A modified fiber-reinforced foamed cement composite floor and its preparation method

A technology of foamed cement and modified fiber, which can be applied to ceramic products, other household utensils, floors, etc., and can solve the problems of all-light concrete due to the variation of light aggregate properties, high cost of reinforced composite wood flooring, and difficult quality monitoring. , to achieve the effects of improving building utilization efficiency, fast construction, low energy consumption in production and use

Inactive Publication Date: 2019-06-04
上海天行新型材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] With the improvement of building energy-saving requirements for building thermal performance and green building promotion, in addition to the comprehensive promotion and use of external wall insulation, ground insulation and sound insulation have also gradually received attention. Most of the existing technologies are based on reinforced composite wood flooring. However, the reinforced composite wood floor is covered in the later stage of home decoration; and because the cost of reinforced composite wood floor is relatively high, nowadays, there is an urgent need for a kind of light weight, high strength, which can be used as a ground cushion and has a Pre-floor with excellent thermal insulation and sound insulation performance
[0005] At present, cast-in-place foam concrete, benzene board, and full-light concrete are mostly used for ground insulation. However, cast-in-place foam concrete is hollow and severely cracked due to the typical sandwich structure of aggregate, clean slurry, and foam due to the layering and segregation of slurry.
The thermal conductivity of benzene board is low, and the heat insulation effect is good, but there are also disadvantages such as easy to be compressed and deformed, fatigue strength deformation, and thermal conductivity increase.
However, the quality of all-light concrete is difficult to monitor due to the variation, instability, and multi-component properties of light aggregates.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A modified fiber-reinforced foamed cement composite floor and its preparation method
  • A modified fiber-reinforced foamed cement composite floor and its preparation method
  • A modified fiber-reinforced foamed cement composite floor and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Embodiment 1: as figure 1 , figure 2 The modified fiber-reinforced foamed cement composite floor shown mainly includes a wear-resistant layer 1, a decorative layer 2, an insulation layer 3, an interface connection layer 4 and a connection notch 5; the decorative layer 2 is a wood grain layer printed on base paper , the decorative layer 2 is arranged under the wear-resistant layer 1, the heat-insulation layer 3 is arranged under the decoration layer 2, the interface connection layer 4 is arranged under the heat-insulation layer 3; the connection notch 5 is arranged on the wear-resistant layer 1, the decoration layer 2 , the side ports of the insulation layer 3 and the interface connection layer 4;

[0045] The thermal insulation layer 3 includes a thermal insulation board 30, an alkali-resistant sealing layer 31, a glass fiber mesh cloth 32 and a low-alkalinity anti-cracking glue layer 33; the thermal insulation board 30 is a cuboid, and the alkali-resistant sealing la...

Embodiment 2

[0064] Embodiment 2: Different from Embodiment 1: insulation board 30 is made of 110 parts of Portland cement, 113 parts of calcium stearate, 6 parts of modified fiber, 10 parts of gypsum, 1.2 parts of diphenylamine-4-sodium sulfonate , prepared by mixing 1 part of alkylphenol polyoxyethylene ether, 10 parts of additives for foamed cement insulation boards, 3 parts of water reducing agent, 6 parts of coupling agent, 7 parts of foaming agent, and 65 parts of water; The modified fiber is mixed with 30 parts of carboxymethyl cellulose, 9 parts of polyamide, 13 parts of cellulose acetate, 12 parts of acrylate, 13 parts of graphene oxide, and 25 parts of diethylene glycol diacrylate before heating After stirring evenly, mix it with ionized water at a mass ratio of 1:15; then ultrasonically disperse and beat to obtain a mixed solution; centrifuge, dry, and grind; the low-alkalinity anti-cracking mortar is made of 12 parts of phosphate cement , 16 parts of sodium chloride and / or calc...

Embodiment 3

[0081] Embodiment 3: Different from Embodiment 1: insulation board 30 is made of 120 parts of Portland cement, 20 parts of calcium stearate, 8 parts of modified fiber, 20 parts of gypsum, 1.6 parts of diphenylamine-4-sodium sulfonate , 2 parts of alkylphenol polyoxyethylene ether, 12 parts of additives for foamed cement insulation boards, 5 parts of water reducing agent, 8 parts of coupling agent, 10 parts of foaming agent, and 80 parts of water are mixed and prepared; The modified fiber is mixed with 50 parts of carboxymethyl cellulose, 10 parts of polyamide, 15 parts of cellulose acetate, 15 parts of acrylate, 20 parts of graphene oxide, and 60 parts of diethylene glycol diacrylate before heating After stirring evenly, mix it with ionized water at a mass ratio of 1:15; then ultrasonically disperse and beat to obtain a mixed solution; centrifuge, dry, and grind; the low-alkalinity anti-cracking mortar is made of 15 parts of phosphate cement , 25 parts of sodium chloride and / o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a modified fibre enhanced foaming cement composite floor. The modified fibre enhanced foaming cement composite floor comprises a wearing layer, a decorative layer, an insulating layer and an interface connecting layer. The decorative layer is arranged below the wearing layer, the insulating layer is arranged below the decorative layer, and the interface connecting layer isarranged below the insulating layer. The preparation method comprises the steps of preparing modified fibre, making an insulation plate, making the insulating layer, and post processing of the insulating layer. The modified fibre enhanced foaming cement composite floor has the advantages of high compressive strength, sound insulation, low thermal conductivity, steady chemical property, environmental protection, small deformation and the like. The construction only needs to use special adhesive mortar to paste directly in the base layer, the working procedure is few, the construction is quick,and the efficiency is high. Product tight seam splices, maintenance and replacement are convenient.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a modified fiber-reinforced foamed cement composite floor and a preparation method thereof. Background technique [0002] Laminate flooring is one type of flooring. However, the composite floor is artificially changed the natural structure of the floor material to achieve a floor whose physical properties meet the expected requirements. Composite flooring often refers to laminate flooring and solid wood composite flooring in the market. [0003] Foamed cement is to fully foam the foaming agent mechanically through the foaming system of the foaming machine, and evenly mix the foam with the cement slurry, and then go through the pumping system of the foaming machine for cast-in-place construction or mold molding. A new type of lightweight thermal insulation material with a large number of closed pores formed by natural conservation. It belongs to the bubble-like therm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04F15/08E04F15/18C04B28/14C04B28/34C04B38/02C04B38/10
CPCC04B28/14C04B28/34C04B38/02C04B38/10E04F15/082E04F15/181E04F2290/04C04B7/02C04B24/08C04B24/20C04B24/32C04B2103/302C04B16/06C04B22/124C04B9/00C04B11/00C04B2103/0057
Inventor 丁以瑟
Owner 上海天行新型材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products