A kind of temperature-resistant real stone paint and preparation method thereof

A real stone paint, temperature-resistant technology, applied in the direction of coating, etc., can solve the problems of increasing construction difficulty, prolonging construction time, and different fluidity, so as to prevent flying sand phenomenon, facilitate gunning, and lower color difference Effect

Active Publication Date: 2018-06-01
广东施彩新材料科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, one of the main problems in the use of real stone paint is the color difference. The real stone paint containing more than two kinds of different sands will appear uneven spots on the surface of the coating film after application. The root cause is this. Due to the different fluidity of different sands, finer sands are more fluid and easy to float on the surface to form the base color, and under the influence of temperature, the fluidity of sand will also be greatly different, construction at different temperatures, The color difference of real stone paint can be greater than 2 grades
Therefore, the current construction time is generally limited to the morning and evening when the temperature is low, while the construction is stopped during the daytime when the visibility is high but the temperature is high, which not only greatly prolongs the construction time, but also increases the difficulty of construction.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of temperature-resistant real stone paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A kind of preparation method of the real stone paint of temperature-resistant construction, it is characterized in that: comprise the steps:

[0043] (1) Primary mixing: Add 2 parts by weight of hydroxyethyl cellulose (250HBR from Ashland) and 1 part by weight of rheological agent (WS-40 from Miron) to 127 parts by weight of water in sequence, stir and mix at a speed of 500r / min, stirring time is 5min;

[0044] (2) Secondary mixing: Add 1 part by weight of pH regulator (AMP-95) to the primary mixed raw materials in step (1). After the hydroxyethyl cellulose is fully dissolved, add 7 parts by weight of antifreeze, 6 Parts by weight of film-forming aid (Texanol from Eastman), 105 parts by weight of emulsion (992 from Bardford) and 1.5 parts by weight of preservative (MV from Sol), and stir evenly;

[0045] (3) Three times of mixing: Add 750 parts by weight of natural colored sand to the raw materials after the second mixing in step (2), and stir and mix. The natural col...

Embodiment 2

[0048] A kind of preparation method of the real stone paint of temperature-resistant construction, it is characterized in that: comprise the steps:

[0049](1) Primary mixing: Add 1 part by weight of hydroxyethyl cellulose (250HBR from Ashland) and 0.1 part by weight of rheological agent (B-4000 from Hymens) to 100 parts by weight of water in sequence, stir and mix, and the stirring speed 400r / min, stirring time is 6min;

[0050] (2) Secondary mixing: Add 0.5 parts by weight of pH regulator (AMP-95) to the primary mixed raw materials in step (1). After the hydroxyethyl cellulose is fully dissolved, add 5 parts by weight of antifreeze, 3 Parts by weight of film-forming aid (Texanol from Eastman), 90 parts by weight of emulsion (8039 from Wanhua), stir evenly;

[0051] (3) Three times of mixing: add 500 parts by weight of natural colored sand to the raw materials after the second mixing in step (2), and stir and mix. The natural colored sand is composed of 470 parts by weight ...

Embodiment 3

[0054] A kind of preparation method of the real stone paint of temperature-resistant construction, it is characterized in that: comprise the steps:

[0055] (1) Primary mixing: Add 3 parts by weight of hydroxyethyl cellulose (250HBR from Ashland) and 2.0 parts by weight of rheological agent (WS-40 from Miron) to 150 parts by weight of water in sequence, stir and mix at a speed of 600r / min, stirring time is 4min;

[0056] (2) Secondary mixing: Add 2.0 parts by weight of pH adjuster (organic amine) to the primary mixed raw materials in step (1). After the hydroxyethyl cellulose is fully dissolved, add 9 parts by weight of antifreeze, 9 parts by weight 1 part film-forming aid (Texanol from Eastman), 120 parts by weight emulsion (992 from Bardford) and 3 parts by weight preservative (MV from Sol), and stir evenly;

[0057] (3) Three times of mixing: add 900 parts by weight of natural colored sand to the raw materials after the second mixing in step (2), and stir and mix. Wherein...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of stone-like coatings, in particular to a stone-like coating resisting temperature variation construction and a preparation method thereof. The stone-like coating is prepared from, by weight, 1-3 parts of hydroxyethyl cellulose, 0.1-2 parts of a rheological agent, 0.1-2 parts of a pH regulator, 5-9 parts of an antifreezing agent, 3-9 parts of a coalescing agent, 90-120 parts of emulsion, 0-3 parts of a preservative, 600-900 parts of natural colored sand in reasonable granular composition and a proper amount of water. By reasonably controlling the fineness and use amount of the natural colored sand and introducing the rheological agent, flowing of the fine sand is greatly hindered, the construction temperature range is widened while good texture is maintained, the problem that the color of the colored sand varies at different temperatures is solved, all-day construction of the stone-like coating can be achieved, and thus working efficiency is improved.

Description

technical field [0001] The invention relates to the technical field of real stone varnish, in particular to a real stone varnish for temperature-resistant construction and a preparation method thereof. Background technique [0002] Real stone paint is a kind of paint with a decorative effect similar to marble and granite. It is mainly made of natural stone powder of various colors, and it is applied to the imitation stone effect of building exterior walls, so it is also called liquid stone. The buildings decorated with real stone paint have natural and real natural color, which gives people elegant, harmonious and solemn aesthetic feeling. It is suitable for indoor and outdoor decoration of all kinds of buildings. Especially when it is decorated on curved buildings, it is vivid and lifelike, and has an effect of returning to nature. Real stone paint has fire protection, waterproof, acid and alkali resistance, and pollution resistance. Non-toxic, tasteless, strong adhesion...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/04C04B26/06C04B26/32C04B111/54
CPCC04B26/06C04B26/32C04B2111/00482C04B2111/542C04B24/383C04B2103/0068C04B2103/0094C04B2103/601C04B2103/61C04B14/068
Inventor 叶邦君钟小秋
Owner 广东施彩新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products