Gravure roller coating and knife coating alternate printing technique

A printing process and knife coating technology, applied in dyeing, textiles and papermaking, etc., can solve the problems of poor product competitiveness, low product grade and added value, no differentiation and specialization of products, etc., and achieve excellent color fastness , improve the grade and added value, and increase the effect of product competitiveness

Inactive Publication Date: 2018-12-25
ZHEJIANG MIZUDA TEXTILE PRINTING & DYEING TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the printing effect of the existing fabrics obtained by gravure roller coating does not have tactile differences or functional effects such as skin feeling, hazy, anti-aging, smooth, crisp or dry, waxy, skin feeling, and the product does not have the above differentiation, Special features, not very good color fastness, low product grade and added value, poor product competitiveness
Therefore, the existing gravure roller coating has the problems that the product does not have the above-mentioned differentiation and characteristic features, the color fastness is not very good, the grade and added value of the product are low, and the product competitiveness is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Gravure roll coating and knife coating cross printing process, including the following steps:

[0024] A, the fabric is carried out gravure roll printing, wherein the doctor blade angle used in the gravure roll printing is 30-55 °, and the speed of a vehicle is 13-16m / min, obtains A product;

[0025] B. Pre-dry product A in a drying room at a drying temperature of 50-70°C and a drying time of 10-15s to obtain product B;

[0026] C. Flatten product B with a pressure roller at a temperature of 100-130°C and a pressure of 2-2.5 MPa to obtain product C;

[0027] D. Dry product C to obtain product D;

[0028] E. Knife coating of product D, wherein the radius of the knife edge of the knife coating is 0.5mm, the thickness of the knife edge is 0.3-0.4cm, and the vehicle speed is 40-50m / min, to obtain product E;

[0029] F. Dry product E at a temperature of 150-190° C. and a drying time of 30-35 seconds to obtain a finished product.

[0030] Both gravure roll printing and kni...

Embodiment 2

[0032] Gravure roll coating and knife coating cross printing process, including the following steps:

[0033] A, the fabric is carried out gravure roll printing, wherein the doctor blade angle used in the gravure roll printing is 30 °, and the speed of a vehicle is 15m / min, obtains A product;

[0034] B. Pre-dry product A in a drying room at a drying temperature of 60°C and a drying time of 12s to obtain product B;

[0035] C. Flatten product B with a pressure roller at a temperature of 120°C and a pressure of 2.2 MPa to obtain product C;

[0036] D. Dry product C to obtain product D;

[0037] E. Knife-coating product D, wherein the knife-edge radius size of the knife-coating is 0.5mm, the thickness of the knife-edge is 0.35cm, and the speed of a vehicle is 45m / min, to obtain product E;

[0038] F. Dry product E at a temperature of 170° C. and a drying time of 33 seconds to obtain a finished product.

[0039] The coatings used in step A and step E are made of the following ...

Embodiment 3

[0041] Gravure roll coating and knife coating cross printing process, including the following steps:

[0042] A, the fabric is carried out gravure roll printing, wherein the doctor blade angle used in the gravure roll printing is 55 °, and the speed of a vehicle is 16m / min, obtains A product;

[0043] B. Pre-dry product A in a drying room at a drying temperature of 70°C and a drying time of 10s to obtain product B;

[0044] C. Flatten product B with a pressure roller at a temperature of 130°C and a pressure of 2.5 MPa to obtain product C;

[0045] D. Dry product C to obtain product D;

[0046] E. Knife coating of product D, wherein the knife-edge radius size of the knife coating is 0.5mm, the thickness of the knife-edge is 0.4cm, and the vehicle speed is 50m / min, to obtain product E;

[0047] F. Dry product E at a temperature of 190° C. and a drying time of 30 seconds to obtain a finished product.

[0048] The coating used in step A and step E comprises the following raw ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a gravure roller coating and knife coating alternate printing technique, including: subjecting fabric to gravure roller printing prior to pre-drying, flattening with a presserroller under the temperature of 100-130 DEG C and the pressure of 2-2.5 MPa, drying, performing knife coating, and drying to obtain a finished product. The manufactured fabric has the differential andspecial printing features of dryness, coolness, softness and smoothness, has excellent color fastness, has effectively improved grade and added value and has improved competitiveness.

Description

technical field [0001] The invention relates to a gravure printing process, in particular to a gravure roller coating and knife coating cross printing process. Background technique [0002] Traditional printing is generally a processing method in which dyes such as reactive dyes or paints are directly printed on fabrics through a nickel mesh. The effect obtained by this printing method is a traditional flat effect, which lacks three-dimensionality and is not flexible enough. On this basis, gravure roll coating is produced. Gravure roll coating is a special printing method. Through materials and processing methods such as color paste, PU paste, pearlescent, and glitter sheets, a printing effect with obvious three-dimensional effect can be obtained. Combined with different The gravure process can achieve a three-dimensional effect with distinct layers, giving the pattern a "lifelike" visual experience. However, the printing effect of the existing fabrics obtained by gravure ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06P5/00
CPCD06P5/00
Inventor 杨雪峰
Owner ZHEJIANG MIZUDA TEXTILE PRINTING & DYEING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com