A kind of pp antibacterial plastic and preparation method thereof

An antibacterial plastic and plasticizer technology, applied in the polymer field, can solve the problems of short service life, poor heat resistance, poor safety, etc., and achieve the effects of simple and convenient operation, super antibacterial properties, and low requirements.

Active Publication Date: 2017-12-12
广州美泰包装科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Organic antibacterial agents have a fast sterilizing speed, and some can effectively kill and inhibit mold. However, in addition to poor safety in use, they also have problems such as poor heat resistance, easy hydrolysis, and short service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of pp antibacterial plastic and preparation method thereof
  • A kind of pp antibacterial plastic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Embodiment 1: the preparation of a kind of PP antibacterial plastic

[0029] Ingredients: 120 parts of polypropylene, 4 parts of dodecyltrimethylammonium chloride, 3 parts of chitosan, 4 parts of betaine, 3 parts of nano-zinc oxide powder, 4 parts of nano-calcium oxide, 1 part of zinc stearate , 1.5 parts of white oil, 2 parts of coupling agent, 1 part of nonylphenol polyoxyethylene ether, 0.5 parts of ethylene-octene copolymer, 0.7 parts of antioxidant, 2 parts of random copolymer of styrene and maleic anhydride , 1 part of plasticizer; coupling agent is a combination of titanate coupling agent and silane coupling agent, the ratio of the two is 2:1; plasticizer is triethyl citrate; antioxidant is 4 , a combination of 4′-thiobis(6-tert-butyl-3-methylphenol) and sodium tripolyphosphate, the ratio of the two is 1:1;

[0030] Preparation includes the following steps:

[0031] (1) Premixing dodecyltrimethylammonium chloride, chitosan, betaine and antioxidant to obtain a p...

Embodiment 2

[0034] Embodiment 2: the preparation of a kind of PP antibacterial plastic

[0035] Ingredients: 100 parts of polypropylene, 3 parts of lauryltrimethylammonium chloride, 2 parts of chitosan, 2 parts of betaine, 2 parts of nano-zinc oxide powder, 3 parts of nano-calcium oxide, 0.5 part of zinc stearate , 0.5 parts of white oil, 0.5 parts of coupling agent, 0.5 parts of nonylphenol polyoxyethylene ether, 0.1 parts of ethylene-octene copolymer, 0.5 parts of antioxidant, 0.1 part of random copolymer of styrene and maleic anhydride , 0.5 parts of plasticizer; coupling agent is a combination of titanate coupling agent and silane coupling agent, the ratio of the two is 2:1; plasticizer is triethyl citrate; antioxidant is 4 , a combination of 4′-thiobis(6-tert-butyl-3-methylphenol) and sodium tripolyphosphate, the ratio of the two is 1:1;

[0036] Preparation includes the following steps:

[0037] (1) Premixing dodecyltrimethylammonium chloride, chitosan, betaine and antioxidant to ...

Embodiment 3

[0040] Embodiment 3: the preparation of a kind of PP antibacterial plastic

[0041] Ingredients: 150 parts of polypropylene, 5 parts of lauryltrimethylammonium chloride, 5 parts of chitosan, 5 parts of betaine, 5 parts of nano zinc oxide powder, 5 parts of nano calcium oxide, 2 parts of zinc stearate , 2 parts of white oil, 5 parts of coupling agent, 2 parts of nonylphenol polyoxyethylene ether, 1 part of ethylene-octene copolymer, 1 part of antioxidant, 3 parts of random copolymer of styrene and maleic anhydride , plasticizer 2 parts; coupling agent is a combination of titanate coupling agent and silane coupling agent, the ratio of the two is 2:1; plasticizer is triethyl citrate; antioxidant is 4 , a combination of 4′-thiobis(6-tert-butyl-3-methylphenol) and sodium tripolyphosphate, the ratio of the two is 1:1;

[0042] Preparation includes the following steps:

[0043] (1) Premixing dodecyltrimethylammonium chloride, chitosan, betaine and antioxidant to obtain a premixed m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention relates to PP antibacterial plastic and a preparation method thereof. The antibacterial plastic is prepared from, by weight, 100-150 parts of polypropylene, 3-5 parts of dodecyl trimethyl ammonium chloride, 2-5 parts of chitosan, 2-5 parts of glycine betaine, 2-5 parts of nano zinc oxide powder, 3-5 parts of nano calcium oxide, 0.5-2 parts of zinc stearate, 0.5-2 parts of white oil, 0.5-5 parts of a coupling agent, 0.5-2 parts of nonylphenol polyoxyethylene ether, 0.1-1 parts of ethylene-1-octene copolymer, 0.5-1 part of antioxidant, 0.1-3 parts of styrene and maleic anhydride random copolymer and 0.5-2 parts of plasticizer.The antibacterial plastic is good in mechanical property and processability, good in flame retardancy, good in antibacterial performance and capable of being used for plastic thin films, pipes, plates and various plastic products.

Description

technical field [0001] The invention belongs to the technical field of polymers, and relates to an antibacterial plastic and a preparation method thereof, in particular to a PP antibacterial plastic and a preparation method thereof. Background technique [0002] At present, plastic products play a very important role in people's daily life and industrial and agricultural production. However, with the change of people's health concept, it is gradually realized that a large number of various healing bacteria that are harmful to human health will grow on the surface of plastic products. In order to effectively prevent and kill the bacteria attached to the plastic surface, people usually add antibacterial agents to the plastic to make antibacterial plastic, so that the plastic itself has antibacterial properties, which can kill or kill the bacteria that are stained on the plastic within a certain period of time. Inhibition, compared with conventional chemical and physical metho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08L5/08C08L91/00C08L71/02C08L23/08C08L35/06C08K13/02C08K5/19C08K3/22C08K5/098
CPCC08K2201/011C08K2201/014C08L23/12C08L2201/08C08L2205/02C08L2205/035C08L5/08C08L91/00C08L71/02C08L23/0815C08L35/06C08K13/02C08K5/19C08K2003/2296C08K2003/2206C08K5/098
Inventor 余家地
Owner 广州美泰包装科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com