Process for synthetic lubricant production

A technology of catalysts and mixtures, applied in lubricating compositions, carbon compound catalysts, chemical instruments and methods, etc., which can solve problems such as loss of lubricating oil yield

Inactive Publication Date: 2016-09-07
EXXONMOBIL CHEM PAT INC
View PDF13 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Thus, the light fractions in the metallocene oligomerization process represent a loss in lube oil yield if they cannot be converted to lube oil products by other means

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for synthetic lubricant production
  • Process for synthetic lubricant production
  • Process for synthetic lubricant production

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0068]Metallocene PAOs can be synthesized using batch mode operation using the following exemplary procedure. A stock solution of purified 1-decene (50 g) and 3.173 g of triisobutylaluminum (TIBA) was injected into a 500 ml flask under nitrogen atmosphere. The reaction flask was then heated to 120° C. with stirring. Another funnel installed on the reaction flask contains 20g toluene, 0.079g TIBA raw material solution, 0.430g rac-ethylenebis(4,5,6,7-tetrahydro-1-indenyl) dichloride A solution of zirconium solution and 0.8012 NCA stock solution was added to the 1-decene mixture within 15 minutes while maintaining the reaction temperature close to 120°C, not more than 3°C up or down. The reaction mixture was stirred at the reaction temperature for 16 hours. The heat was then switched off and the mixture was quenched with 3 ml of isopropanol. The crude product was then washed three times with 100 ml of 5% aqueous NaOH followed by 100 ml of deionized water. The organic layer wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
pour pointaaaaaaaaaa
pour pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a process for synthetic lubricant production. The process for the preparation of oligomeric poly alpha-olefins includes oligomerizing low molecular weight PAO oligomer in the presence of a Lewis acid catalyst such as promoted aluminum trichloride or boron trifluoride under oligomerization conditions. The low molecular weight PAO oligomers used as a feed or feed component of the present process are the light olefinic by-product fractions including the dimers and light fractions from the metallocene-catalyzed PAO oligomerization process which are characterized by a molecular weight of 150 to 600 and a terminal olefin (vinylidene) content of at least 25%.

Description

field of invention [0001] This application is a divisional application of Chinese patent application 200980109216.9. The present disclosure relates to improved production methods for poly-alpha-olefins (PAOs) useful as synthetic lubricant basestocks. Background of the invention [0002] PAOs have been recognized for more than 30 years as a class of materials that are particularly suitable as building blocks for high-performance synthetic lubricants. They have good low temperature fluidity, high thermal and oxidative stability, low evaporation loss at high temperature, high viscosity index, good friction behavior, good hydrolytic stability, and good corrosion resistance. PAOs are non-toxic and miscible with mineral oils, other synthetic hydrocarbon liquids, fluids and esters. Thus, PAOs are suitable for use in engine oils, compressor oils, hydraulic oils, gear oils, greases and functional fluids. The term PAO has been used broadly and commonly to name these lubricant bases...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M107/10C07C2/22C07C2/20C10G50/02
CPCC07C2/22C07C2/34C07C2527/126C07C2531/14C07C2531/22C08F210/14C10G50/02C10G2400/10C08F2500/17C10M107/10C07C2/20C07C2527/1213C10G2300/1088C10M2205/0285
Inventor A·O·帕蒂尔N·扬M·M·吴
Owner EXXONMOBIL CHEM PAT INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com