A shielded Cat6e cable with water-blocking and tensile-resistant functions

A shielding, super six-type technology, applied in the field of machinery, can solve the problems of low expansion rate of plastic expanded microspheres, affecting the final water-blocking performance of the product, uneven expansion, etc. The effect of density

Active Publication Date: 2018-11-02
ZHEJIANG SHIP ELECTRONICS TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the expansion ratio of the plastic expanded microspheres used is low and the expansion is uneven, which affects the final water-blocking performance of the product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A shielded Cat6e cable with water-blocking and tensile-resistant functions
  • A shielded Cat6e cable with water-blocking and tensile-resistant functions
  • A shielded Cat6e cable with water-blocking and tensile-resistant functions

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Prepare the required raw materials by said parts by weight:

[0041] Paraffinic base oil: 25 parts

[0042] Naphthenic oil: 50 parts

[0043] Polymethacrylate: 5 parts

[0044] Ethylene-propylene copolymer: 5 parts

[0045] Fumed silica: 6 parts

[0046] SEP: 3 parts

[0047] Expanded microsphere particles: 4 parts

[0048] Aluminum silicate mineral granules: 2 parts

[0049] N-phenyl-1-naphthylamine: 0.05 parts.

[0050] Place the weighed SEP in paraffinic base oil and naphthenic oil, raise the temperature to 140°C and keep stirring for 70 minutes, add N-phenyl-1-naphthylamine, and continue stirring for 40 minutes; lower the temperature to 95°C, add poly Methacrylate, ethylene-propylene copolymer, and fumed silica were kept warm and stirred thoroughly for 70 minutes; the temperature was lowered to 80°C, the remaining raw materials were added, and fully stirred for 150 minutes to obtain a premix, which was homogeneously ground and vacuum After degassing, the fin...

Embodiment 2

[0052] Prepare the required raw materials by said parts by weight:

[0053] Paraffinic base oil: 20 parts

[0054] Naphthenic oil: 50 parts

[0055] Polymethacrylate: 4 parts

[0056] Ethylene-propylene copolymer: 5 parts

[0057] Fumed silica: 6 parts

[0058] SEB: 4 copies

[0059] Expanded microsphere particles: 5 parts

[0060] Aluminum silicate mineral particles: 1 part

[0061] N-phenyl-2-naphthylamine: 1 part.

[0062] Put the weighed SEB into paraffin base oil and naphthenic oil, raise the temperature to 160°C and keep stirring for 60 minutes, add N-phenyl-2-naphthylamine, continue stirring for 30 minutes; lower the temperature to 100°C, add poly Methacrylate, ethylene-propylene copolymer and fumed silica were kept warm and stirred thoroughly for 70 minutes; the temperature was lowered to 80°C, and the remaining raw materials were added and stirred fully for 150 minutes to obtain a premix, which was homogeneously ground and vacuum After degassing, the final wat...

Embodiment 3

[0064] Prepare the required raw materials by said parts by weight:

[0065] Paraffinic base oil: 22 parts

[0066] Naphthenic oil: 53 parts

[0067] Polymethacrylate: 3 parts

[0068] Ethylene-propylene copolymer: 6 parts

[0069] Fumed silica: 5 parts

[0070] Sebs: 4 servings

[0071] Expanded microsphere particles: 5 parts

[0072] Aluminum silicate mineral granules: 2 parts

[0073] N,N'-diarylbutyl-p-phenylenediamine: 0.05-1 parts.

[0074] Put the weighed SEBS into paraffin base oil and naphthenic oil, raise the temperature to 160°C and keep stirring for 70 minutes, add N,N'-diarylbutyl-p-phenylenediamine, and continue stirring for 40 minutes; lower the temperature to 110°C, add polymethacrylate, ethylene-propylene copolymer and gas-phase silica and keep stirring for 70 minutes; cool down to 80°C, add the remaining raw materials, and stir for 160 minutes to obtain a premix. After homogeneous grinding and vacuum degassing, the final water-blocking ointment is obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of machinery, relates to a cable and particularly discloses a shielding type category-6 type cable with water blocking and tensile functions. The cable comprises a cable core, an inner sheath and an outer sheath from inside to outside in sequence, wherein the cable core is filled with water-blocking ointment to form a diaphragm with moisture in a cable embedded ground; and the water-blocking ointment comprises the following components in parts by weight: 20-30 parts of paraffin-base oil, 50-60 parts of naphthenic oil, 5-10 parts of organic thickening agent, 3-6 parts of fumed silica, 3-5 parts of oil separation inhibitor, 3-8 parts of expanded microsphere particles, 1-3 parts of aluminum silicate salt mineral particles, and 0.05-1 parts of antioxidant. By filling the cable core with the water-blocking ointment, the waterproof performance of the cable is greatly improved, the cable density is lowered, and meanwhile, the impedance performance of the cable is effectively improved, so that the service life of the cable is further prolonged.

Description

technical field [0001] The invention belongs to the technical field of machinery, and relates to a cable, in particular to a shielded Cat6e cable with functions of water resistance and tension resistance. Background technique [0002] With the rapid development of optical communication technology, optical cables have been widely used in the backbone network and inter-office trunk lines of wired communication networks, and it has become an inevitable trend for optical fibers to enter the access network. [0003] Existing data cables include a cross-shaped skeleton and a sheath arranged outside the cross-shaped skeleton, and multiple sets of twisted wire pairs are respectively arranged in the installation grooves corresponding to the skeleton. When a data cable with such a structure is used, each set of wire pairs The relative position of the cable is easy to shift, and the anti-crosstalk performance is weak, which affects the service life of the cable. And the waterproof per...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01B7/18H01B7/20H01B7/282
CPCY02A30/14
Inventor 赵天明张林
Owner ZHEJIANG SHIP ELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap