Black tea withering method

A technology of withering and black tea, which is applied in the field of black tea withering, which can solve the problems of unfavorable raw tea quality and achieve the effects of shortening the withering time, uniform withering, and accelerating the transformation of the contained substances

Inactive Publication Date: 2017-02-15
柳城县国营伏虎华侨农场茶厂
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, withering must be moderate, both excessive and insufficient are detrimental to the quality of Maocha

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Black tea withering method of the present invention is specifically:

[0023] 1) Pick fresh, undamaged tea tree leaves, place them on a withering rack, wither thickness 2cm, wither time 2 hours, turn 4 times in the middle;

[0024] 2) Place the tea leaves in a withering machine, spread the tea leaves to a thickness of 50 cm, and wither in cold air for 40 minutes;

[0025] 3) Hot air withering for 70 minutes, hot air temperature 38°C;

[0026] 4) Cold wind withering for 60 minutes;

[0027] 5) Hot air withering for 40 minutes, hot air temperature 38°C;

[0028] 6) Shutdown for 1 hour;

[0029] 7) Hot air withering for 140 minutes, the temperature of the hot air is 38°C; during the whole withering process, the tea leaves are turned every 15 minutes.

Embodiment 2

[0031] Black tea withering method of the present invention is specifically:

[0032] 1) Pick fresh, undamaged tea tree leaves and place them on a withering rack with a withering thickness of 3.5 cm and a withering time of 1.5 hours, turning them 5 times in the middle;

[0033] 2) Place the tea leaves in a withering machine, spread the tea leaves to a thickness of 60 cm, and wither in cold air for 30 minutes;

[0034] 3) Hot air wilting for 80 minutes, hot air temperature 40°C;

[0035] 4) Cold wind withering for 50 minutes;

[0036] 5) Hot air withering for 50 minutes, hot air temperature 35°C;

[0037] 6) Shutdown for 1 hour;

[0038] 7) Hot air withering for 150 minutes, the temperature of the hot air is 35°C; during the whole withering process, the tea leaves are turned every 15 minutes.

Embodiment 3

[0040] The black tea withering method of the present invention is specifically as follows: 1) picking fresh, undamaged tea tree fresh leaves, placing them on a withering frame, withering thickness 0.5cm, withering time 2.5 hours, turning 4 times in the middle;

[0041] 2) Place the tea leaves in a withering machine to wither, spread the tea leaves to a thickness of 40cm, and wither in cold air for 45 minutes;

[0042] 3) Hot air withering for 60 minutes, hot air temperature 35°C;

[0043] 4) Cold wind withering for 70 minutes;

[0044] 5) Hot air withering for 30 minutes, hot air temperature 40°C;

[0045] 6) Shutdown for 1 hour;

[0046] 7) Hot air withering for 130 minutes, the temperature of the hot air is 40°C; during the whole withering process, the tea leaves are turned every 15 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a black tea withering method. The black tea withering method comprises the following steps: 1), picking fresh tea leaves from tea trees, placing the picked tea leaves on a withering shelf, wherein the withering thickness is 0.5-3.5 centimeters and the withering time is 1.5-2.5 hours, and turning the tea leaves for 4-5 times during withering; 2) placing the tea leaves in a withering machine, wherein the spreading thickness of the tea leaves is 40-60 centimeters, and withering the tea leaves by using cold air for 30-45 minutes; 3), carrying out withering by using hot air for 60-80 minutes, wherein the temperature of the hot air is 35-40 DEG C; 4), carrying out withering by using cold air for 50-70 minutes; 5), carrying out withering by using hot air for 30-50 minutes, wherein the temperature of the hot air is 35-40 DEG C; 6) stopping the withering machine for 1 hour; and 7), carrying out withering by using hot air for 130-150 minutes, wherein the temperature of the hot air is 35-40 DEG C. The tea leaves are turned once every 15 minutes during the whole withering processes. The black tea withering method has the advantages of accelerating water loss of the fresh leaves, speeding up internal substance transformation in the fresh tea leaves and so on. By adopting the black tea withering method disclosed by the invention, the tea leaves are uniformly and fully withered; moreover, the withering time is greatly reduced.

Description

technical field [0001] The invention belongs to the technical field of tea, and in particular relates to a black tea withering method. Background technique [0002] Withering is the first process of the initial processing of Gongfu black tea, and it is also the basic process for forming the quality of Gongfu black tea. Withering has both the physical dehydration effect and the chemical change process of the contained substances. Through withering, the fresh tea leaves mainly undergo the following two changes: one is to evaporate part of the water, reduce the tension of the fresh tea leaf cells, make the leaves and stems from brittle to soft, increase the toughness of the buds and leaves, and facilitate rolling into strips; The loss of water causes a series of chemical changes in the substances contained in the tea tip, laying the foundation for the material changes in the specific quality of black tea color, aroma and taste. The mastery of the degree of withering has a gre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A23F3/06
CPCA23F3/06
Inventor 何海华罗莲花
Owner 柳城县国营伏虎华侨农场茶厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com