Glass cleaning agent suitable for spray cleaning and preparation method thereof

A technology of glass cleaning agent and chelating agent, which is applied in the direction of detergent compounding agent, chemical instrument and method, detergent composition, etc., which can solve the problems of easy hanging water drops and achieve good low foam performance

Inactive Publication Date: 2017-02-22
CHENGDU JIAPENG TECH
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the shortcomings of the prior art, to provide a glass cleaning agent suitable for spray cleaning and its preparation method, to solve the disadvantage that water drops are easy to hang on the glass surface after the existing glass cleaning agent cleans the glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass cleaning agent suitable for spray cleaning and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Example 1: Take 6 parts of isomeric C10 fatty alcohol ether (Lutensol XL70), 3 parts of low-foam fatty alcohol alkoxylate (Plurafac LF221), 0.5 part of dodecyl dimethyl betaine (BS-12) As amphoteric surfactant, 5 parts of acid and alkali resistant surfactant (SIMULSOL SL4) as brightener, 5 parts of acrylic acid homopolymer sodium salt (445N), 10 parts of hydrophilic polymer (Surf-S210) as hardener Surface film-forming agent, 0.5 part of disodium ethylenediaminetetraacetic acid (EDTA-2Na) as chelating agent, 10 parts of isopropanol as solvent, 60 parts of demineralized water, set aside.

[0032] Add demineralized water at 30°C to the container, start the agitator to stir the container, add the chelating agent to the demineralized water and stir until completely dissolved, then add isomeric C10 fatty alcohol ether, low-foaming fatty alcohol alkoxylate and amphoteric surfactant and stirred until completely dissolved to obtain solution a.

[0033] Add the brightener to sol...

Embodiment 2

[0035] Example 2: Take 3 parts of isomeric C10 fatty alcohol ether (Lutensol XL70), 2 parts of low-foam fatty alcohol alkoxylate (Plurafac LF221), 1 part of dodecyl dimethyl betaine (BS-12) As an amphoteric surfactant, 3 parts of acid and alkali resistant surfactant (SIMULSOL SL4) as a brightener, 3 parts of acrylic acid homopolymer sodium salt (445N), 8 parts of a hydrophilic polymer (Surf-S210) as a hardener Surface film-forming agent, 0.5 part of disodium ethylenediaminetetraacetic acid (EDTA-2Na) as chelating agent, 15 parts of ethanol as solvent, 64.5 parts of demineralized water, set aside.

[0036] Add demineralized water at 10°C to the container, start the agitator to stir the container, add the chelating agent to the demineralized water and stir until completely dissolved, then add isomeric C10 fatty alcohol ether, low-foaming fatty alcohol alkoxylate and amphoteric surfactant and stirred until completely dissolved to obtain solution a.

[0037] Add the brightener to...

Embodiment 3

[0039] Example 3: 7 parts of isomeric C10 fatty alcohol ether (Lutensol XL70), 3 parts of low-foaming fatty alcohol alkoxylate (Plurafac LF221), 0.5 part of dodecyl dimethyl betaine (BS-12) as Amphoteric surfactant, acid and alkali resistant surfactant (SIMULSOL SL4) 6 parts as brightener, acrylic acid homopolymer sodium salt (445N) 3 parts, hydrophilic polymer (Surf-S210) 7 parts as hard surface As a film-forming agent, 0.5 parts of disodium ethylenediaminetetraacetic acid (EDTA-2Na) is used as a chelating agent, 15 parts of ethanol is used as a solvent, and 58 parts of demineralized water are set aside.

[0040] Add demineralized water at 40°C to the container, start the agitator to stir the container, add the chelating agent to the demineralized water and stir until completely dissolved, then add isomeric C10 fatty alcohol ether, low-foam fatty alcohol alkoxylate and amphoteric surfactant and stirred until completely dissolved to obtain solution a.

[0041] Add the brighte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a glass cleaning agent suitable for spray cleaning and a preparation method thereof. The glass cleaning agent is prepared from the following raw materials in parts by weight: 2-10 parts of isomeric C10 fatty alcohol ether, 2-10 parts of a low foaming type fatty alcohol alkoxy compound, 0.5-2 parts of an ampholytic surfactant, 3-10 parts of a brightening agent, 2-10 parts of acrylic homopolymer sodium salt, 3-15 parts of a hard surface film forming agent, 0.2-1 part of a chelating agent, 10-20 parts of a solvent and 50-70 parts of softened water. The glass cleaning agent disclosed by the invention has the advantages of being low in foaming, easy to rinse and free from water droplet hung on the glass surface after the glass is cleaned; a layer of hydrophilic thin film can be formed on the glass surface, and after being dried, the glass surface is smooth, clean and bright, is suitable for a spray cleaning manner and is naturally dried without being dried in a scraping or wiping manner after being cleaned.

Description

technical field [0001] The invention specifically relates to a glass cleaning agent, in particular to a glass cleaning agent suitable for spray cleaning and a preparation method thereof. Background technique [0002] At present, the glass cleaners on the market are mainly neutral cleaners. After cleaning the glass with such cleaners, water droplets are easy to hang on the glass surface. It must be scraped or wiped dry to achieve a transparent and bright effect; Water drops will leave water stains on the glass surface and affect the appearance of the glass; in summary, this type of glass cleaner is not suitable for spraying glass to clean glass. Contents of the invention [0003] The object of the present invention is to overcome the shortcoming of prior art, provide a kind of glass cleaning agent suitable for spray cleaning and preparation method thereof, to solve the shortcoming that water droplet is easy to hang on the glass surface after cleaning glass with existing gla...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C11D1/94C11D3/60C11D3/37C11D3/33C11D3/20
CPCC11D1/945C11D1/721C11D1/90C11D3/2013C11D3/202C11D3/33C11D3/3746
Inventor 朱云先
Owner CHENGDU JIAPENG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap