Badminton antibacterial adhesive and preparation method thereof

An adhesive and badminton technology, applied in the directions of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of nitrocellulose flammability, low bonding strength, brittle coating film, etc., and achieve improved sterilization. Duration, long-lasting antibacterial effect, bleed improvement effect

Active Publication Date: 2018-09-28
盐城大数据资产经营管理有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Usual badminton bottom adhesives and badminton string adhesives use nitrocellulose as the main film-forming material, and use esters such as butyl acetate as solvents, but nitrocellulose is flammable, difficult to store, and the odor of esters such as butyl acetate is relatively large, and This kind of adhesive also has the disadvantages of low bonding strength after film formation, brittle coating film and easy breakage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Badminton antibacterial adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A. Preparation of Regenerated Bamboo Charcoal Micropowder Solution

[0045] (1) Add 0.9% polyvinyl alcohol by volume in deionized water, heat to 100°C in a water bath, and stir until completely dissolved under the action of an electric stirrer;

[0046] (2) Add 3000-mesh bamboo charcoal micropowder with 10% volume of deionized water to the solution in (1), and stir evenly until it is completely dissolved and dispersed to obtain a bamboo charcoal micropowder solution;

[0047] (3) In a 150mL three-neck flask equipped with a condensing device and a stirring bar, add 50mL of an aqueous solution of 0.1mol hydantoin and 0.1molKOH, heat the system to 60°C, and slowly add 0.1mol of allyl group dropwise while stirring. Bromine solution in methanol 20mL, reacted for 2h and then cooled to obtain 3-allyl-5,5-dimethylhydantoin (AM) solution;

[0048] (4) In a 150mL three-necked flask equipped with a condensing device and a stirring bar, add 50mL of AM solution, and at 60°C, add 30...

Embodiment 2

[0061] A. Preparation of Regenerated Bamboo Charcoal Micropowder Solution

[0062] (1) Add 1.5% polyvinyl alcohol by volume to deionized water, heat to 100°C in a water bath, and stir until completely dissolved under the action of an electric stirrer;

[0063] (2) Add 4000-mesh bamboo charcoal micropowder with 25% volume of deionized water to the solution in (1), and stir evenly until it is completely dissolved and dispersed to obtain a bamboo charcoal micropowder solution;

[0064] (3) In a 150mL three-necked flask equipped with a condensing device and a stirring bar, add 50mL of an aqueous solution of 0.2mol hydantoin and 0.2mol KOH, heat the system to 60°C, and slowly add 0.1~0.3mol Allyl bromide in methanol solution 20mL, reacted for 2h and then cooled to obtain 3-allyl-5,5-dimethylhydantoin (AM) solution;

[0065] (4) In a 150mL three-necked flask equipped with a condensing device and a stirring bar, add 50mL of AM solution, and at 60~70°C, add 30mL of bamboo charcoal mi...

Embodiment 3

[0078] A. Preparation of Regenerated Bamboo Charcoal Micropowder Solution

[0079] (1) Add 1.2% polyvinyl alcohol by volume in deionized water, heat to 100°C in a water bath, and stir until completely dissolved under the action of an electric stirrer;

[0080] (2) Add 4000-mesh bamboo charcoal micropowder with 20% volume of deionized water into the solution in (1), and stir evenly until it is completely dissolved and dispersed to obtain a bamboo charcoal micropowder solution;

[0081] (3) In a 150mL three-necked flask equipped with a condensing device and a stirring bar, add 50mL of an aqueous solution of 0.2mol hydantoin and 0.2molKOH, heat the system to 60°C, and slowly add 0.2mol of allyl group dropwise while stirring. Bromine solution in methanol 20mL, reacted for 2h and then cooled to obtain 3-allyl-5,5-dimethylhydantoin (AM) solution;

[0082] (4) At a certain temperature, add 55mL of AM solution to a 150mL three-necked flask equipped with a condensing device and a stir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a badminton antibacterial adhesive and a preparation method thereof. According to the antibacterial adhesive, self-healing mesoporous silica microspheres are subjected to loading for regeneration treatment and then mixed with bamboo charcoal powder with antibacterial, anti-mildew and moisture-absorption effects to prepare a micromicelle core, and then the micromicelle core and a micromicelle shell material of blocked isocyanate betaine serving as an antibacterial material with high fiber binding capability are prepared into a micromicelle type antibacterial repairing agent according to a specific ratio. The badminton antibacterial adhesive prepared by the method has good grafting performance, great antibacterial, antibacterial and moisture-absorption capabilities anda great self-healing effect, and meanwhile the antibacterial material has regenerative performance, good water resistance and good stability of coating a film.

Description

technical field [0001] The invention belongs to the technical field of adhesives, in particular to an antibacterial adhesive for badminton and a preparation method thereof. Background technique [0002] Badminton is an indoor and outdoor sport. For friends who like to play badminton, badminton is a consumable item. After a game, it is not a big problem to consume half a barrel of balls. When encountering better quality, the quantity will be relatively small. In the production process of badminton, it is necessary to use adhesives to bond the feathers and the ball head together, but some low-quality adhesives are not effective in bonding, and the feathers will be separated from the ball head after the shuttlecock has been used for a period of time. Seriously affect the use effect of badminton. [0003] Badminton adhesives include badminton header adhesives, badminton splicing adhesives, badminton bottom adhesives, and badminton string adhesives. Usual badminton bottom adhe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J4/00C09J11/04C09J11/06C09J11/08
CPCC09J4/00C09J11/04C09J11/06C09J11/08
Inventor 潘桂花
Owner 盐城大数据资产经营管理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com