MOF-type hierarchical porous material based on zif-8 and its preparation method and application

A ZIF-8, multi-level pore technology, applied in separation methods, chemical instruments and methods, other chemical processes, etc., can solve the problems of removing blockage, unfavorable mesopores of surfactants, increasing production costs, etc., and achieves good thermal stability. good lipophilicity and hydrophobicity

Active Publication Date: 2019-03-22
BEIJING SIDAAN NEW MATERIAL TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this patent has the following disadvantages: the so-called template agent (anionic surfactant) used for pore formation is used, which increases the production cost and the preparation process, and the use of complex surfactants is not only unfavorable for the generation of mesopores, but also because Difficult to remove completely and block some pores between particles
[0007] In the prior art, there is also a method of preparing porous MOF materials using hydrosol, which follows the synthesis method of inorganic mesoporous molecular sieves, but the obtained is still a hierarchical porous material dominated by mesoporous pores between ZIF-8 nanoparticles. The so-called template surfactant makes the pore size distribution of this material very wide, resulting in poor thermal stability and poor adsorption performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • MOF-type hierarchical porous material based on zif-8 and its preparation method and application
  • MOF-type hierarchical porous material based on zif-8 and its preparation method and application
  • MOF-type hierarchical porous material based on zif-8 and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] 1.188 grams (4mmol) of Zn(NO 3 ) 2 ·6H 2 O and 0.656 g (8 mmol) of Hmim were added to 18 mL of absolute ethanol, and 8 mmol of sodium hydroxide was added to stir evenly at room temperature, then transferred to a polytetrafluoroethylene reactor with a capacity of 20 mL and sealed at 100°C for 6 hours. After cooling to room temperature, the jelly-like substance was dried at room temperature to form a dry gel, and then it was extracted and washed with absolute ethanol for 7 hours with a Soxhlet extractor. 150 DEG C of vacuum (0.2mmHg) slough residual ethanol and promptly obtain MOF type hierarchical porous material of the present invention, yield 96% (calculated by Hmim), figure 2 It is the X-ray diffraction pattern of the MOF type hierarchical porous material synthesized, and the nanoparticle particle size is less than 60nm, and Fig. 3 is the scanning electron microscope (SEM) picture of the MOF type hierarchical porous material synthesized, micropore (1.1nm) and mesop...

Embodiment 2

[0043] 1.188 grams (4mmol) of Zn(NO 3 ) 2 ·6H 2 O and 10mmol Hmim were added to 18mL of absolute ethanol, and 10mmol of sodium hydroxide was added, stirred at room temperature, then transferred to a 20ml polytetrafluoroethylene reactor and sealed at 120°C for 6 hours. After cooling to room temperature, the jelly-like substance was dried at room temperature to form a dry gel, and then it was extracted and washed with absolute ethanol for 7 hours with a Soxhlet extractor. 150 DEG C vacuum (0.2mmHg) removes residual ethanol and promptly obtains MOF type hierarchical porous material of the present invention, yield 97% (calculated by Hmim), nano particle size is less than 60nm, micropore (1.1nm) and mesoporous (35nm) , BET specific surface 1670M 2 / g, total pore volume 1.54cm 3 / g, mesopore volume 1.03cm 3 / g.

Embodiment 3

[0045] 1.188 grams (4mmol) of Zn(NO 3 ) 2 ·6H 2 O and 0.656 g (8 mmol) of Hmim were added to 15 mL of absolute ethanol, and 8 mmol of sodium hydroxide was added to stir evenly at room temperature, then transferred to a polytetrafluoroethylene reactor with a capacity of 20 mL and sealed at 120°C for 6 hours. After cooling to room temperature, the jelly-like substance was dried at room temperature to form a dry gel, and then it was extracted and washed with absolute ethanol for 7 hours with a Soxhlet extractor. 150 DEG C vacuum (0.2mmHg) removes residual ethanol and promptly obtains MOF type hierarchical porous material of the present invention, yield 97% (calculated by Hmim), nano particle size is less than 60nm, micropore (1.1nm) and mesoporous (35nm) , BET specific surface 1660M 2 / g, total pore volume 1.47cm 3 / g, mesopore volume 0.97cm 3 / g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
mesoporeaaaaaaaaaa
microporeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to an MOF type hierarchical porous material.The diameter of mesoporous ranges from 2 nm to 50 nm, the size of micropores is smaller than 2 nm, the BET specific surface ranges from 1300 M<2> / g to 1850 M<2> / g, the total pore volume ranges from 1.20 cm<3> / g to 2.80 cm<3> / g, and the pore volume of the mesoporous ranges from 0.5 cm<3> / g to 1.90 cm<3> / g.The preparation method comprises the following steps that 1, metal zinc salt, 2-methylimidazole, alkali and an organic solvent are stirred to be uniform and transferred into a reaction kettle to be subjected to a reaction for 2-12 h at the constant temperature of 80-130 DEG C; 2, the reaction is completed, cooling is performed to reach the room temperature, obtained gel materials are dried under the temperature of 20-50 DEG C to form a dry adhesive, and then extraction and washing are performed for 6 h or longer; 3, finally, heating is performed for 12 h or longer under the vacuum condition at the temperature of 130-150 DEG C, and then the hierarchical porous material is obtained.The micropores are from the ZIF-8 structure, the mesoporous is frame holes between particles, and the hierarchical porous material can be used for adsorbing and purifying organic pollutants.

Description

technical field [0001] The invention belongs to the technical field of porous material synthesis, and in particular relates to a ZIF-8-based MOF type hierarchical porous material and its preparation method and application. Background technique [0002] Metal-organic frameworks (Metal-Organic Frameworks, MOF), also known as metal-organic framework compounds, metal-organic coordination polymers, which use metal ions as coordination centers, and form metal ions with multi-dentate ligands. Complexes with a certain spatial structure, also known as MOF porous materials, are a new type of inorganic-organic hybrid porous materials developed in the past 20 years. Due to its selective adsorption of some gases and organic molecules, it has been widely researched and applied in the world as a new type of porous adsorption material. [0003] Zeolitic imidazolate framework (Zeolitic imidazolate framework, ZIF) material is a new type of nanoporous material with zeolite topological structu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/22B01J20/30B01J20/28B01D53/02C02F1/28
CPCB01D53/02B01D2253/204B01J20/226B01J20/28066B01J20/28073B01J20/28076B01J20/2808B01J20/28083B01J2220/4812C02F1/285
Inventor 田运齐张敏刘春苗
Owner BEIJING SIDAAN NEW MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com