Impregnated paper finished OSB composite floor and preparation method

A composite flooring and impregnated paper technology, applied in the direction of floors, adhesive types, aldehyde/ketone condensation polymer adhesives, etc., can solve the problems of weather resistance, easy loss, poor compatibility of water-based adhesives, etc., and achieve stability Enhanced performance, increased strength, enhanced performance

Active Publication Date: 2016-04-06
DEHUA TB NEW DECORATION MATERIAL CO LTD
View PDF7 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN103171014B (2015-4-15) discloses a preparation method of scientific and technological wood, but the formaldehyde emission of the technological wood is high, the dyeing agent is difficult to penetrate, easy to lose, not weather-resistant, poor compatibility with water-based adhesives, and environmental pollution in the bleaching and dyeing process more serious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Impregnated paper finished OSB composite floor and preparation method
  • Impregnated paper finished OSB composite floor and preparation method
  • Impregnated paper finished OSB composite floor and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] 1. Preparation and transportation of shavings: OSB has higher requirements for raw materials than ordinary particleboards. Generally, its raw materials are single tree species, and the diameter of logs is generally above 80mm. Long planer is used to slice them along the direction of wood fibers. Processing, so that the processed shavings are thin and long strips, and the geometric dimensions are: length 100-120mm, width 14-20mm, thickness 05-0.7mm. In order to ensure that the thin and long shavings are not broken during transportation, the transportation equipment generally adopts belt conveyors, and it is not suitable to use pneumatic conveying equipment. Avoid using screw conveyors to prevent the shavings from being broken under the impact of the cyclone vortex and the extrusion of the spiral blades. Affect the paving effect, and ultimately affect the mechanical properties of the board.

[0052] 2. Drying of shavings: Because OSB shavings are thin and long, it is best...

Embodiment 2

[0071] The impregnated paper facing OSB laminate flooring includes OSB substrate layer, veneer layer, buffer paper layer, balance paper layer, and sprayed decorative paper layer from bottom to top;

[0072] The longitudinal static bending strength of the OSB substrate layer is ≥50MPa, and the water absorption thickness expansion rate is ≤12%;

[0073] The veneer layer is poplar bleached veneer with a thickness of 0.6mm;

[0074] The amount of glue on impregnated kraft paper with a buffer paper layer thickness of 0.4mm is more than 80%;

[0075] The weight of the balanced paper layer is 70g, and the amount of glue is 100%;

[0076] The weight of the sprayed decorative paper is 70g, and the amount of glue is 100%.

[0077] The weight of the buffer paper layer is 90g.

[0078] The volatile content of buffer paper layer, balance paper layer and spray decorative paper layer is 6-9% respectively, and the formaldehyde emission is ≤1.0mg / L.

[0079] The formaldehyde emission of th...

Embodiment 3

[0083] The impregnated paper facing OSB laminate flooring includes OSB substrate layer, veneer layer, buffer paper layer, balance paper layer, and sprayed decorative paper layer from bottom to top;

[0084] The longitudinal static bending strength of the OSB substrate layer is ≥50MPa, and the water absorption thickness expansion rate is ≤12%;

[0085] The veneer layer is poplar bleached veneer with a thickness of 1.2mm;

[0086] The amount of glue on impregnated kraft paper with a buffer paper layer thickness of 0.6mm is more than 80%;

[0087] The weight of the balanced paper layer is 80g, and the amount of glue is 120%;

[0088] The weight of the sprayed decorative paper is 80g, and the amount of gluing is 120%.

[0089] The weight of the buffer paper layer is 130g.

[0090] The volatile content of buffer paper layer, balance paper layer and sprayed decorative paper layer is 9% respectively, and the formaldehyde emission is ≤1.0mg / L.

[0091] The formaldehyde emission of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
weightaaaaaaaaaa
Login to View More

Abstract

The invention relates to a plate, in particular to an impregnated paper finished OSB composite floor and a preparation method. The impregnated paper finished OSB composite floor sequentially comprises an OSB base material layer, a veneer layer, a buffer paper layer, a balance paper layer and a sprayed decorative paper layer from bottom to top. The longitudinal static bending intensity of the OSB base material layer is larger than or equal to 50 MPa, and the water absorption thickness swelling rate of the OSB base material layer is smaller than or equal to 12%. The veneer layer is a poplar bleached veneer, and the thickness ranges from 0.6 mm to 1.2 mm. The buffer paper layer is impregnated kraft paper with the thickness of 0.4 mm to 0.6 mm, and the glue quantity is 80% or above. The weight of the balance paper layer ranges from 70 g to 80 g, and the glue quantity ranges from 100% to 120%. The weight of the sprayed decorative paper ranges from 70 g to 80 g, and the glue quantity ranges from 100% to 120%. The impregnated paper finished OSB composite floor has high environment friendliness, stability and water resistance.

Description

technical field [0001] The invention relates to a board, in particular to an OSB composite floor with an impregnated paper finish and a preparation method thereof. Background technique [0002] Flooring is an essential material in interior decoration. At present, laminate flooring accounts for about 70% of the flooring industry, and has a large market share. Laminate floors generally use urea-formaldehyde resin glue as the adhesive, which has poor water resistance and high water-absorbing thickness expansion rate. Nowadays, the quality of the laminate flooring market is mixed. The limit of formaldehyde emission is generally E1 level, or even E2 level, which seriously affects the indoor air quality after decoration. Moreover, the shortage of resources and the gradual decline of internal quality make consumers doubtful. Oriented strand board (OSB) is made of natural poplar wood, and its formaldehyde emission limit reaches the formaldehyde-free level. At the same time, OSB ha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F15/10C09J161/32C08G12/46C08G12/40C08G12/38
CPCC08G12/38C08G12/40C08G12/46C09J161/32E04F15/102
Inventor 叶交友刘元强沈金祥盛时雄王平杜波翁耀列王进项亮亮
Owner DEHUA TB NEW DECORATION MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com