A kind of decorative glaze for medium-temperature daily-use ceramics and its application method

A medium-temperature, daily-use technology, applied in the field of decorative glazes for medium-temperature daily-use ceramics, can solve the problems of high cost, low product qualification rate, flow glaze, etc., and achieve the effect of reducing raw material costs, high ornamental value, and strong covering ability

Active Publication Date: 2019-08-27
HUNAN KARPERY INDAL
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition to the special formula matching of multi-layer reaction glaze, the glazing process is relatively complicated and the cost is high; moreover, the firing system is strictly required, and the firing system control is unreasonable. , the product qualification rate is very low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The basic formula of flower glaze by weight percentage: 12% kaolin, 35% quartz, 3% albite feldspar, 3% potassium feldspar, 14% calcite, 12% wollastonite, 3% zinc oxide, 3% titanium dioxide, ashes 5%, calcium phosphate 5%, ammonium molybdate 5%, cerium oxide 3%, yttrium oxide 3%, plus Co 2 o 3 2%;

[0022] The raw materials are divided into two groups according to the basic formula of flower glaze above, wherein the first group of raw materials is composed of kaolin, albite, calcite, zinc oxide, ammonium molybdate, cerium oxide, and the second group of raw materials is composed of quartz, potassium feldspar, silicon Composed of limestone, titanium dioxide, bone ash, calcium phosphate, and yttrium oxide; firstly, the first group of raw materials are mixed, ball milled, and sieved to obtain a particle diameter of D 50 =1um glaze slurry, mix the second group of raw materials, ball mill, and sieve to obtain a particle diameter of D 50 =4um glaze slurry, and then two sets ...

Embodiment 2

[0024] Glaze formulation by weight percentage: 13% kaolin, 40% quartz, 5% albite, 5% potassium feldspar, 9% calcite, 8% wollastonite, 5% zinc oxide, 4% titanium dioxide, bone ash 4 %, calcium phosphate 4%, ammonium molybdate 3%, cerium oxide 2%, yttrium oxide 2%, plus Fe 2 o 3 3%;

[0025] The raw materials are divided into two groups according to the basic formula of flower glaze above, wherein the first group of raw materials is composed of kaolin, albite, calcite, zinc oxide, ammonium molybdate, cerium oxide, and the second group of raw materials is composed of quartz, potassium feldspar, silicon Composed of limestone, titanium dioxide, bone ash, calcium phosphate, and yttrium oxide; firstly, the first group of raw materials are mixed, ball milled, and sieved to obtain a particle diameter of D 50 =1um glaze slurry, mix the second group of raw materials, ball mill, and sieve to obtain a particle diameter of D 50 =4um glaze slurry, and then two sets of glaze slurry with a ...

Embodiment 3

[0027] Glaze formula: kaolin 14%, quartz 28%, albite 4%, potassium feldspar 4%, calcite 14%, wollastonite 11%, zinc oxide 4%, titanium dioxide 5%, bone ash 5%, calcium phosphate 5%, ammonium molybdate 6%, cerium oxide 1%, yttrium oxide 1%, plus MnO 2 4%;

[0028] The raw materials are divided into two groups according to the basic formula of flower glaze above, wherein the first group of raw materials is composed of kaolin, albite, calcite, zinc oxide, ammonium molybdate, cerium oxide, and the second group of raw materials is composed of quartz, potassium feldspar, silicon Composed of limestone, titanium dioxide, bone ash, calcium phosphate, and yttrium oxide; firstly, the first group of raw materials are mixed, ball milled, and sieved to obtain a particle diameter of D 50 =1um glaze slurry, mix the second group of raw materials, ball mill, and sieve to obtain a particle diameter of D 50 =4um glaze slurry, and then two sets of glaze slurry with a particle diameter of D 50 =...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fancy glaze for decorating medium-temperature daily ceramic, and a use method thereof. The base formula of the fancy glaze comprises 10-14 wt% of kaolin, 20-40 wt% of quartz, 2-6 wt% of albite, 2-6% of feldspar, 7-14 wt% of calcite, 7-12 wt% of wollastonite, 2-6 wt% of zinc oxide, 2-6 wt% of titanium dioxide, 2-6 wt% of bone ash, 2-6 wt% of calcium phosphate, 3-6 wt% of ammonium molybdate, 1-3 wt% of cerium oxide, 1-3 wt% of yttrium oxide, and 2-5 wt% of an external coloring oxide. The use method comprises the following steps: carrying out mixing, ball milling and sieving on the above raw materials, applying the obtained raw materials to a medium-temperature daily ceramic briquette, and carrying out medium-temperature one-time sintering to obtain the product. Medium-temperature daily ceramic decorated with the fancy glaze has the advantages of simple process, high adaptability and unique effect, so the fancy glaze has broad market prospect.

Description

technical field [0001] The invention belongs to the field of ceramic glazes, and in particular relates to a decorative glaze for medium-temperature daily-use ceramics and a use method thereof. Background technique [0002] With the improvement of living standards, people are increasingly pursuing high quality of life. Objects used in daily life are no longer simply satisfied with the value of their use, but also require ornamental value. At present, in terms of exterior decoration of daily-use ceramics, there are already a series of decorations such as on-glaze decals, reliefs, over-glaze colors, under-glaze colors, color glazes and comprehensive decorations. In order to meet people's high-quality life needs, decorative glazes, as artistic porcelain decorations, are applied to daily-use ceramics - floral glazed daily-use ceramics emerged as the times require, and are more and more popular with people, and the market prospect is very good. [0003] The so-called flower glaz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/00C04B41/86
Inventor 肖杨李木根
Owner HUNAN KARPERY INDAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products