Ultrahigh strength steel wire rope and wire drawing method thereof

An ultra-high-strength, steel wire rope technology, applied in the field of steel wire rope, can solve problems such as unreachable

Active Publication Date: 2016-05-04
济宁长龙钢丝绳有限公司
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing standards often fail to meet the requirements of the breaking force of 190kN required by the customer, and the weight of the zinc layer of the steel wire is not less than 60d

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultrahigh strength steel wire rope and wire drawing method thereof
  • Ultrahigh strength steel wire rope and wire drawing method thereof
  • Ultrahigh strength steel wire rope and wire drawing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0062] The present invention will be further elaborated below through specific examples. It should be noted that the following descriptions are only for explaining the present invention, and do not limit its content.

[0063] According to the materials and control parameters selected for the new structure steel wire rope 6×19W+21-Φ13.2mm for ultra-high-strength conveyor belts, large-scale production can be realized.

[0064] Such as figure 1 As shown, an ultra-high-strength steel wire rope has a structural specification of 6×19W+21-Φ13.2mm (6 indicates the number of side strands; W indicates that the steel strand structure is Valentin; 19 indicates the side strand structure: 1+6+6 / 6; 21 indicates the core strand structure: 3×1+6+6 / 6; 13.2mm indicates the diameter of the wire rope), including core strands and side strands, and the core strands and side strands include central steel wire, Inner layer steel wire and outer layer steel wire, the steel strand structure of the co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
strengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an ultrahigh strength steel wire rope and a wire drawing method thereof. The ultrahigh strength steel wire rope has a structure of 6*19W+21-phi 13.2mm. The ultrahigh strength steel wire rope comprises a core strand and edge strands. Each one of the core strand and edge strands orderly comprises central steel wires, inner layer steel wires and outer layer wires from inside to outside. The core strand has a steel strand structure comprising three central steel wires, six inner layer steel wires and 12 outer steel wires. The edge strand has a steel strand structure comprising one central steel wire, six inner layer steel wires and 12 outer steel wires. Each one of the central steel wire, inner layer steel wires and outer steel wires of the core strand and edge strands is prepared from a ultrahigh strength steel wire with the diameter of 2.60-2.80mm and a zinc layer with weight of 150-200g / m<2> on the surface of the steel wire by drawing. The wire drawing method simplifies a wire drawing process, steel wires of the core strand and edge strands have small diameter difference and under load, steel wire contact stress is reduced. The wire drawing method easily controls uniformity of zinc coating layer weight. The ultrahigh strength steel wire rope has a large density coefficient, a large breaking force and a long service life.

Description

technical field [0001] The invention relates to a steel wire rope, in particular to an ultra-high-strength steel wire rope and a drawing method thereof. Background technique [0002] Wire ropes are used in material handling machinery for lifting, pulling, tensioning and carrying. The steel wire rope has high strength, light weight, stable operation, and is not easy to break suddenly, and the operation is reliable. The load-bearing capacity of steel wire rope is the most important mechanical performance index of steel wire rope, and the breaking force of steel wire rope is a scientific index that can fully reflect the actual load-bearing capacity of steel wire rope. At present, the breaking force of the 6×19W-WSC-Φ13.2mm ultra-high-strength grade in the GB / T12753-2008 steel wire rope standard for conveyor belts is 148kN. With the expansion of many fields such as aerospace and aerospace, the requirements for the breaking force of steel wire ropes are gradually increasing. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21C1/02B21C3/02D07B1/06C23C2/18C23C2/38C21D9/52C21D1/18
CPCB21C1/02B21C3/02C21D1/18C21D9/525C23C2/185C23C2/38D07B1/0673D07B2201/1016D07B2201/102D07B2201/1032D07B2201/2006D07B2205/3025D07B2205/3071D07B2401/2055D07B2801/18D07B2801/10
Inventor 郭占林樊建刚夏承堂陈众
Owner 济宁长龙钢丝绳有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com