Antibacterial and moisture-absorbing bath towel fabric

An antibacterial material and fabric technology, applied in the manufacture of conductive/antistatic filaments, plant fibers, fiber processing, etc., can solve problems such as easy breeding of bacteria, and achieve the effect of inhibiting the production of bacteria, comfortable and healthy use, and good hygroscopic performance.

Active Publication Date: 2019-12-31
HUZHOU KEBO INFORMATION TECH CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the problem that bacteria are easy to breed in bath towels in a humid environment or state, the purpose of the present invention is to provide an antibacterial and moisture-absorbing bath towel fabric, which can inhibit the production of bacteria, has good hygroscopic performance, and is comfortable and healthy to use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] An antibacterial and hygroscopic bath towel fabric is made of the following components: 100g of antibacterial modified polyurethane fiber, 70g of polyethylene terephthalate fiber, 30g of cotton fiber, 20g of apocynum fiber, 20g of bamboo fiber, and the cotton fiber is antibacterial The material liquid is soaked and dried for use.

[0019] The antibacterial modified polyurethane fiber used is made of the following components: 100g polyurethane masterbatch, 30g nano-bamboo charcoal particles, 10g nano-titanium oxide, 3g magnetite powder, 12g lignin powder, 3g boric acid powder, 1g benzalkonium chloride powder, diatom 3g of soil powder, 1.3g of vinyl silane coupling agent and 1g of zinc stearate, the above-mentioned raw material components are made into mixed masterbatch through a screw extruder, and then antistatic modified polyurethane fiber is obtained through wet spinning.

[0020] The used lignin powder is used after being treated by the following process: soak the li...

Embodiment 2

[0026] An antibacterial and moisture-absorbing bath towel fabric is made of the following components: 100g of antibacterial modified polyurethane fiber, 75g of polyethylene terephthalate fiber, 40g of cotton fiber, 22.5g of apocynum fiber, and 25g of bamboo fiber, of which cotton fiber After being soaked in antibacterial liquid, it is used dry.

[0027] The antibacterial modified polyurethane fiber used is made of the following components: 100g polyurethane masterbatch, 35g nano-bamboo charcoal particles, 11.5g nano-titanium oxide, 4g magnetite powder, 14g lignin powder, 4.5g boric acid powder, 1.5g benzalkonium chloride powder , 3.5g of diatomite powder, 1.55g of vinyl silane coupling agent and 1.5g of zinc stearate, the above-mentioned raw material components are made into a mixed masterbatch through a screw extruder, and then obtained by wet spinning Modified polyurethane fibers.

[0028] The lignin powder used is used after being treated by the following process: soak the...

Embodiment 3

[0034]An antibacterial and hygroscopic bath towel fabric is made of the following components: 100g of antibacterial modified polyurethane fiber, 80g of polyethylene terephthalate fiber, 50g of cotton fiber, 25g of apocynum fiber, 30g of bamboo fiber, and the cotton fiber is antibacterial The material liquid is soaked and then dried for use.

[0035] The antibacterial modified polyurethane fiber used is made of the following components: 100g polyurethane masterbatch, 40g nano-bamboo charcoal particles, 13g nano-titanium oxide, 5g magnetite powder, 16g lignin powder, 6g boric acid powder, 2g benzalkonium chloride powder, diatom 4g of soil powder, 1.8g of vinyl silane coupling agent and 2g of zinc stearate, the above-mentioned raw material components are made into mixed masterbatch through a screw extruder, and then antistatic modified polyurethane fiber is obtained through wet spinning.

[0036] The used lignin powder is used after being processed by the following process: soak ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of bath towel fabrics, and in particular to an antimicrobial and moisture-absorbing bath towel fabric. The bath towel fabric is formed by blending antimicrobial modified polyurethane fibers, polyethylene terephthalate fibers, cotton fibers, apocynum venetum fibers and bamboo fibers, wherein the cotton fibers become available as being soaked in antimicrobial material liquid and dried; and the antimicrobial modified polyurethane fibers are added with nano bamboo charcoal particles, nano titanium oxide, magnetite powder, lignin powder, boric acid powder, benzalkonium chloride powder and diatomite powder. The bath towel fabric provided by the invention, through combined actions of the antimicrobial modified polyurethane fibers, the apocynum venetumfibers, the bamboo fibers and the cotton fibers coated with the antimicrobial material liquid, can inhibit the generation of bacteria, and moreover, the bath towel fabric is good in moisture-absorbingperformance and is comfortable and healthy to use.

Description

technical field [0001] The invention relates to the technical field of bath towel fabrics, in particular to an antibacterial and moisture-absorbing bath towel fabric. Background technique [0002] Bath towels are commonly used hygiene products in people's lives. They belong to a category of towels and are made of fibers. They are used for wiping, covering and keeping warm after taking a bath. Because bath towels are often in a humid state or in a humid environment, bacteria are easy to breed on the surface. Since bath towels are daily necessities that directly contact the human body, bacteria are likely to cause skin allergies, dullness, and inflammation. Therefore, the bath towel is required to be cleaned in time after use, and the bath towel itself is also required to have certain antibacterial and antibacterial properties. In addition, the bath towel should have good hygroscopic performance, while the existing common bath towel has a lower hygroscopic performance after b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A47K10/02D01F6/94D01F1/09D01F1/10D06M11/38D06M11/00D06M13/00D06M15/00C08H7/00D06M101/06
CPCA47K10/02C08H6/00D01F1/09D01F1/10D01F1/103D01F6/94D06M11/00D06M11/38D06M13/00D06M15/00D06M16/00D06M2101/06
Inventor 赵志云
Owner HUZHOU KEBO INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com