A kind of hexagonal dendritic manganese series lithium ion sieve adsorbent and preparation method thereof

A lithium ion and adsorbent technology, which is applied in the field of hexagonal dendritic manganese-based lithium ion sieve adsorbent and its preparation, can solve the problems of high energy consumption, lack of effective methods, particle uniformity and dispersibility, etc. The effect of reducing reaction steps and preparation costs, and stable performance

Active Publication Date: 2021-03-16
QINGHAI INST OF SALT LAKES OF CHINESE ACAD OF SCI
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing methods not only consume too much energy, but also do not use effective methods to control the uniformity and dispersion of particles and regulate their crystal growth process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hexagonal dendritic manganese series lithium ion sieve adsorbent and preparation method thereof
  • A kind of hexagonal dendritic manganese series lithium ion sieve adsorbent and preparation method thereof
  • A kind of hexagonal dendritic manganese series lithium ion sieve adsorbent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] As an aspect of the technical solution of the present invention, what it relates to is a preparation method of a hexagonal dendritic manganese series lithium ion sieve adsorbent, comprising the following steps:

[0031] (1) adding manganese source and lithium source into water, stirring to obtain the first mixed solution;

[0032] (2) adding an organic lipid compound into the first mixed solution, and stirring to obtain a second mixed solution;

[0033] (3) Place the second mixed solution in a microwave reactor, react at 160-200° C. for 20-60 minutes, and then perform solid-liquid separation on the solid and liquid in the second mixed solution to obtain LiMnO 2 particles;

[0034] (4) the resulting LiMnO 2 The particles were calcined at 400-600°C for 4-8 hours to obtain Li 1.6 mn 1.6 o 4 Hexagonal dendritic manganese-based lithium ion sieve adsorbent.

[0035] In some embodiments, the manganese source includes any one or two or more of potassium permanganate, sodi...

Embodiment 1

[0051] (1) Potassium permanganate and anhydrous lithium hydroxide were added into deionized water at a ratio of 0.8:1, and magnetically stirred to obtain a first mixed solution.

[0052] (2) Add ethyl acetate to the first mixed solution, the ratio of ethyl acetate to potassium permanganate is 100:1, mix and magnetically stir to obtain the second mixed solution.

[0053] (3) Put the second mixed solution into a microwave reactor at a temperature of 200° C. and a reaction time of 1 hour. After the reaction is completed, the solid and liquid mixtures are subjected to solid-liquid separation to obtain solids that are washed and dried to obtain pure LiMnO 2 particles.

[0054] (4) LiMnO will be obtained 2 Calcined at 600°C for 8 hours to obtain Li 1.6 mn 1.6 o 4 Lithium ion adsorbent.

[0055] (5) Li will be obtained 1.6 mn 1.6 o 4 The lithium-ion adsorbent was exchanged and washed three times with deionized water and ethanol.

[0056] The XRD diffraction pattern of the h...

Embodiment 2

[0059] (1) Sodium permanganate and lithium chloride were added into deionized water at a ratio of 0.15:1, and magnetically stirred to obtain the first mixed solution.

[0060] (2) Add methyl formate to the first mixed solution, the ratio of methyl formate and sodium permanganate is 8:1, mix and magnetically stir to obtain the second mixed solution.

[0061] (3) Put the second mixed liquid into a microwave reactor at a temperature of 160° C. and a reaction time of 20 minutes. After the reaction is completed, the solid and liquid mixtures are subjected to solid-liquid separation to obtain solids that are washed and dried to obtain pure LiMnO 2 particles.

[0062] (4) LiMnO will be obtained 2 Calcined at 400-600°C for 4 hours to obtain Li 1.6 mn 1.6 o 4 Lithium ion adsorbent.

[0063] (5) Li will be obtained 1.6 mn 1.6 o 4 The lithium-ion adsorbent was exchanged and washed three times with deionized water and ethanol.

[0064] The SEM scanning picture of the hexagonal d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hexagonal dendritic manganese lithium ion sieve adsorbent and a preparation method thereof. The method includes: adding a manganese source and a lithium source into water, and stirring to obtain first mixed solution; adding an organic aliphatic compound into the first mixed solution, and stirring to obtain second mixed solution; adding the second mixed solution into a microwave reactor, performing reaction for 20-60min at 160-200 DEG C, and subjecting solid and liquid in the second mixed solution to solid-liquid separation to obtain LiMnO2 particles; calcining the obtained LiMnO2 particles for 4-8h at 400-600 DEG C to obtain Li1.6Mn1.6O4 hexagonal dendritic manganese lithium ion sieve adsorbent. A microwave hydrothermal reaction method is adopted for preparing thehexagonal dendritic manganese lithium ion sieve adsorbent, organic lipids are adopted as a reducing agent and a structural regulating agent for growth regulation, and simplicity of selected raw materials and a preparation process and high purity, high yield, particle size uniformity and stable performances of an obtained product are realized.

Description

technical field [0001] The invention relates to a lithium ion sieve adsorbent, in particular to a hexagonal dendritic manganese series lithium ion sieve adsorbent and a preparation method thereof. Background technique [0002] Lithium exists in nature mainly in pegmatite ores such as spodumene and lepidolite, or in salt lake brine and seawater in the form of lithium ions. Lithium ion extraction methods in brine mainly include: precipitation method, evaporation crystallization method, solvent extraction method, calcination leaching method, salting out method, carbonization method, selective semipermeable membrane method, "Xu's" method, adsorption method, among which adsorption method The process is simple and the cost is low, and it is an ideal method for extracting lithium from the solution. Lithium-manganese spinel-type lithium adsorbent is the most widely studied and has the highest adsorption capacity, and is expected to be used for lithium extraction in high-magnesium-l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/04B01J20/28B01J20/30
CPCB01J20/04B01J20/28014
Inventor 刘忠钱方仁郭敏周永全钱志强李权吴志坚
Owner QINGHAI INST OF SALT LAKES OF CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More