Graphene lubricant additive and preparation method thereof

A lubricating oil additive and graphene technology, applied in the field of lubricating oil, can solve problems such as agglomeration and affecting the dispersion stability of lubricating oil, and achieve the effects of preventing rust and corrosion, increasing anti-oxidation, and increasing airtightness

Active Publication Date: 2017-02-01
ZHENGZHOU UNIV OF IND TECH
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, graphene is prone to agglomeration in lubricating oil, which affects its dispersion stability in lubricating oil.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene lubricant additive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A graphene lubricating oil additive, the formula is as follows: polyvinyl alcohol 30 g, alkyl glucoside 10 g, alkylphenol polyoxyethylene ether 10 g, dimethyl silicone 3 g, lanthanum 3 with a particle size of 20-50nm g, Cu 6 g with a particle size of 20-50nm, SiO with a particle size of 20-50nm 2 6 g, 1 g graphene, 3 g 2,6-di-tert-butyl-4-methylphenol, 3 g benzotriazole, 5 g sodium alkylbenzenesulfonate, 5 g 2-mercaptobenzothiazole, Sodium benzoate 5 g.

Embodiment 2

[0025] A graphene lubricating oil additive, the formula is as follows: polyvinyl alcohol 20 g, alkyl glucoside 5 g, alkylphenol polyoxyethylene ether 5 g, dimethyl silicone 1 g, neodymium 3 with a particle size of 20-50 nm g, Cu 4 g with a particle size of 20-50nm, SiO with a particle size of 20-50nm 2 4 g, 0.1 g graphene, 1 g 2,6-di-tert-butyl-4-methylphenol, 1 g benzotriazole, 3 g sodium alkylbenzenesulfonate, 3 g 2-mercaptobenzothiazole, benzene Sodium formate 3 g.

Embodiment 3

[0027] A graphene lubricating oil additive, the formula is as follows: polyvinyl alcohol 20 g, alkyl glucoside 10 g, alkylphenol polyoxyethylene ether 5 g, dimethyl silicone 3 g, neodymium 1 with a particle size of 20-50 nm g, Cu 6 g with a particle size of 20-50nm, SiO with a particle size of 20-50nm 2 4 g, 1 g graphene, 1 g 2,6-di-tert-butyl-4-methylphenol, 3 g benzotriazole, 3 g sodium alkylbenzenesulfonate, 5 g 2-mercaptobenzothiazole, Sodium Benzoate 3 g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a graphene lubricant additive. The graphene lubricant additive comprises the following raw materials by weight: 20-30 parts of polyving akohol, 5-10 parts of alkyl glycoside, 5-10 parts of alkylphenol polyoxyethylene ether, 1-3 parts of dimethyl silicone, 1-3 parts of rare earth element of which the particle size is 20-50 nm, 4-6 parts of Cu of which the particle size is 20-50 nm, 4-6 parts of SiO of which the particle size is 20-50 nm, 0.1-1 part of graphene, 1-3 parts of 2,6-ditertiary butyl-4-methylphenol, 1-3 parts of benzotriazole, 3-5 parts of sodium alkyl benzene sulfonate, 3-5 parts of 2-mercaptobenzothiazole, and 3-5 parts of sodium benzoate. The graphene lubricant additive is added to the lubricant for passivating the catalytic action of the metal to the oxidation reaction, and inhibiting the oxidation process of the oils, so that the anti-oxygenation effect of the lubricant is enhanced, the service life of the lubricant is prolonged, and the machine can be protected.

Description

technical field [0001] The invention relates to a lubricating oil, in particular to a graphene lubricating oil additive and a preparation method thereof. Background technique [0002] Friction and wear is one of the most common problems encountered in many fields. Friction and wear consume a lot of energy, and a lot of material and equipment are wasted as a result. With the rapid development of science and technology and the improvement of machinery manufacturing technology, a large number of high-speed and heavy-duty working conditions have appeared, which put forward higher requirements for the high-temperature bearing capacity and anti-friction and anti-wear performance of lubricating oil. Lubricant additives are critical to improving lubricant performance. [0003] Lubricating oil is a liquid lubricant used on various types of machinery to reduce friction and protect machinery and processed parts. It mainly plays the role of reducing friction, cooling, sealing, bufferi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M161/00C10N30/18C10N30/12C10N30/16C10N30/06C10N10/02
CPCC10M161/00C10M2201/041C10M2201/05C10M2201/10C10M2207/026C10M2207/046C10M2207/141C10M2209/104C10M2215/223C10M2219/044C10M2219/104C10M2229/041C10N2030/12C10N2030/16C10N2030/18C10N2030/76C10N2010/02
Inventor 郭富强王建军李海英王艳丽侯宏涛
Owner ZHENGZHOU UNIV OF IND TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com