Ink and preparation method thereof

A technology of ink and scheme, applied in the direction of ink, optics, instruments, etc.

Inactive Publication Date: 2018-02-09
ZHIJING NANOTECH CO LTD
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Professor Zeng Haibo from Nanjing University of Science and Technology reported inorganic CsPbX on Advanced Materials 2015, 27, 7162-7167 3 Synthesis method of perovskite quantum dots, but does not break away from the defect of thermal injection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ink and preparation method thereof
  • Ink and preparation method thereof
  • Ink and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] Scheme I: 2g of PbCl 2 , 2g of CH 3 NH 3 Cl, 400g of N,N-dimethylformamide, 50g of polyvinylidene fluoride, 2g of 5±1nm SiO 2 The ink was obtained by stirring and mixing at 40° C. for 1 hour. The obtained ink parameters are shown in Table 1.

Embodiment 2

[0071] Scheme I: 1g of PbBr 2 , 1g of CH 3 NH 3 Cl, 1000g of toluene, 50g of polyacrylonitrile, 2g of 5±1nmSiO 2 The ink was obtained by stirring and mixing at 40° C. for 1 hour. The obtained ink parameters are shown in Table 1.

Embodiment 3

[0073] Scheme I: 1g of PbBr 2 , 2g of CH 3 CH 2 NH 3 Br, 1000 g of dimethyl sulfoxide, 80 g of polyacrylonitrile, and 2 g of 4±1 nm ZnO were stirred and mixed at 45° C. for 1 hour to obtain the ink. The obtained ink parameters are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface tensionaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides ink and a preparation method thereof and particularly relates to printable ink containing organic-inorganic hybrid perovskite nanocrystals and a preparation method of the ink. The ink is prepared from 0.01wt%-5wt% of the organic-inorganic hybrid perovskite nanocrystals, 70wt%-99wt% of an organic solvent, 1wt%-30wt% of an optical and transparent polymer with a film-forming property and 0.1wt%-10wt% of a stabilizer. The ink has the viscosity ranging from 10 mPaS to 150 mPaS and has the surface tension ranging from 20 mN / m to 70 mN / m.

Description

technical field [0001] The application provides an ink and a preparation method thereof, in particular to a printable ink containing organic-inorganic hybrid perovskite nanocrystals and a preparation method thereof. Background technique [0002] With the rapid development of flexible electronic technology, printed electronic material products on the market are advancing by leaps and bounds. The printed electronic materials that have appeared include organic polymer inks, inorganic nanomaterial inks, and organic polymer inks containing inorganic nanomaterials. Among them, the organic polymer ink containing inorganic nanomaterials has attracted a lot of attention due to its advantages of combining the characteristics of the two materials, and it has great application prospects in the fields of display, energy, environmental protection, transportation, and monitoring. For example, the literature Adv.Mater.2009, 21, 1–5 reported that polyisobutylene is used as the main polymer m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/38C09D11/50G02F1/1335
CPCC09D11/38C09D11/50G02F1/133516
Inventor 曹超伟刘瑞扩
Owner ZHIJING NANOTECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com