Preparation method of composite nanofiber membrane, composite nanofiber membrane, application of composite nanofiber membrane to enzyme immobilization and immobilized enzyme

A technology of composite nanofibers and nanofibers, which is applied in the directions of immobilization on/in organic carriers, fiber processing, textiles and papermaking, etc., can solve the problems of affecting enzyme immobilization efficiency and unfavorable film formation, so as to improve the surface area ratio and Adsorption effect, multi-adsorption point, high surface area effect

Active Publication Date: 2018-11-06
ANHUI UNIVERSITY OF TECHNOLOGY AND SCIENCE
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Polypeptide nanofibers, as a new nanomaterial, usually have a diameter of only a few nanometers, have obvious nano-effects, have good adsorption properties and good biocompatibility, but polypeptide nanofibers are usually only a few nanometers in length, which is not conducive to film formation. , it is difficult to simply use polypeptide nanofibers to prepare membranes for enzyme immobilization, which will affect the efficiency of enzyme immobilization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of composite nanofiber membrane, composite nanofiber membrane, application of composite nanofiber membrane to enzyme immobilization and immobilized enzyme
  • Preparation method of composite nanofiber membrane, composite nanofiber membrane, application of composite nanofiber membrane to enzyme immobilization and immobilized enzyme

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] The embodiments described below by referring to the figures are exemplary only for explaining the present invention and should not be construed as limiting the present invention.

[0030] Embodiments of the present invention provide a method for preparing a composite nanofiber membrane comprising polypeptide nanofibers, which includes the following steps:

[0031] (1) 130g terminal amino acid is negatively charged Ac-A 6 D-OH polypeptide and 135g of Ac-A whose terminal amino acid is positively charged 6 K-NH 2 The polypeptide, preferably according to the molar ratio of 1:1, is dissolved in trifluoroethanol to form a 1mg / mL solution to obtain a polypeptide mixture, which is stored at -20°C for later use. During implementation, the polypeptide mixture is diluted to 50ng.uL -1 , mixed with ethanol 4:1, cultured at room temperature for 6-10 days, preferably 8 days, to obtain a mixed solution containing polypeptide nanofibers for use, wherein the diameter of the polypeptid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of nanofiber membranes, and particularly relates to a preparation method of a composite nanofiber membrane, the composite nanofiber membrane, application of the composite nanofiber membrane to enzyme immobilization and an immobilized enzyme. An electrostatic spinning solution containing chitosan is adopted for preparing the nanofiber membrane, and the membrane has a good film-forming property and an enzyme-immobilizing function; meanwhile, polypeptide nanofibers are adopted and loaded onto the membrane, in this way, the property of the membrane is further improved, and the enzyme-immobilizing property of the membrane is improved.

Description

technical field [0001] The invention belongs to the field of nanofiber membranes, in particular to a preparation method of a composite nanofiber membrane, a composite nanofiber membrane and its application in enzyme immobilization and immobilized enzymes. Background technique [0002] In recent years, the use of nanofibers as carriers to immobilize enzymes has become a major research hotspot at home and abroad. It mainly has the following advantages: (1) The amount of enzyme loaded is relatively large; (2) It can be separated from the product, which simplifies the purification process, increases the number of repeated use of the enzyme, and reduces the cost of the enzyme; (3) Can be used according to the carrier (4) It reduces the diffusion resistance of the substrate during enzyme catalysis, and the preparation of enzyme carriers with excellent performance is a research hotspot in enzyme immobilization technology. Electrospinning to prepare nanofibers has good performance, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/728D04H1/4382D01D5/00C12N11/12C12N11/08
CPCC12N11/08C12N11/12D01D5/003D04H1/4382D04H1/728
Inventor 刘新华宋远丁
Owner ANHUI UNIVERSITY OF TECHNOLOGY AND SCIENCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap