A manufacturing method and technology for glazed tiles are applied in the field of glazed tile manufacturing to achieve the effects of low manufacturing cost, rich product categories and stable product quality

Active Publication Date: 2017-08-29
FOSHAN SANSHUI NEW PEARL CONSTR CERAMICS IND +2
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] The technical problem to be solved by the present invention is to provide a method for manufacturing glazed tiles with a frosted surface, which can overcome the shortcomings of existing similar methods in terms of technology, manufacturing process, cost and product effect, and is low in cost, Manufacturing method of ceramic glazed tile with stable manufacturing process and better surface frosting effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method of manufacturing glazed tiles with a frosted surface

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037]First, add 35% by weight of quartz, 15% by weight of feldspar, and 5% by weight of hard clay to 25% by weight of plastic clay, stir evenly, and then add 20% by weight of lime powder Mix evenly, then ball mill to remove iron, the fineness reaches 250 mesh sieve: 2.0%. Then, the powder material with a moisture content of 4 to 5% is formed through spray drying and other processes, and is molded into a biscuit kiln by a press with a pressure of 320 bar. The biscuit after biscuit firing is ready for use.

[0038] The raw materials such as frosted dry granules, water and printing paste are mixed according to the formula ratio of 55%: 10%: 35% (weight percentage), and are ground by a high-speed grinder to make frosted dry granulated floral glaze for later use. Wherein frosted dry grain comprises (weight percentage): SiO 2 : 52.66%, Al 2 o 3 : 20.31%, Fe 2 o 3 : 0.15%, TiO 2 : 0.05%, CaO: 11.57%, MgO: 0.93%, K 2 O: 2.65%, Na 2 O: 4.04%, ZnO: 3.44%, SrO: 3.04%, B 2 o 3...

Embodiment 2

[0041] First, add 35% by weight of quartz, 15% by weight of feldspar, and 5% by weight of hard clay to 25% by weight of plastic clay, stir evenly, and then add 20% by weight of lime powder Mix evenly, then ball mill to remove iron, the fineness reaches 250 mesh sieve: 2.0%. Then, the powder material with a moisture content of 4 to 5% is formed through spray drying and other processes, and is molded into a biscuit kiln by a press with a pressure of 320 bar. The biscuit after biscuit firing is ready for use.

[0042] The raw materials such as frosted dry granules, water and printing paste are mixed according to the formula ratio of 55%: 10%: 35% (weight percentage), and are ground by a high-speed grinder to make frosted dry granulated floral glaze for later use. Wherein frosted dry grain comprises (weight percentage): SiO 2 : 52.66%, Al 2 o 3 : 20.31%, Fe 2 o 3 : 0.15%, TiO 2 : 0.05%, CaO: 11.57%, MgO: 0.93%, K 2 O: 2.65%, Na 2 O: 4.04%, ZnO: 3.44%, SrO: 3.04%, B 2 o ...

Embodiment 3

[0045] First, add 35% by weight of quartz, 15% by weight of feldspar, and 5% by weight of hard clay to 25% by weight of plastic clay, stir evenly, and then add 20% by weight of lime powder Mix evenly, then ball mill to remove iron, the fineness reaches 250 mesh sieve: 2.0%. Then, the powder material with a moisture content of 4 to 5% is formed through spray drying and other processes, and is molded into a biscuit kiln by a press with a pressure of 320 bar. The biscuit after biscuit firing is ready for use.

[0046] The raw materials such as frosted dry granules, water and printing paste are mixed according to the formula ratio of 55%: 10%: 35% (weight percentage), and are ground by a high-speed grinder to make frosted dry granulated floral glaze for later use. Wherein frosted dry grain comprises (weight percentage): SiO 2 : 52.66%, Al 2 o 3 : 20.31%, Fe 2 o 3 : 0.15%, TiO 2 : 0.05%, CaO: 11.57%, MgO: 0.93%, K 2 O: 2.65%, Na 2 O: 4.04%, ZnO: 3.44%, SrO: 3.04%, B 2 o ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing method of a glazed tile with a matte surface. The method includes: A. conducting raw material treatment and biscuit firing to make a biscuit; B. spraying ground glaze and cover glaze to the biscuit, performing ink-jet printing, then carrying out silk-screen printing of frosted dry granular fancy glaze to make a glazed tile primary product; and C. subjecting the glazed tile primary product to glaze firing so as to obtain the glazed tile finished product finally. The ceramic glazed tile manufacturing method provided by the invention can overcome the disadvantages of existing similar methods in technology, manufacturing process, cost, product effect and other aspects, and has the advantages of low cost, stable manufacturing process, and excellent surface frosting effect.

Description

technical field [0001] The invention relates to a method for manufacturing glazed tiles with frosted surfaces. Background technique [0002] Ceramic glazed tiles are currently one of the indispensable building decoration materials for home kitchens, bathrooms, balconies, and living rooms. Because of their high strength, wear resistance, easy cleaning, and no special care, they are widely used. Consumers love it. [0003] Traditional ceramic glazed tiles are limited by the types of glaze formulations. There are only two types of gloss effect glazes, matt and bright, which are commonly used. The effect is single, and the individualized and diversified needs of consumers cannot be met. It is a better way to solve this problem to develop a new kind of glazed surface that is different from the existing glazed surface effect, and a method for manufacturing glazed tiles with a frosted surface is one of the effective ways to solve the above problems. [0004] The known methods tha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/04
Inventor 叶德林洪卫李辉黄诗程段佑平
Owner FOSHAN SANSHUI NEW PEARL CONSTR CERAMICS IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap