A kind of preparation method of cellulose/carbon nanotube composite fiber

A carbon nanotube composite and carbon nanotube technology, which is applied in the field of composite fibers, can solve problems such as low efficiency and inability to apply industrial production, and achieve the effects of high thermal ablation residual carbon rate, stable properties, and excellent mechanical properties

Active Publication Date: 2018-11-23
DONGHUA UNIV
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These two methods have the problem of low efficiency and cannot be applied to industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A preparation method of cellulose / carbon nanotube composite fiber, comprising the steps of:

[0032] Using cellulose solvent N-methylmorpholine-N-oxide (NMMO) / water (wherein the proportion of water is 13.8wt%) to dissolve the cellulose with a low polymerization degree of 200 to obtain a low polymerization degree fiber The carrier solution of single-walled carbon nanotubes with a concentration of 6wt%; then the single-walled carbon nanotubes with a purity of 90.1%, a diameter of 0.75nm, and a length of 1 μm are stirred and mixed with the carrier solution by a screw extruder, wherein the stirred The speed is 100 rpm, the duration of stirring is 0.5 hours, the mass ratio of low-polymerization cellulose and single-walled carbon nanotubes is 1:1, and the carbon nanotube mother liquor is obtained; finally, the carbon nanotube mother liquor is added online The method is to inject the cellulose spinning solution with a degree of polymerization of 500 and a concentration of 6wt%...

Embodiment 2

[0035] A preparation method of cellulose / carbon nanotube composite fiber, comprising the steps of:

[0036] Using cellulose solvent N-methylmorpholine-N-oxide (NMMO) / water (wherein the proportion of water is 13.4wt%) to dissolve the cellulose with a low polymerization degree of 500 to obtain a low polymerization degree fiber The carrier solution of single-walled carbon nanotubes with a concentration of 15 wt%; then the single-walled carbon nanotubes with a purity of 90.5%, a diameter of 3 nm, and a length of 5 μm are stirred and mixed with the carrier solution by a kneader, and the stirring speed is 300 rpm / min, the duration of stirring is 1 hour, the mass ratio of cellulose with low degree of polymerization to single-walled carbon nanotubes is 9:1, and the mother liquor of carbon nanotubes is obtained; finally, the mother liquor of carbon nanotubes is injected into the degree of polymerization by adding online 1500, the concentration is 15wt% in the cellulose spinning soluti...

Embodiment 3

[0039] A preparation method of cellulose / carbon nanotube composite fiber, comprising the steps of:

[0040] Using cellulose solvent 1-butyl-3-methylimidazolium chloride salt to dissolve cellulose with a low degree of polymerization of 300 to prepare a carrier solution of single-walled carbon nanotubes with a concentration of cellulose with a low degree of polymerization of 7% by weight; then The single-walled carbon nanotubes with a purity of 90.8%, a diameter of 1nm, and a length of 2μm are mixed with the carrier solution using a screw extruder, wherein the stirring rate is 200 rpm, the stirring time is 0.6 hours, and the degree of polymerization is low. The mass ratio of cellulose to single-walled carbon nanotubes is 10:1, and the carbon nanotube mother liquor is prepared; finally, the carbon nanotube mother liquor is injected into the cellulose spinning solution with a degree of polymerization of 600 and a concentration of 8wt% in the form of online addition. Specifically, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a cellulose / carbon nanotube composite fiber. The preparation method comprises the steps that a cellulose solvent is adopted to dissolve a low-polymerization-degree cellulose, and a carrier solution for carbon nanotubes is prepared; under the strong shear effect provided by a stirring device, the carbon nanotubes is mixed with the carrier solution to prepare a carbon nanotube mother solution; the carbon nanotube mother solution is injected into a cellulose spinning solution in an online adding mode, the spinning solution is subjected to extrusion, solidification and drawing to prepare the cellulose / carbon nanotube composite fiber. For solving the problem that the carbon nanotubes are difficultly and uniformly mixed with a high-viscosity spinning solution, the carbon nanotube mother solution is injected into the cellulose spinning solution, and further the cellulose / carbon nanotube composite fiber is prepared in a spin-forming mode. The mother solution carrier used by the method solidifies and is formed with the fiber without the operation of feeding an additional additive into a solvent and coagulation bath system. The preparation method is simple, flexible and efficient, and production of the cellulose / carbon nanotube composite fiber can be achieved based on a conventional production line.

Description

technical field [0001] The invention relates to the field of composite fibers, in particular to a preparation method of cellulose / carbon nanotube composite fibers. Background technique [0002] Carbon nanotubes are one-dimensional nanomaterials that can be used to improve the mechanical, thermal, and electrical properties of regenerated cellulose fibers. Chinese patent ZL200710036886.5 introduces the preparation method of cellulose / carbon nanotube composite fibers, dispersing carbon nanotubes in N-methylmorpholine-N-material aqueous solution, and then mixing with cellulose pulp to obtain fibers Composite spinning solution, the spinning solution is extruded and coagulated to obtain cellulose / carbon nanotube composite fiber. Chinese patent ZL201010589210.0 mixes a certain proportion of carbon nanotubes, carbon black and ionic liquid, and then dissolves cellulose pulp to obtain a cellulose composite spinning solution, and prepares cellulose / carbon by dry spray wet spinning met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F2/00D01F1/10D01F9/16
CPCD01F1/10D01F2/00D01F9/16
Inventor 靳宏张玉梅王华平李建武吴开建
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com