A kind of winding molding method of all-composite material shell

A composite material and winding molding technology, which is applied in the field of winding molding of all-composite material shells, can solve the problems of complicated assembly and disassembly of core molds, high inertia of equipment operation, and increased production costs, and achieve simple and practical operation and promotion , Reduce the difficulty of production operations and improve production efficiency

Active Publication Date: 2018-09-04
DALIAN UNIV OF TECH
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problems in the prior art that the central axis deflection is too large due to the excessive weight of the mandrel, the operation inertia of the equipment is large, the control is difficult, the assembly and disassembly process of the mandrel is complicated, and a large amount of water is needed to crack the mandrel. Thereby reducing the molding efficiency and increasing the production cost, and providing a winding molding method for composite material shells with small self-weight, strong controllability, simple structure assembly and disassembly, low environmental pollution, high quality and high efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of winding molding method of all-composite material shell
  • A kind of winding molding method of all-composite material shell
  • A kind of winding molding method of all-composite material shell

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Example 1 According to the design requirements: preform a carbon fiber phenolic resin-based composite shell with an inner wall length of 2000mm, a diameter of 500mm, a head radius of 300mm, two head openings with a diameter of 300mm and 200mm, and a thickness of 10mm. The designed metal rotating shaft 1 has a length of 3000 mm, a diameter of 150 mm and a thickness of 10 mm. The airbag 3 is made of high-temperature-resistant silicon rubber airbag, which is filled with 0.5MPa nitrogen gas 6 and expands. The length of the outer wall is 2000mm, the diameter is 500mm, the radius of the head is 300mm, and the thickness is 5mm; the outer diameter of the positioning flange in the positioning part 2 is 200mm , the inner diameter is 150mm, and the thickness is 30mm; the outer diameter of the fixed flange in the fixed part 4 is 300mm, the inner diameter is 150mm, and the thickness is 20mm.

[0019] figure 1 It is a flow chart of the winding forming method of the present invention...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a winding molding method of all-composite material shells, belongs to the technical field of molding process, and relates to the winding molding method of the all-composite material shells. The winding molding method comprises the steps: firstly, assembling a core mold, and filling a gas bag with light gas; next, carrying out surface treatment of the gas bag; then adopting the winding molding control program to control a winding machine to wind the outer surface of the gas bag with fiber bundles or cloth belts according to the program, and curing and molding according to temperature and time requirements required for molding; and finally, obtaining the composite material shells through a demolding process. The winding molding method has wide applicability, and can be used for manufacturing the composite material shells with different shapes and sizes and meeting a requirement of asymmetric front and back sealing surfaces. The process has good stability, equipment is simple and convenient, low in weight and strong in controllability, and the method is simple, practical, and easy to operate and popularize. Workers are prevented from entering the interior of the core mold for operation, the complex assembly and disassembly processes in a traditional winding process are greatly reduced, the difficulty of production operation is reduced, and the production efficiency is improved.

Description

technical field [0001] The invention belongs to the technical field of forming technology, and relates to a winding forming method for a full composite material shell. Background technique [0002] The existing full-composite shell molding method is to use metal or water-soluble materials as the material of the mandrel, and wrap resin fibers on its surface to obtain a semi-finished composite material. After curing and molding, the mandrel structure is disassembled or broken to obtain a composite Material shell. For example, the Chinese patent application number 2012103112711.3 of Zhao Xueping, Chen Xiaopeng, etc. discloses a water-soluble mandrel for forming a fiber-wound shell and its preparation method. It is easy to be damaged during the process; and for large composite shells with large shell diameter and length-to-diameter ratio and asymmetrical molding requirements for front and rear sealing surfaces, the core mold's self-weight is too large, which poses higher challe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C70/34
CPCB29C70/342
Inventor 赵丹阳王海瑞郭纯方杨睿王敏杰
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com