Anti-slip wear-resistant ceramic tile preparation method

A ceramic tile and anti-skid technology, applied in the field of ceramic tiles, can solve the problems of low surface friction coefficient of ceramic products, affecting the safe use of products, insufficient surface hardness, etc., and achieve good anti-skid and wear-resistant effect, low gloss and low cost.

Active Publication Date: 2017-11-21
GUANGDONG KITO CERAMICS GROUP CO LTD +2
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current ceramic products (such as ceramic tiles, etc.) have insufficient surface hardness, are not wear-resistant, and are easy to scratch, which affects the appearance of the product; the friction coefficient of the surface of ceramic products is low, not slippery, easy to fall, thus affecting the safety of the product use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-slip wear-resistant ceramic tile preparation method
  • Anti-slip wear-resistant ceramic tile preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] The invention provides a method for preparing an anti-slip and wear-resistant ceramic tile, which mainly includes the following steps: (a) preparing a green body layer; (b) spreading an anti-slip and wear-resistant glaze on the green body layer to form an anti-slip and wear-resistant layer; (c) sintering;

[0034] The anti-slip and wear-resistant glaze is mainly prepared from the following raw materials in parts by mass: 90-110 parts of anti-slip and wear-resistant particles, 90-110 parts of printing paste and 0.2-0.4 parts of sodium tripolyphosphate;

[0035] The anti-skid and wear-resistant particles are mainly composed of the following components in parts by mass: SiO 2 60-70 parts, Al 2 o 3 20-30 parts, Fe 2 o 3 0.01-1 parts, TiO 2 0.1-2 parts, Na 2 O 1-5 parts, K 2 O 1-10 parts, MgO 0.01-1 parts, CaO 0.1-5 parts and ignition loss 0.1-2 parts.

[0036] The preparation method of the above-mentioned anti-slip and wear-resistant ceramic tiles firstly prepar...

Embodiment 1

[0072] A preparation method of anti-slip and wear-resistant ceramic tiles, mainly comprising the following steps: (a) preparing a green body layer: (a1) raw materials for the green body are subjected to batching and dry ball milling for 10 hours to obtain slurry, and the fineness of the slurry is After passing through a 100-mesh sieve, the sieve residue is 5%;

[0073] (a2) The slurry is sieved after deironing, sieving, stale, and spray milling to obtain a blank. The particle gradation of the blank is 0 for 20 mesh and above, 20% for 20-40 mesh, and 20% for 20-60 mesh. 50% for mesh, 8% for less than 100 mesh, and 60-100 mesh for the rest;

[0074] (a3) Pressing and forming the blank by using a mold through a press to obtain the green body layer;

[0075] (b) spraying anti-slip and wear-resistant glaze on the body layer to form an anti-slip and wear-resistant layer;

[0076] The anti-slip and wear-resistant glaze is mainly prepared from the following raw materials in parts by...

Embodiment 2

[0080] A preparation method of anti-slip and wear-resistant ceramic tiles, mainly comprising the following steps: (a) preparing a green body layer: (a1) raw materials for the green body are subjected to batching and dry ball milling for 10 hours to obtain slurry, and the fineness of the slurry is After passing through a 100-mesh sieve, the sieve residue is 5%;

[0081] (a2) The slurry is sieved after deironing, sieving, stale, and spray milling to obtain a blank. The particle gradation of the blank is 0 for 20 mesh and above, 20% for 20-40 mesh, and 20% for 20-60 mesh. 50% for mesh, 8% for less than 100 mesh, and 60-100 mesh for the rest;

[0082] (a3) Pressing and forming the blank by using a mold through a press to obtain the green body layer;

[0083] (b) spraying anti-slip and wear-resistant glaze on the body layer to form an anti-slip and wear-resistant layer;

[0084] The anti-slip and wear-resistant glaze is mainly prepared from the following raw materials in parts by...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
whitenessaaaaaaaaaa
glossaaaaaaaaaa
Login to View More

Abstract

The invention relate to the field of ceramic tiles, in particular to an anti-slip wear-resistant ceramic tile preparation method. The method mainly includes the steps of a), preparing a green-body layer; b), spreading anti-slip wear-resistant glaze on the green-body layer to form an anti-slip wear-resistant layer; c), performing sintering. The anti-slip wear-resistant glaze is mainly prepared from anti-slip wear-resistant particles, printing paste and sodium tripolyphosphate; the anti-slip wear-resistant particles are mainly composed of SiO2, Al2O3, Fe2O3, TiO2, Na2O, K2O, MgO, CaO and ignition loss. The method is simple in operation, scientific and reasonable in process, easy to implement and low in cost, and the anti-slip wear-resistant ceramic tile is good in anti-slip and wear-resistant effects, high in product quality, durable and safe and reliable.

Description

technical field [0001] The invention relates to the field of ceramic bricks, in particular to a preparation method of anti-slip and wear-resistant ceramic bricks. Background technique [0002] With the rapid development of science and technology, people's lives are changing with each passing day. At the same time, an era of pursuing fashion and showing individuality has been created, and the field of building decoration materials is no exception. With its superior performance and decorative effect, ceramic tiles are favored by more and more consumers, and are widely used in people's daily life. Ceramic antique brick is a kind of building decoration material that has become popular in recent years. It has many advantages such as the magnificence of polished brick and the rich and colorful patterns of porcelain tiles, modern or retro charm, and personalization, and is very popular in the market. Consumer favorite. [0003] With the continuous improvement of people's living s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20C04B41/86
CPCC03C8/20C04B41/5022C04B41/86C04B41/4535
Inventor 李德英喻劲军钟礼丰戴永刚
Owner GUANGDONG KITO CERAMICS GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com