High tensile strength water-based surface treatment agent for automobile leather and preparation method thereof

A high-tensile-strength, water-based surface treatment agent technology, applied in the direction of textiles and papermaking, can solve the problems of toughness and tensile properties without obvious improvement, and achieve the effect of enhancing market competitiveness, improving the working environment, and eliminating potential safety hazards

Inactive Publication Date: 2018-12-18
SUZHOU RUIGAO NEW MATERIAL CO LTD
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the surface treatment method provided by this patent, the composition of the sprayed material is simple, and the toughness and tensile properties of the automobile leather are not significantly improved after treatment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Preparation of water-based surface treatment agent:

[0035] 65 parts of water-based matt polyurethane, 35 parts of water-based flat polyurethane, 0.03 parts of graphene, 3 parts of water-based crosslinking agent, 1 part of water-based leveling agent, 1 part of water-based defoamer, 3 parts of water-based hand feeling agent, 2 parts of thickener , the above are parts by weight. After mixing evenly, the water-based surface treatment agent is obtained by grinding and filtering.

[0036] The TPO automotive leather using this surface treatment agent adopts the GB / T1040.3-2006 test method, and the tensile strength in the warp direction is ≥8MPa, and the tensile strength in the weft direction is ≥8MPa.

Embodiment 2

[0038] Preparation of water-based surface treatment agent:

[0039] 65 parts of water-based matt polyurethane, 35 parts of water-based flat polyurethane, 0.03 parts of graphene, 3 parts of water-based crosslinking agent, 1 part of water-based leveling agent, 1 part of water-based defoamer, 3 parts of water-based hand feeling agent, 2 parts of thickener , the above are parts by weight. After mixing evenly, the water-based surface treatment agent is obtained by grinding and filtering.

[0040] The PU automobile leather using the surface treatment agent adopts the GB / T1040.3-2006 test method, and the tensile strength is 800N / 5cm in the warp direction and 800N / 5cm in the weft direction.

Embodiment 3

[0042] Preparation of water-based surface treatment agent:

[0043]65 parts of water-based matte polyurethane, 35 parts of water-based flat polyurethane, 0.03 parts of graphene, 3 parts of water-based crosslinking agent, 1 part of water-based leveling agent, 1 part of water-based defoamer, 3 parts of water-based hand feeling agent, thickener 2 Parts, all the above are parts by weight. After mixing evenly, the water-based surface treatment agent is obtained by grinding and filtering.

[0044] The PVC automobile leather using the surface treatment agent adopts the GB / T1040.3-2006 test method, and the tensile strength in the warp direction is 500N / 5cm, and the tensile strength in the weft direction is 400N / 5cm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a high tensile strength water-based surface treatment agent for automobile leather and a preparation method thereof. The surface treatment agent comprises the following components by weight: 90-110 parts of waterborne polyurethane, 0.01-0.06 part of graphene, 2-8 parts of a water-borne crosslinking agent, 0.2-1 part of a water-borne leveling agent, 0.2-1 part of a water-borne defoamer, 0.3-3 parts of a water-borne hand feeling agent, and 0.5-5 parts of a thickener. The water-based surface treatment agent provided by the invention utilizes the high strength and good toughness advantages of graphene to greatly improve the tensile strength of automobile leather, adopts waterborne polyurethane to replace the traditional solvent-based polyurethane, eliminates the organicsolvent pollution from the source, eliminates potential safety hazards, improves the working environment of workers, and is eco-environment-friendly, thus enhancing the market competitiveness of automobile leather.

Description

technical field [0001] The invention belongs to the technical field of automobile leather surface treatment, and in particular relates to a high tensile strength water-based surface treatment agent for automobile leather and a preparation method thereof. Background technique [0002] Automotive Interior (Automotive Interior) mainly refers to the automotive products used in the interior modification of the car, involving all aspects of the car interior, such as car steering wheel covers, car seat cushions, car floor mats, car perfume, car pendants, interior decorations, storage boxes, etc. etc. are automotive interior products. [0003] What we call car interiors in China is actually the Interiors System in English. Because this part of auto parts has a certain degree of decoration, the usual translation in the industry is called "car interior". However, from the English "Interiors", we can know that these parts are not only for decoration, but they are very rich in functio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/14D06N3/00
CPCD06N3/14D06N3/0063D06N3/141D06N2209/103D06N2211/28
Inventor 李超高金岗吴丽娜韩立业
Owner SUZHOU RUIGAO NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com