A kind of preparation method of high-strength porous sound-absorbing material

A porous sound-absorbing, high-strength technology, applied in glass manufacturing equipment, manufacturing tools, glass forming, etc., can solve the problem of low utilization of blast furnace slag

Active Publication Date: 2021-05-11
SICHUAN UNIV
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is particularly worth mentioning that the utilization of blast furnace slag in these two patents is relatively low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Add 40.5wt.% high-titanium blast furnace slow cooling slag, 50.5wt.% waste glass powder, 1wt.% AlN, 5wt.% borax. Ball mill and mix at a speed of 180r / min for 30min in a ball mill. Put it into a corundum crucible and send it to a resistance furnace for sintering. First, the temperature is raised to 400°C at a rate of 8°C / min and kept at a temperature of 20 minutes, and then raised to 1020°C at a rate of 10°C / min and kept at a temperature of 60 minutes for sintering. After sintering, cool down to 500°C at a rate of 25°C / s, and finally cool slowly to room temperature at a rate of 5°C / s to prepare a high-strength porous sound-absorbing material.

[0022] The volume density of the high-strength porous sound-absorbing material is 0.95g / cm 3 , The opening rate is 50.43%, the average pore diameter is 1.28mm, the compressive strength is 12.49MPa, and the average sound absorption coefficient is 0.29.

Embodiment 2

[0024] Add 39wt.% high-titanium blast furnace slow cooling slag, 52wt.% waste glass powder, 2wt.% AlN, 7wt.% borax. Ball mill and mix at a speed of 250r / min for 25min in a ball mill. Put it into a corundum crucible and send it to a resistance furnace for sintering. First, the temperature is raised to 400°C at a rate of 5°C / min and kept at a temperature of 20 minutes, and then raised to 1000°C at a rate of 10°C / min and kept at a temperature of 40 minutes for sintering. After sintering, cool to 500°C at a rate of 30°C / s, and finally cool slowly to room temperature at a rate of 4°C / s to prepare a high-strength porous sound-absorbing material.

[0025] The volume density of the high-strength porous sound-absorbing material is 0.96g / cm 3 , The opening rate is 53.62%, the average pore diameter is 0.88mm, the compressive strength is 16.64MPa, and the average sound absorption coefficient is 0.36.

Embodiment 3

[0027] Add 48wt.% high-titanium blast furnace slow cooling slag, 42wt.% waste glass powder, 4wt.% AlN, 6wt.% borax. Ball mill and mix at a speed of 300r / min for 30min in a ball mill. Put it into a corundum crucible and send it to a resistance furnace for sintering. First, the temperature is raised to 400°C at a rate of 8°C / min and kept at a temperature of 20 minutes, and then raised to 1020°C at a rate of 10°C / min and kept at a temperature of 60 minutes for sintering. After sintering, cool to 500°C at a rate of 28°C / s, and finally cool slowly to room temperature at a rate of 5°C / s to prepare a high-strength porous sound-absorbing material.

[0028] The volume density of the high-strength porous sound-absorbing material is 1.17g / cm 3 , The opening rate is 55.34%, the average pore diameter is 0.70mm, the compressive strength is 15.65MPa, and the average sound absorption coefficient is 0.39.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention intends to disclose a method for preparing a high-strength porous sound-absorbing material by using high-titanium blast furnace slowly cooled slag as a main raw material. In this method, firstly, high-titanium blast furnace slow cooling slag is mixed with siliceous raw materials, foaming agent and flux are added to form a batch, and the ball-milled batch is directly put into a container for sintering according to a specified sintering process. The method improves the utilization rate of high-titanium type blast furnace waste slag, reuses waste resources and protects the environment. The high-strength porous sound-absorbing material produced has excellent sound-absorbing performance, low cost, non-combustible, non-toxic, corrosion-resistant, and will not generate dust during installation to endanger health. At the same time, it has higher strength than foam glass sound-absorbing materials, and is expected to be used Sound-absorbing materials for traffic road network noise barriers.

Description

technical field [0001] The invention relates to the field of building sound-absorbing materials, in particular to a high-strength porous sound-absorbing material and a preparation method thereof. Background technique [0002] In recent years, with the rapid development of my country's economic construction, the construction of traffic road network is also changing with each passing day, which greatly facilitates people's travel and material exchange. However, the noise pollution caused by the well-connected roads and a large amount of traffic flow has become increasingly prominent, which has become a major factor that interferes with people's work and rest and endangers their physical and mental health. At present, the more effective solution is to set up sound barriers on both sides of the road in order to achieve the purpose of sound absorption and noise reduction. Traditional sound barrier sound-absorbing materials such as fiber sound-absorbing materials have disadvantag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C11/00C03B19/06E01F8/00
CPCC03B19/06C03C11/007E01F8/00
Inventor 冯可芹严子迪周虹伶
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com