a copper gong

A technology of gong copper and electrolytic copper, which is applied in the field of gong copper to avoid the difficulty in controlling the content of each element

Active Publication Date: 2018-10-09
ANHUI CHUJIANG TECHCAL NEW MATERIAL CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problems in the prior art that the addition of manganese element in the processing of gong copper is difficult to control, and the product belt shape is difficult to control in subsequent processing, the present invention provides a kind of gong copper, which solves the problem of how to add manganese element, and can be compared Good control of the product belt shape, to get a good sound quality copper gong

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of gong copper of the present invention, the mass percentage of Cu element in gong copper is 60.5~61%, the mass percentage of Sn element is 0.8~1%, the mass percentage of Mn element is 0.025~0.035%, the mass percentage of Pb element is The percentage is not more than 0.008%. When the content of each element meets the requirements of the above standards, the musical instrument reed made of gong copper can have a more beautiful sound quality, which is more in line with the market's quality requirements for gong copper. Specifically in the present embodiment, the mass percentage of Cu element is 60.5%, the mass percentage of Sn element is 0.8%, the mass percentage of Mn element is 0.025%, and the mass percentage of Pb element is 0.008%. It is composed of electrolytic copper, tin Ingots, manganese alloys and zinc ingots are processed after smelting, and the specific processing steps are as follows:

[0033] Step 1: smelting of raw materials;

[0034] The raw materia...

Embodiment 2

[0045] The present embodiment is the same as embodiment 1, and the difference is that the mass percentage of the Cu element in the gong copper of the present embodiment is 61%, the mass percentage of the Sn element is 1%, the mass percentage of the Mn element is 0.035%, and the Pb element The mass percentage is 0.003%, and the annealing temperature in the roller hearth furnace is 650°C.

Embodiment 3

[0047] The present embodiment is the same as embodiment 1, and the difference is that the mass percentage of the Cu element in the gong copper of the present embodiment is 60.8%, the mass percentage of the Sn element is 0.9%, the mass percentage of the Mn element is 0.03%, and the Pb element The mass percentage is 0.006%, and the annealing temperature in the roller hearth furnace is 640°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses sound spring copper, and belongs to the technical field of copper fabrication. The sound spring copper is manufactured by smelting and machining electrolytic copper, tin ingots, manganese alloy and zinc ingots. Finally, the mass percent of the Cu element is 60.5-61%; the mass percent of the Sn element is 0.8-1%; the mass percent of the Mn element is 0.025-0.035%; the mass percent of the Pb element is no more than 0.008%. The sound spring copper is manufactured by the following steps of smelting of raw materials, manufacturing of ingot blanks, hot rolling, edge cutting, cold rolling, inspection and storage. The specific cold rolling process is 2.1 mm-1.05 mm-0.85 mm-0.65 mm-0.5mm-0.39 mm-0.32 mm. According to the technical scheme, the problem that the Mn element is difficult to add can be effectively solved, and the sound spring copper with the good sound quality is obtained.

Description

technical field [0001] The invention relates to the technical field of copper processing, and more specifically, relates to a special gong copper for musical instruments. Background technique [0002] Gong copper is a kind of brass product specially used as musical instrument reed. In order to meet the special requirements of this musical instrument for timbre and the internal quality requirements of environmental protection and non-toxicity of the product, gong copper must be used on the basis of environmentally friendly brass belt products. In addition, adding a certain proportion of manganese can meet the basic requirements of this type of instrument. However, the difficulties in the production of gong copper mainly lie in: (1) when, how, and how much manganese is added; (2) how to transition to subsequent products after smelting and producing gong copper, and how to ensure that the influence of manganese is eliminated Reduce it to a controllable range to ensure the qual...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C9/04C22C1/03C22F1/08
CPCC22C1/03C22C9/04C22F1/08
Inventor 方友胜王明龙秦申海赵世美丁枫
Owner ANHUI CHUJIANG TECHCAL NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com