A kind of manufacturing method of special-shaped hollow thermal insulation polyester low elastic yarn

A polyester low elastic yarn and manufacturing method technology, applied in the field of textile production, can solve problems such as inability to prepare polyester fiber, affect melt viscosity, equipment friction, etc., improve far-infrared emission effect and health care effect, and reduce powder reaction contact area , Promote blood circulation and metabolism

Active Publication Date: 2017-05-03
福建百宏聚纤科技实业有限公司
View PDF34 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is mainly to solve the problems existing in the prior art that adding color masterbatches and matting agents to flame-retardant chips will affect the viscosity of the melt during spinning and the friction on equipment during processing, so it is impossible to prepare colored and flame-retardant materials. Technical problems of burning and matting finished polyester fiber etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of manufacturing method of special-shaped hollow thermal insulation polyester low elastic yarn
  • A kind of manufacturing method of special-shaped hollow thermal insulation polyester low elastic yarn
  • A kind of manufacturing method of special-shaped hollow thermal insulation polyester low elastic yarn

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] A method for manufacturing special-shaped hollow warm polyester low elastic yarn comprises the following steps:

[0063] (1) Preparation of far-infrared and anion-emitting functional powders

[0064] Using jade powder, natural gypsum, bamboo charcoal, and ginseng extract as raw materials, first add bamboo charcoal, natural gypsum and jade powder into the ball mill in proportion, and use the method of dry powder ball mill to grind to prepare mixed mineral powder. Jade powder, natural gypsum Fully mix with bamboo charcoal, and fully contact and replace the minerals in jade powder, natural gypsum and bamboo charcoal during the grinding process, control the average particle size of the powder after grinding to 20-50 microns; then mix the mineral powder after grinding Soak the body in the ginseng extract for 20-45 days, then take it out and dry it naturally to get the pretreated mixed mineral powder, then place the pretreated mixed mineral powder in a nitrogen atmosphere at ...

Embodiment 2

[0086] A method for manufacturing special-shaped hollow warm polyester low elastic yarn comprises the following steps:

[0087] (1) Preparation of far-infrared and anion-emitting functional powders

[0088] Using jade powder, natural gypsum, bamboo charcoal, and ginseng extract as raw materials, first add bamboo charcoal, natural gypsum and jade powder into the ball mill in proportion, and use the method of dry powder ball mill to grind to prepare mixed mineral powder. Jade powder, natural gypsum Fully mix with bamboo charcoal, and fully contact and replace the minerals in jade powder, natural gypsum and bamboo charcoal during the grinding process, control the average particle size of the powder after grinding to 20-50 microns; then mix the mineral powder after grinding Soak the body in the ginseng extract for 20-45 days, then take it out and dry it naturally to get the pretreated mixed mineral powder, then place the pretreated mixed mineral powder in a nitrogen atmosphere at ...

Embodiment 3

[0104] A method for manufacturing special-shaped hollow warm polyester low elastic yarn comprises the following steps:

[0105] (1) Preparation of far-infrared and anion-emitting functional powders

[0106] Using jade powder, natural gypsum, bamboo charcoal, and ginseng extract as raw materials, first add bamboo charcoal, natural gypsum and jade powder into the ball mill in proportion, and use the method of dry powder ball mill to grind to prepare mixed mineral powder. Jade powder, natural gypsum Fully mix with bamboo charcoal, and fully contact and replace the minerals in jade powder, natural gypsum and bamboo charcoal during the grinding process, control the average particle size of the powder after grinding to 20-50 microns; then mix the mineral powder after grinding Soak the body in the ginseng extract for 20-45 days, then take it out and dry it naturally to get the pretreated mixed mineral powder, then place the pretreated mixed mineral powder in a nitrogen atmosphere at ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention relates to a manufacturing method of special-shaped hollow warmth keeping polyester drawn textured yarn. Special-shaped warmth keeping polyester fibers are adopted as raw materials, a DTY elasticity enhancing method is adopted, and the needed special-shaped hollow warmth keeping polyester drawn textured yarn is prepared through a pre-interlaced nozzle, a first roller, a deformation heat box, a cooling plate, a false twister, a second roller, a main interlace nozzle, an auxiliary second roller, a sizing heat box, a third roller and an oiling wheel in a winding formation mode. The special-shaped hollow warmth keeping polyester drawn textured yarn has excellent three-dimensional curling performance and warmth keeping performance; the special-shaped hollow warmth keeping polyester drawn textured yarn is widely applied to home textiles, especially underwear, the elasticity of the polyester drawn textured yarn is between the elasticity of spandex and the elasticity of nylon, and the special-shaped hollow warmth keeping polyester drawn textured yarn can have excellent warmth keeping performance on the basis of keeping excellent elasticity; the special-shaped hollow warmth keeping polyester drawn textured yarn can have an excellent healthcare function through far infrared and anion emitting functional particles added into the fibers, has a coordinated warmth keeping effect and has very excellent use prospects in high-end underwear and decorative fabric.

Description

technical field [0001] The invention relates to the technical field of textile production, in particular to a method for manufacturing special-shaped hollow heat-retaining polyester low elastic yarn. Background technique [0002] Draw texturing yarn (DTY for short) is a textured yarn type of polyester chemical fiber. It uses polyester chip (PET) as raw material, spins polyester pre-oriented yarn (POY) at high speed, and then draws False twist processing. It has the characteristics of short process, high efficiency and good quality. In addition to the characteristics of general polyester high breaking strength and elastic modulus, excellent heat setting, good resilience, heat resistance, light resistance, strong corrosion resistance, easy to wash and quick dry, it also has high bulkiness, It has the characteristics of good heat insulation, comfortable hand feeling and soft luster, and is widely used in home textile and clothing fields. As a hollow polyester low-elastic yar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01D5/092D01D5/24D01D5/253D01F1/10D01F6/92D02G1/02
CPCD01D5/092D01D5/24D01D5/253D01F1/10D01F6/92D02G1/0206
Inventor 谌建国刘智敏鲁传旺陈文阳李艺龙
Owner 福建百宏聚纤科技实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com