medical cloth

一种医疗用、布帛的技术，应用在医药科学、血管、假体等方向，能够解决低透水性和撕裂强度等问题，达到透水率小、厚度薄、实现细径化的效果

Active Publication Date: 2020-05-05
ASAHI KASEI KK
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0019] The present inventors conducted in-depth research and repeated experiments, and found that by adjusting the twist coefficient of the warp and / or weft, the problems of low water permeability and tear strength can be solved, and then the grafts for branched stent grafts Composed of fabric, and the branches form a specific weave structure, thereby preventing liquid leakage, and completed the present invention

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • medical cloth
  • medical cloth
  • medical cloth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0205]

[0206] Polyethylene terephthalate (PET) was used as a raw material, and melt spinning was performed to wind up an undrawn yarn of 65 decitex.

[0207] The properties of the raw material PET polymerized with the germanium catalyst are as follows.

[0208] Reduced viscosity (ηsp / c): 1.162dl / g

[0209] Titanium content: 2ppm

[0210] Diethylene glycol content: 0.8% by weight

[0211] Oligomer content: 1.2% by weight

[0212] The spinneret holes used were 5-layered spinneret holes with a hole diameter of 0.08 mmφ, the distance between the innermost jet nozzles was 1.7 mm, and the distance between all the rows was 8 mm. The cooling of the filaments basically used a cooling air jetting device having a jetting outlet at an elevation angle of 37°. In addition, under the spinning conditions (the surface temperature of the spinneret hole is 303°C, the temperature distribution of the spinneret hole is 3°C, the length of the hot zone is 36mm, the temperature of the cooling ai...

Embodiment 2

[0222]

[0223] Polyethylene terephthalate (PET) was used as a raw material, and melt spinning was performed to wind up an undrawn yarn of 140 decitex. Microfibers were produced under the same conditions as in Example 1.

[0224]

[0225] By the above-mentioned spinning, a total fineness of 72.4 dtex / 450 filaments was produced as a weft.

[0226] The total fineness used in the warp yarn is 34.1 dtex / 24 filaments, the appropriate spinneret holes are selected, melt spinning is performed, and the draw ratio is set to produce.

[0227]

[0228] Using a known twister, warp yarns were twisted 500 times / m (S direction twist) and weft yarns were twisted 100 times / m (S direction twist) to produce twisted yarns.

[0229]

[0230] Using the above-mentioned warp and weft, under the same conditions as in Example 1, a flat-woven tubular seamless fabric with an inner diameter of 50 mm was produced. Furthermore, scouring and heat setting are performed on this fabric to perform finis...

Embodiment 3

[0232]

[0233] Microfibers were produced under the same conditions as in Example 1.

[0234]

[0235] By the above-mentioned spinning, a total fineness of 20.1 dtex / 155 filaments was produced as a weft. Spinning was performed under the same conditions as in Example 2. As the warp, a total fineness of 34.1 decitex / 24 filaments was produced.

[0236]

[0237] Using a known twister, warp yarns were twisted 500 times / m (S direction twist) and weft yarns were twisted 100 times / m (S direction twist) to produce twisted yarns.

[0238]

[0239] Using the above-mentioned warp and weft, under the same conditions as in Example 1, a flat-woven tubular seamless fabric with an inner diameter of 50 mm was produced. Furthermore, scouring and heat setting are performed on this fabric to perform finishing. The evaluation results of the obtained fabrics are shown in Tables 1 and 2 below.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

We provide medical fabrics that are thin, have high tear strength, and low water permeability. A medical fabric, characterized in that multifilaments with a total fineness of 7 to 80 decitex are disposed in the warp and weft, and at least one of the multifilaments in the warp and weft has a monofilament fineness of 0.5 decitex or less, The weft yarn has a twist coefficient A of 50-2000, a thickness of 10-90 μm, and a water permeability of 300 cc / min / cm before and after needling. 2 the following.

Description

technical field [0001] The present invention relates to fabrics suitable as implantable materials that are thin but have excellent tear strength and water permeability and can be applied to stent grafts, for example, medical fabrics for grafts having branches for stent grafts. Background technique [0002] Conventionally, the treatment of aortic aneurysm has been performed by artificial blood vessel replacement using an artificial blood vessel, but recently, catheter-based endovascular treatment using a stent graft has rapidly expanded. [0003] This is because stent-graft surgery does not involve thoracotomy or laparotomy, so physical and economic burdens are reduced. The stent-graft is loaded into a catheter, inserted through an artery at the base of the leg, and delivered to the surgical site. Therefore, catheters with small diameters are required so that they can also be used in patients with thin arteries, and it is expected that the stent grafts will also be folded sm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61F2/07D03D1/00D03D3/02
CPCD03D3/02A61F2002/065A61F2250/0023A61F2/07A61F2240/001D03D15/33A61F2/95D03D1/00D10B2509/06D03D15/43D01D5/088D06C7/02D10B2331/04
Inventor 中泽彰仁奥野登起男
Owner ASAHI KASEI KK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap