Flame-retardant and anti-aging fabric processing method

A processing method and anti-aging technology, which is applied in the direction of flame-retardant fibers, textiles, papermaking, fiber treatment, etc., can solve the problems of short service life and poor anti-aging properties, and achieve the purpose of hindering heat transfer, improving flame-retardant performance, and inhibiting combustion Effect

Inactive Publication Date: 2016-10-12
广德毅维纺织有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, some products made of current flame-retardant fabrics have problems such as poor aging resistance and short service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A method for processing flame-retardant and anti-aging fabrics, comprising the following steps:

[0019] (1) Fabrics are made by blending warp and weft yarns;

[0020] (2) Spread the fabric, spray both sides of the fabric with white vinegar with a concentration of 5.2% until moist, then wrap the fabric with non-woven fabric and bury it in the distiller's grains, take it out after keeping it for 2 hours, and then dry the fabric;

[0021] (3) Put the fabric into a cold storage at -10°C and keep it for 30 minutes, and after taking it out, fumigate the fabric with jujube wood burning smoke for 20 minutes;

[0022] (4) Take the attachment solution and heat it to 84°C, spray the attachment solution evenly on both sides of the fabric, and then dry the fabric;

[0023] (5) Mix and stir nano-graphene, nano-silica and water in a ratio of 1:2:5 to prepare a mixture, then heat to 92°C, immerse the fabric in the mixture, soak the fabric in the mixture, and then dry the fabric Dry....

Embodiment 2

[0027] A method for processing flame-retardant and anti-aging fabrics, comprising the following steps:

[0028] (1) Fabrics are made by blending warp and weft yarns;

[0029] (2) Spread the fabric, spray both sides of the fabric with white vinegar with a concentration of 5.2% until moist, then wrap the fabric with non-woven fabric and bury it in the distiller's grains, take it out after keeping it for 2 hours, and then dry the fabric;

[0030] (3) Put the fabric in a cold storage at -15°C and keep it for 30 minutes, and after taking it out, fumigate the fabric with jujube wood burning smoke for 20 minutes;

[0031] (4) Take the attachment solution and heat it to 80°C, spray the attachment solution evenly on both sides of the fabric, and then dry the fabric;

[0032] (5) Mix and stir nano-graphene, nano-silica and water in a ratio of 1:1:5 to prepare a mixture, then heat to 90°C, immerse the fabric in the mixture, soak the fabric in the mixture, and then dry the fabric Dry. ...

Embodiment 3

[0036] A method for processing flame-retardant and anti-aging fabrics, comprising the following steps:

[0037] (1) Fabrics are made by blending warp and weft yarns;

[0038] (2) Spread the fabric, spray both sides of the fabric with white vinegar with a concentration of 5.2% until moist, then wrap the fabric with non-woven fabric and bury it in the distiller's grains, take it out after keeping it for 2 hours, and then dry the fabric;

[0039] (3) Put the fabric into a cold storage at 0°C for 30 minutes, and after taking it out, fumigate the fabric with jujube wood burning smoke for 20 minutes;

[0040] (4) Take the attachment solution and heat it to 88°C, spray the attachment solution evenly on both sides of the fabric, and then dry the fabric;

[0041] (5) Mix and stir nano-graphene, nano-silica and water in a ratio of 1:3:5 to prepare a mixture, then heat to 95°C, immerse the fabric in the mixture, soak the fabric in the mixture, and then dry the fabric Dry.

[0042] Bot...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Provided is a flame-retardant and anti-aging fabric processing method. The method comprises the following steps that fabric is spread, the two faces of the fabric are sprayed with white vinegar with the concentration of 5.2% till the fabric is wet, and the fabric is rolled up, wrapped by non-woven fabrics and embedded in distillers' grains; the fabric is put into a cold storage at -15 DEG C to 0 DEG C for 30 min, and then the fabric is taken out and fumigated with smoke generated through common jujube burning for 20 min; an attachment solution is taken, heated to 80 DEG C to 88 DEG C and evenly sprayed on the surfaces of the two sides of the fabric; nano graphene, nano-silica and water are mixed and stirred to obtain a mixture according to the proportion of 1:1:5 to 1:3:5, heating is conducted to 90 DEG C to 95 DEG C, and the fabric is dipped into the mixture and the dried. The flame retardance of fabric treated through the method is significantly improved, a heat-insulating charring layer is formed in burning of the fabric, the fabric is prevented from being burnt continuously, the fabric has a very good anti-aging property, and in the environment of high temperature, intensive ultraviolet and strong acid and alkali, the property of the fabric is stable, and the flame retardance remains unchanged.

Description

technical field [0001] The invention relates to the technical field of textile fabric production, in particular to a method for processing flame-retardant and anti-aging fabrics. Background technique [0002] In order to avoid the continuation of the fire, flame-retardant fabrics are often used in daily life, such as fire-resistant curtains, flame-retardant carpets for hotels, etc., all in order to reduce the possibility of fire. However, some products made of current flame-retardant fabrics have problems such as poor aging resistance and short service life. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a method for processing flame-retardant and anti-aging fabrics. [0004] The technical problem to be solved by the present invention adopts the following technical solutions to realize: [0005] A method for processing flame-retardant and anti-aging fabrics, comprising the following steps: [0006] (1) Fabric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/188D06M13/144D06M11/79D06M11/74D06M15/01D06M13/00D06M15/15
CPCD06M13/188D06M11/74D06M11/79D06M13/00D06M13/144D06M15/01D06M15/15D06M2200/30
Inventor 王建谊
Owner 广德毅维纺织有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com