Preparation method of high-solid-content epoxy composite material for badminton racket

A technology for badminton rackets with high solid content, applied to rackets, string-through rackets, sports accessories, etc., can solve the problems of improving the flexibility of epoxy compositions, and achieve the effect of improving flexibility and improving flexibility

Inactive Publication Date: 2018-07-06
卢迪
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the flexibility of epoxy compositions has not been improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-solid-content epoxy composite material for badminton racket

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of high-solid-content epoxy composite material for badminton racket, in parts by weight, comprises the following components

[0030] 73 parts of epoxy resin, 23 parts of butyl methacrylate,

[0031] 7 parts of nano titanium sol, 2.5 parts of curing agent,

[0032] 2.5 parts of amino polyether, 3.5 parts of carboxylated styrene-butadiene rubber,

[0033] 1.5 parts of antirust agent, 2.5 parts of dispersant, 2.5 parts of leveling agent.

[0034] Its preparation method comprises the following steps:

[0035] (1) Add epoxy resin to xylene, heat to 85°C, stir under the protection of nitrogen, add free radical initiator (benzoyl peroxide), drop butyl methacrylate monomer, drop Stop stirring after finishing, and continue to insulate for 4h, after cooling to room temperature, obtain mixed solution A, be the epoxy resin solution of butyl methacrylate modification,

[0036] (2) Add carboxylated styrene-butadiene rubber, amino polyether, and dispersant to mixed solution...

Embodiment 2

[0040] A kind of high-solid-content epoxy composite material for badminton racket, in parts by weight, comprises the following components

[0041] 78 parts of epoxy resin, 24 parts of butyl methacrylate,

[0042] 7.5 parts of nano titanium sol, 2.7 parts of curing agent,

[0043] 4.3 parts of amino polyether, 4.0 parts of carboxylated styrene-butadiene rubber,

[0044] 1.5 parts of antirust agent, 2.8 parts of dispersant, 2.7 parts of leveling agent.

[0045] Its preparation method comprises the following steps

[0046] (1) Add epoxy resin to xylene, heat to 90°C, stir under the protection of nitrogen, add free radical initiator (benzoyl peroxide), drop butyl methacrylate monomer, drop Stop stirring after finishing, and continue to insulate for 4h, after cooling to room temperature, obtain mixed solution A, be the epoxy resin solution of butyl methacrylate modification;

[0047] (2) Add carboxylated styrene-butadiene rubber, amino polyether, and dispersant to mixed solutio...

Embodiment 3

[0051] A kind of high-solid-content epoxy composite material for badminton racket, in parts by weight, comprises the following components

[0052] 82 parts of epoxy resin, 25 parts of butyl methacrylate,

[0053] 8 parts of nano titanium sol, 2 parts of curing agent,

[0054] 4 parts of amino polyether, 3.7 parts of carboxylated styrene-butadiene rubber,

[0055] 2.3 parts of antirust agent, 3.5 parts of dispersant, 3.2 parts of leveling agent.

[0056] Its preparation method comprises the following steps

[0057](1) Add epoxy resin to xylene, heat to 95°C, stir under the protection of nitrogen, add free radical initiator (benzoyl peroxide), drop butyl methacrylate monomer, drop Stop stirring after finishing, and continue to insulate for 4h, after cooling to room temperature, obtain mixed solution A, be the epoxy resin solution of butyl methacrylate modification;

[0058] (2) Add carboxylated styrene-butadiene rubber, amino polyether, and dispersant to mixed solution A and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention aims to provide a high-solid-content epoxy composite material for a badminton racket. The high-solid-content epoxy composite material for the badminton racket is prepared from the following components in parts by weight: 70 to 90 parts of epoxy resin, 20 to 30 parts of butyl methacrylate, 5 to 10 parts of nano-titanium sol, 2 to 3 parts of curing agent, 2.5 to 5.5 parts of amino polyether, 3.5 to 4.5 parts of carboxylic styrene butadiene rubber, 1 to 3 parts of antirust agent, 2 to 4 parts of dispersing agent, and 2.5 to 5 parts of flatting agent. The invention also discloses a preparation method of the composite material. The composite material is higher in solid content and has favorable flexibility at the same time. The composite material also has the characteristics of excellent recoatability, high coverability, and acid and alkali corrosion resistance.

Description

[0001] This application is a divisional application of the invention patent with application number 201610165046.8. Technical field: [0002] The invention designs a high-solid-content epoxy composite material, especially a high-solid-content epoxy composite material suitable for badminton rackets. Background technique: [0003] The coating material with high solid content has good hiding power and large coating area, which can greatly reduce the content of volatile organic compounds in the coating material and the energy consumption of the curing process during the construction process. Therefore, the use of coating materials with high solid content has become the first choice of various businesses, but coating materials with high solid content still have some defects in performance. [0004] Sports rackets will be impacted by balls during use and produce small vibrations, which have higher requirements on the flexibility of coating materials. However, when the solid conte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/08C08L13/00C08L71/00C08K13/02C08K3/22C08F283/10C08F220/18A63B49/10A63B102/04
CPCA63B49/10A63B2102/04A63B2209/00C08F283/10C08K2003/2241C08K2201/011C08L51/08C08L2205/03C08L2205/035C08L13/00C08L71/00C08K13/02C08K2003/2237C08K3/22C08F220/1804
Inventor 董芬芳
Owner 卢迪
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap