Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A preparation method of poly 1,5-diaminoanthraquinone nanorods

A technology of diaminoanthraquinone and nanorods, which is applied in the field of preparation of conjugated polymer materials, and can solve problems such as ion transmission limitations

Active Publication Date: 2021-05-11
DONGHUA UNIV
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is not yet a very suitable oxidizing agent to polymerize 1,5-diaminoanthraquinone
In addition, poly-1,5-diaminoanthraquinone (PDAA) polymerized by traditional methods is extremely limited in its ion transport due to its dense packing structure.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of poly 1,5-diaminoanthraquinone nanorods
  • A preparation method of poly 1,5-diaminoanthraquinone nanorods
  • A preparation method of poly 1,5-diaminoanthraquinone nanorods

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) Preparation of manganese dioxide nanorods by hydrothermal method: take 0.237g of KMnO 4 and 2.5 mg of NaOH were dissolved in 30 ml of deionized water. In addition, take 0.38g of MnSO 4 ·H 2 O was dissolved in 30 ml of deionized water. Then the two solutions were mixed, added to an 80ml hydrothermal kettle, and reacted in an oven at 140°C for 12h. Finally, the obtained product was collected by suction filtration, and dried in an oven at 60° C. for 12 hours to obtain manganese dioxide nanorods.

[0029] (2) 108.5 mg of manganese dioxide nanorods in step (1) were dissolved in 25 ml of a mixed solution of N,N-dimethylacetamide and ethanol containing sulfuric acid (the concentration of sulfuric acid was 1 M). After that, 297.8 mg of 1,5-diaminoanthraquinone was dissolved in 25 ml of N,N-dimethylacetamide and ethanol mixed solution containing sulfuric acid (the concentration of sulfuric acid was 1M). Then the two solutions were mixed and reacted at 25°C for 48h. Whe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of poly 1,5-diaminoanthraquinone nanorods, comprising: preparing manganese dioxide nanorods by a hydrothermal method; dissolving manganese dioxide nanorods and 1,5-diaminoanthraquinone respectively Mix the obtained manganese dioxide solution and 1,5-diaminoanthraquinone solution in acid-containing ethanol and N,N-dimethylacetamide mixed solution, polymerize, filter with suction, wash, and dry to obtain . The invention utilizes the mixed solvent of oxidant manganese dioxide and ethanol and N,N dimethylacetamide to polymerize 1,5-diaminoanthraquinone, builds a structure that is beneficial to ion transmission, and improves the poly-1,5-diaminoanthraquinone Electrochemical properties of nanorods.

Description

technical field [0001] The invention belongs to the field of preparation of conjugated polymer materials, in particular to a preparation method of poly-1,5-diaminoanthraquinone nanorods. Background technique [0002] With the increasingly severe energy crisis and the deterioration of the global environment, the development of sustainable energy has become a global concern. Although solar energy and wind energy are clean and sustainable, they are difficult to be directly used by people because they are greatly affected by regionality and intermittency. Therefore, it is particularly important to develop efficient energy storage devices to solve this problem. [0003] Supercapacitor is an ideal energy storage device because of its ultra-high power density and energy density, and has become a hot spot in social research. As a new type of conjugated polymer, poly-1,5-diaminoanthraquinone has a wider electrochemical window and higher cycle stability than traditional conjugated c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G61/12
CPCC08G2261/11C08G2261/133C08G2261/18C08G2261/516
Inventor 张超王煜烽刘天西朱天宜李乐刘颖刘思良
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More