A kind of oil-in-water antirust emulsion with high oil phase content and preparation method thereof

An anti-rust emulsion, oil-in-water technology, applied in the field of anti-corrosion and anti-rust materials, can solve the problem of inability to ensure the sealing of the protective film, and achieve the effect of excellent long-term protection effect, good protection effect and good rust resistance.

Active Publication Date: 2019-02-05
SUZHOU HIMAX AUTOMOBILE PROTECTION MATERIAL
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The anti-rust protective wax is easy to be dispersed by water after forming a film, so the sealing property of the protective film cannot be guaranteed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of oil-in-water antirust emulsion with high oil phase content and preparation method thereof
  • A kind of oil-in-water antirust emulsion with high oil phase content and preparation method thereof
  • A kind of oil-in-water antirust emulsion with high oil phase content and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～4

[0046] Table 1 Composition content and comparative examples of Examples 1-4

[0047]

[0048] Carry out salt spray test to each embodiment and comparative example respectively, the result is as follows. The salt spray test is carried out in accordance with SH / T 0081.

Embodiment 1

[0050] According to the ingredients and proportions of Example 1 in Table 1, heat the wax and base oil to 80-100°C to become A, and heat the anti-rust agent and neutralizer to 80-100°C to become B, and then stir A and B to melt Form oil phase; add emulsifier into water and heat to 80-95°C to form water phase; add water phase to oil phase under stirring, keep warm, stir, neutralize, and cool to form oil-in-water type with high oil phase content Anti-rust lotion.

[0051] The antirust emulsion has the following properties:

[0052] Emulsion type: oil in water

[0053] System solid content: 67.5%;

[0054] Neutral salt spray test results: 0 level after 240 hours; see figure 1 Corrosion comparison chart of the test piece before and after the experiment. in, figure 1 The left is before the salt spray test, and the right is 240 hours after the salt spray test.

Embodiment 2

[0056] According to the composition and ratio of Example 2 in Table 1, the wax and base oil are heated to 80-100°C to become A, and the anti-rust agent and neutralizing agent are heated to 80-100°C to become B, and then A and B are stirred and melted to form Oil phase; add the emulsifier to water and heat to 80-95°C to form a water phase; add the water phase to the oil phase under stirring, keep warm, stir, neutralize, and cool to form an oil-in-water type anti-corrosion oil with high oil phase content. rust lotion.

[0057] The antirust emulsion has the following properties:

[0058] Emulsion type: oil in water

[0059] System solid content: 61%;

[0060] Neutral salt spray test results: after 240 hours, it can be judged as level 0; see image 3 Corrosion comparison chart of the test piece before and after the experiment. in, figure 2 The left is before the salt spray test, and the right is 240 hours after the salt spray test.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides high oil phase content oil-in-water type anti-rusting emulsion. The high oil phase content oil-in-water type anti-rusting emulsion is composed of, by weight, 5-30% of wax, 0-40% of base oil, 1-20% of anti-rusting agents, 0.1-2% of neutralizers, 1-10% of emulsifying agents and water. The proportion of the oil phase in the emulsion can reach 50-78 wt%. A continuous hydrophobic oil film can be formed on the surface of a metal material, the adhesive force is high, and the anti-rusting property is good. The emulsion has excellent spreading permeability, film-forming property, water displacement property, anti-rusting property and construction performance, and a quite good long-term protection effect is achieved for the metal material.

Description

technical field [0001] The invention relates to anticorrosion and antirust materials, in particular to an oil-in-water antirust emulsion with high oil phase content. Background technique [0002] Pure oil or pure oil composition has existed in the field of metal anti-corrosion for a long time. Such compositions generally contain volatile organic solvents, which are prone to fire, environmental pollution, and human health during construction and storage. . Therefore, it has become a trend in recent years to replace oily rust inhibitors with water-based rust inhibitors. [0003] Water-based antirust emulsion has the advantages of stable storage, low odor, convenient construction, good permeability, and no VOC emission problems. However, the antirust emulsion prepared by high temperature emulsification with base oil, wax, antirust agent, corrosion inhibitor, emulsifier, etc. generally forms a soft film type protective film, which is easily washed off by hot water or detergent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23F11/00
Inventor 张吉春徐加勇刘家芳李毅吕明春曾理强沈寅
Owner SUZHOU HIMAX AUTOMOBILE PROTECTION MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com