Slow-released fertilizer capable of decreasing content of heavy metal ions in soil and preparation method thereof

A technology of heavy metal ions and slow-release fertilizers is applied in the field of slow-release fertilizers to achieve the effects of not easy to run off, cost saving and strong economic advantages

Active Publication Date: 2016-03-23
湖南斯多瑞农业发展有限公司
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method interrupts normal agricultural production, takes a long time and is costly, so its application is also limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Slow-released fertilizer capable of decreasing content of heavy metal ions in soil and preparation method thereof
  • Slow-released fertilizer capable of decreasing content of heavy metal ions in soil and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Sodium sulfide (0.5g) and polyvinyl alcohol 400 (50g) were added to water (500g) in sequence, and stirred for 40 minutes to mix the compounds uniformly to form solution A.

[0041] Add aluminum nitrate nonahydrate (2.6g) and magnesium nitrate hexahydrate (3.2g) into water (45g) from which carbon dioxide has been removed to form a mixed solution. While stirring the mixed solution, use 5wt% NaOH to adjust the pH to 7.0, and place the mixed solution at 70 °C, reacted for 2h under the protection of nitrogen, and filtered out the jelly B.

[0042] Then the solution A and the filtered jelly B were mixed evenly in a weight ratio of 1:1, placed at 50°C, and stirred for 5 hours to obtain a jelly solution C.

[0043] Then C and lignin were uniformly mixed in a weight ratio of 10:1, placed at 20°C, stirred and reacted for 1 hour, and D was obtained.

[0044] Finally, mix D and urea in a weight ratio of 11:2, place at 60°C, stir for 3 hours, dry at 65°C for 10 hours, crush and sie...

Embodiment 2

[0046] Sodium sulfide (0.8g) and polyvinyl alcohol 600 (80g) were added to water (600g) in sequence, and stirred for 40 minutes to mix the compounds uniformly to form solution A. Add aluminum nitrate nonahydrate (2.8g) and magnesium nitrate hexahydrate (3.9g) into water (50g) from which carbon dioxide has been removed to form a mixed solution. While stirring the mixed solution, use 10wt% NaOH to adjust the pH to 8.0, and place the mixed solution at 70 °C, under the protection of nitrogen, react for 10 h, and filter out the jelly B. Then, the solution A and the filtered jelly B were mixed evenly at a weight ratio of 2:1, placed at 60° C., stirred and reacted for 8 hours, and the jelly C was obtained. Then C and lignin were uniformly mixed in a weight ratio of 15:1, placed at 50° C., stirred and reacted for 5 hours, and D was obtained. Finally, mix D and urea at a weight ratio of 8:1, place at 80°C, stir for 6 hours, dry at 65°C for 10 hours, crush and sieve, and take granules ...

Embodiment 3

[0048] Sodium sulfide (1.4g) and polyvinyl alcohol 1000 (40g) were added to water (350g) in sequence, and stirred for 10 minutes to mix the compounds uniformly to form solution A. Then aluminum nitrate nonahydrate (3.1g) and magnesium nitrate hexahydrate (3.7g) were added to the water (65g) from which carbon dioxide was removed to form a mixed solution. While stirring the mixed solution, the pH was adjusted to 7.5 with 15wt% NaOH, and the mixed solution was placed at 75 ℃, reacted under nitrogen protection for 6h, and filtered the jelly B. Then the solution A and the filtered jelly B were mixed evenly in a weight ratio of 3:1, placed at 55°C, stirred and reacted for 7 hours, and the jelly C was obtained. Then C and lignin were uniformly mixed in a weight ratio of 35:2, placed at 40° C., stirred and reacted for 10 h, and D was obtained. Finally, mix D and urea in a weight ratio of 11:4, place at 25°C, stir for 1 hour, dry at 65°C for 10 hours, crush and sieve, and take granule...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a slow-released fertilizer capable of decreasing the content of heavy metal ions in soil and a preparation method thereof. The slow-released fertilizer is prepared through a reaction by taking sodium sulfide, polyvinyl alcohol, aluminum nitrate nonahydrate, magnesium nitrate hexahydrate, lignin and urea as the reaction raw materials and taking sulfurated hydrotalcite and lignin as carriers. Sulfur ions in the slow-released fertilizer and the heavy metal ions can form water-insoluble sulfide precipitation, the effect of decreasing the content of migrated heavy metal ions in the soil is achieved, and meanwhile a compound formed by the sulfurated hydrotalcite and the lignin has a slow-release function on the urea. The bi-functional fertilizer does not affect normal agricultural production and can reduce environmental pollution caused by the excessive heavy metal ions in the soil, and the cost of soil treatment is reduced.

Description

Technical field: [0001] The invention provides a slow-release fertilizer capable of reducing the content of heavy metal ions in soil and a preparation method of the slow-release fertilizer, belonging to the field of organic-inorganic composite materials. Background technique: [0002] With the continuous improvement of industrial development and urbanization, land resources are becoming increasingly tense, and the world today is suffering from various environmental problems. Due to the mining and smelting of metal mines, the discharge of industrial and domestic sewage, the application of heavy metal-containing pesticides and fertilizers, and sewage irrigation, the problem of heavy metal pollution in soil has become increasingly serious. According to statistics, the soil area polluted by heavy metals in my country is about 2×10 7 hm 2 , accounting for about 1 / 6 of the country's total arable land. If such soil is used for agricultural production, the content of heavy meta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C05G3/04C05G3/08C05G3/80C05G3/90
CPCC05C5/00C05C9/00C05G3/00C05G3/80C05G3/90C05G5/12C05D5/00C05F11/00
Inventor 李文卓张松张琳
Owner 湖南斯多瑞农业发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More