning the ceramic surface;

[0035] S3: spraying the glaze on the ceramic surface;

[0036] S4: drying the ceramics once;

[0037] S5: Spray the glaze once more on the surface of the ceramic after drying once;

[0038] S6: drying the ceramics after standing still to obtain a finished product.

[0039] In step S1, the steps of preparing the glaze are as follows:

[0040] 1) Prepare materials according to each component and each component by mass;

[004...

Embodiment 2

[0048] The components contained in the glaze used in the ceramic flash powder glaze of this embodiment and the parts by mass of each component are the same as in Example 1, and the preparation method is basically the same, the difference is:

[0049] In step S3, the thickness of the glaze film of the glaze is controlled at 25 μm.

[0050] In step S4, the conditions for primary drying are: the temperature is 120° C., and the time is 20 minutes.

[0051] In step S5, the thickness of the glaze film of the glaze is controlled at 25 μm.

[0052] In step S6, the ceramics are left to stand for 10 minutes.

[0053] In step S6, the conditions for re-drying are as follows: the temperature is 180° C., and the time is 35 minutes.

Embodiment 3

[0055] The components contained in the glaze used in the ceramic flash powder glaze of this embodiment and the parts by mass of each component are the same as in Example 1, and the preparation method is basically the same, the difference is:

[0056] In step S3, the thickness of the glaze film of the glaze is controlled at 20 μm.

[0057] In step S4, the conditions for primary drying are: the temperature is 110° C., and the time is 15 minutes.

[0058] In step S5, the thickness of the glaze film of the glaze is controlled at 20 μm.

[0059] In step S6, the ceramics are left to stand for 10 minutes.

[0060] In step S6, the conditions for re-drying are as follows: the temperature is 170° C., and the time is 30 minutes.

[0061] The ceramic flash powder glazes prepared in the above three examples are observed and found to have flash characteristics on the surface, and the ceramic product has a strong visual effect and a three-dimensional effect.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses ceramic flash powder glaze and a preparation method thereof. The glaze used by the ceramic flash powder glaze contains the following components in parts by mass: 59.8 parts ofwater-based acrylic resin, 0.2 part of water-based curing agent, 30 parts of colored flash powder and 10 parts of purified water. By using the glaze disclosed by the invention, the ceramic has a highflash property, the visual effect of a ceramic product is enhanced, and the ceramic product has a three-dimensional effect.

Description

technical field [0001] The invention relates to a ceramic flash powder glaze and a preparation method thereof. Background technique [0002] At present, in the porcelain industry, the shape of porcelain blanks is the basis of high-quality products. The deployment of glazes makes porcelain more colorful. Porcelain blanks of the same shape often have different effects on consumers' vision due to different glazes. , ceramics in the prior art generally do not have a three-dimensional effect. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the defects of the prior art and provide a ceramic flash powder glaze, which can make ceramics have high flash characteristics, enhance the visual effect of ceramic products, and make them have a three-dimensional effect. [0004] In order to solve the above technical problems, the technical solution of the present invention is: a kind of ceramic flash powder glaze, the components...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/83
CPCC04B41/48C04B41/83C04B41/4543C04B41/0072
Inventor 王建桥
Owner HUNAN YINHE CERAMICS IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com