Release film for ceramic green sheet production

A technology for ceramic green sheets and mold release films, used in manufacturing tools, ceramic molding machines, synthetic resin layered products, etc., can solve the problems of low protrusion density, pinholes, high pressure, etc. pinhole effect

Active Publication Date: 2019-07-16
TOYOBO CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, according to the above-mentioned prior art, although the height of the protrusions is reduced, the density of the protrusions is low. Therefore, there is a problem that the pressure applied to the protrusions is large, and pinholes are generated when the ceramic green sheet is further thinned.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Release film for ceramic green sheet production
  • Release film for ceramic green sheet production
  • Release film for ceramic green sheet production

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0138] (Adjustment of Slippery Coating Solution 1)

[0139] The slippery coating liquid 1 of the following composition was adjusted.

[0140] (Easy Slip Coating Solution 1)

[0141]

[0142] (manufacturing of polyester film)

[0143] The intrinsic viscosity (solvent: phenol / tetrachloroethane = 60 / 40) of the film raw material polymer is 0.62dl / g, and PET resin pellets (PET(II)) containing substantially no particles are reduced at 133Pa. Press down and dry at 135°C for 6 hours. Thereafter, it was supplied to an extruder, melted and extruded into a sheet at about 280° C., and quenched and solidified on a rotating cooling metal roll whose surface temperature was kept at 20° C. to obtain an unstretched PET sheet.

[0144] The unstretched PET sheet was heated to 100° C. in a heated roll set and an infrared heater, and then stretched 3.5 times in the longitudinal direction by a roll set with a peripheral speed difference to obtain a uniaxially stretched PET film.

[0145] Next...

Embodiment 2

[0149] Using a slippery coating in which the silica particles B-3 in the slippery coating solution 1 used in Example 1 were changed to silica particles B-4 (average particle diameter: 450 nm, solid content concentration: 40% by mass) In liquid 2, except for this, it carried out similarly to Example 1, and obtained the mold release film for ultrathin-layer ceramic green sheet manufacture.

Embodiment 3

[0151] Except having changed the easy-slip coating liquid 1 into the following easy-slip coating liquid 3, it carried out similarly to Example 1, and obtained the release film for ultrathin-layer ceramic green sheet manufacture.

[0152] (Easy Slip Coating Solution 3)

[0153]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

[Problem] To provide an excellent release film for producing a ceramic green sheet that can achieve both good winding performance and prevention of pinholes, partial thickness unevenness, etc. even when the ceramic green sheet is thinned. [Solution] A release film for producing ceramic green sheets, which uses a polyester film substantially free of particles as a base material, has a release coating layer on one surface of the base material, and has a release coating layer on the other surface. There is an easy-slip coating layer containing particles on it, the area surface average roughness (Sa) of the easy-slip coating layer is not less than 1nm and not more than 25nm, the maximum protrusion height (P) is not less than 60nm and not more than 500nm, and the average of the contour unit The width (RSm) is 10 μm or less.

Description

technical field [0001] The present invention relates to a release film for producing ceramic green sheets. More specifically, it relates to a release film for ceramic green sheet production capable of achieving both good winding performance and prevention of pinholes, partial thickness unevenness, and the like even when the ceramic green sheet is thinned. Background technique [0002] Conventionally, there has been disclosed a technique for eliminating the problem of the release film in the state where the release film for ceramic green sheet production is wound by making the surface roughness of the base film opposite to the release agent layer (back surface) rough. Defects such as adhesion (blocking) between the front and back of the release film for ceramic green sheet production during storage (for example, refer to Patent Document 1). However, the aforementioned prior art has problems in that the protrusions are large, resulting in pinholes and partial thickness uneven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B28B1/30B32B27/00B32B27/36C09D201/00
CPCB28B1/30B32B27/00B32B27/36C09D201/00C04B35/62218C08J5/18C08J7/04C09D5/20C09D167/00
Inventor 柴田悠介吉野贤二堀川谅
Owner TOYOBO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com