Method for improving adsorption performance through modification on molecular sieve

A technology of adsorption performance and molecular sieve, applied in chemical instruments and methods, separation/purification of carbonyl compounds, silicates, etc., can solve problems such as waste of resources, high content, and difficulty in meeting the quality requirements of chemical fiber grade cyclohexanone products , to achieve the effect of improving product quality, strong product competitiveness and reducing pollution

Active Publication Date: 2016-04-20
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Chinese patent CN102491889A, a method for removing hexanal and 2-heptanone in cyclohexanone, using a solid adsorbent to remove hexanal and 2-heptanone impurities from solvent-type cyclohexanone, and controlling the two in cyclohexanone The sum of the content is below 40mg / kg, and the supercritical gas carbon dioxide is used to desorb the adsorbate, but the sum of the content of 2-heptanone and hexanal is about 40mg / kg, which is still relatively high, and it is difficult to meet the requirements of chemical fiber grade cyclohexanone. Product Quality Requirements
[0007] The literature "Research on the Adsorption Performance of Molecular Sieves to Hexanal and 2-Heptanone in Cyclohexanone" uses molecular sieves to adsorb cyclohexanone containing hexanal and 2-heptanone, but does not mention the repeated use of molecular sieves, and Used molecular sieves cannot be desorbed and reused, resulting in waste of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Molecular sieve modification: 5g of powdered ZSM-5 molecular sieve with a silicon-aluminum ratio of 200 was activated at 200°C, and 4mL of a 0.05mol / L lanthanum nitrate aqueous solution was prepared, and the above-mentioned molecular sieve was added under stirring, soaked for 10h, 150°C Dry at 500°C for 6 hours to obtain La-modified ZSM-5 molecular sieve.

[0025] Molecular sieve adsorption: Take 400mL of industrial cyclohexanone product in an iodine measuring bottle, cover the stopper, and add 2g of modified ZSM-5 molecular sieve to it, and put it in a water bath shaker for adsorption. The temperature was 20°C, the shaking speed was 10r / min, and it was filtered after adsorption for 0.5h. The filtrate was analyzed by gas chromatography, and 2-heptanone was not detected.

Embodiment 2

[0027] Molecular sieve modification: 10g of powdered ZSM-5 molecular sieve with a silicon-aluminum ratio of 80, activated at 70°C, added to 9mL of ethanol solution with a concentration of 0.05mol / L phosphotungstic acid, stirred and refluxed at 60°C for 2h, then filtered , dried at 80°C, and calcined at 600°C for 12 hours to obtain ZSM-5 molecular sieve modified with phosphotungstic acid.

[0028] Molecular sieve adsorption: Take 300mL of industrial cyclohexanone product in an iodine measuring bottle, cover the stopper, the content of 2-heptanone is 58.3ppm, add 1g of modified ZSM-5 molecular sieve to it, and put it in a water bath shaker for adsorption. The adsorption temperature was 40°C, the shaking rate was 120r / min, and it was filtered after 48 hours of adsorption. The filtrate was analyzed by gas chromatography, and 2-heptanone was not detected.

Embodiment 3

[0030] Molecular sieve modification: 20g of MCM-41 powdered molecular sieve, activated at 70°C, prepared 10mL aqueous solution of cobalt nitrate with a concentration of 0.2mol / L, added the above molecular sieve under stirring, after stirring for 0.5h, dried at 150°C, dried at 300°C Calcined for 2 hours to obtain Co-modified MCM-41 molecular sieve.

[0031] Molecular sieve adsorption: Take 20mL of industrial cyclohexanone product in an iodine measuring bottle, cover the stopper, the content of 2-heptanone is 40.5ppm, add 6g of modified MCM-41 molecular sieve to it, and put it on a magnetic stirrer for stirring and adsorption , the adsorption temperature was 70°C, the stirring rate was 200r / min, after 6 hours of adsorption, it was filtered, and the filtrate was analyzed by gas chromatography, and 2-heptanone was not detected.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention belongs to the technical field of organic chemistry purification, and relates to a method for improving adsorption performance through modification on a molecular sieve. The method is characterized in that a molecular sieve is subjected to loading or exchange modification with a soluble metal salt or heteropoly acid and the like, and the modified molecular sieve is used to adsorb 2-heptanone in a cyclohexanone finished product, wherein the 2-heptanone content in the cyclohexanone after the adsorbing is less than 5 ppm, such that the product quality is substantially improved, and the product competitiveness is strong. According to the present invention, the modified molecular sieve can be applied multiple times, and provides high adsorption quantity compared with the unmodified molecular sieve, and the molecular sieve achieving the saturated adsorption state can be recycled after the molecular sieve is subjected to the desorption treatment.

Description

technical field [0001] The invention belongs to the technical field of organic chemical purification, and in particular relates to a method for improving adsorption performance by molecular sieve modification. Background technique [0002] Cyclohexanone is an important organic intermediate widely used in fiber, synthetic rubber, industrial coatings, pharmaceuticals, pesticides and other industries. Due to the rapid development of the polyamide industry, cyclohexanone has also developed rapidly as a raw material for the production of caprolactam. The by-products 2-hexanone and 2-heptanone produced in the production process of cyclohexanone are important factors affecting the quality of caprolactam. The content is not high but difficult to remove, which is an urgent problem to be solved. At present, there are research reports that 2-hexanone and 2-heptanone in cyclohexanone are adsorbed and removed by adsorbents, but due to the unsatisfactory adsorption effect and treatment ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J20/16B01J20/28B01J20/30C07C45/79C07C49/403
Inventor 刘卓金汉强何育苗季峰崎
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com