A method for producing metallized pellets by direct reduction of sensible heat of high-temperature oxidation pellets

A technology of metallized pellets and oxidized pellets, which is applied in the field of metallurgy, can solve the problems of reducing energy consumption and production costs, long reduction time, high production and operation costs, etc., and achieves the reduction of total carbon emissions, stable reduction temperature, and good reduction effect of effect

Inactive Publication Date: 2017-06-27
泉州寰锋冶金技术有限责任公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Among them, the traditional coal-based tunnel kiln method to produce direct reduced iron (sponge iron) must use expensive refractory tanks (consumption of refractory tanks per ton of reduced iron is generally 230 to 280 yuan / ton), and the annual production capacity of a single production line is at most not To 30,000 tons, backward process equipment, low production capacity, large area, high energy consumption, long reduction time, high production and operation costs, high labor intensity, poor product quality, etc., resulting in high production and operation costs and poor sales. question
[0006] Although the coal-based tankless tunnel kiln method can abandon the expensive silicon carbide tank of the tunnel kiln method, greatly shorten the reduction time, reduce energy consumption and production costs, it can also combine various high-grade ores, various low-poor and refractory iron ores, and composite For ore and iron-containing waste, TFe≥90% metallic iron or even granular iron products can be obtained after reduction, which enables the sustainable development of refractory ore resources, but the production line still occupies a large area, the production line operation is still cumbersome, and the reduction time is still It takes 7h to 9h, the investment scale is also large, and the reduction process is complicated. Therefore, this tankless reduction kiln needs to be further improved and optimized
[0007] The coal-based one-step rotary kiln process technology is gradually mature and the operating cost is low, and it is gradually being promoted. However, it has strict requirements for reducing coal. Granular high-quality long-flame coal and lignite must be used as reducing agents. The operation is difficult and the investment scale is relatively small. Larger, the annual production capacity of a single production line is less than 200,000 tons; the coal-based two-step rotary kiln process technology is gradually mature, but there is a shortage of rich massive iron ore. High-grade oxidized pellets are used, and the production and operation costs are high. Suitable for our national conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for producing metallized pellets by direct reduction of sensible heat of high-temperature oxidation pellets
  • A method for producing metallized pellets by direct reduction of sensible heat of high-temperature oxidation pellets
  • A method for producing metallized pellets by direct reduction of sensible heat of high-temperature oxidation pellets

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] A method for producing metallized pellets by direct reduction of sensible heat of high-temperature oxidation pellets, the steps are as follows:

[0055] (1) Take the magnetite powder of Liaoning Chaoyang grade TFe: 68.2% with a fineness of -200 mesh accounting for 80%, mix with sodium humate adding 2.0% of iron ore powder weight, moisten and grind, pelletize, and pelletize the particle size ¢8~¢16mm, dried in a muffle furnace at 105°C for 4 hours, rapidly raised to 1200°C in an oxidized pellet rotary kiln, and continued sintering for 18 minutes to obtain 1200°C high-temperature oxidized pellets;

[0056] (2) get the high-temperature oxidation pellet of step (1), add the anthracite of high-temperature oxidation pellet weight 45%, particle size 0-15mm (its chemical composition is that fixed carbon is 69.12%, ash content is 15.14% by mass percentage, Volatile content is 12.6%, S is 2.14%), after mixing, preheat at 800°C for 20 minutes, add to the flame-insulated deep reduc...

Embodiment 2

[0058] A method for producing metallized pellets by direct reduction of sensible heat of high-temperature oxidation pellets, the steps are as follows:

[0059] (1) get fineness and be that -200 orders account for more than 80% iron ore powder of grade TFe:69.21% in Yanji City, Jilin Province, add anthracite coal, 2% water-soluble polyvinyl alcohol fine powder of iron ore powder weight 5%, Uniformly mixed and milled, water sprayed into pellets, the pellet size is ¢8~¢16mm, the pellets are dried in a muffle furnace at 105℃ for 4 hours, and the temperature is rapidly raised to 1230℃ in the rotary kiln for oxidation pellets, and sintering is continued for 15min. Obtain high temperature oxidation pellets at 1230°C;

[0060] (2) Get the 1230 DEG C high-temperature oxidation pellets of step (1), add anthracite with 40% high-temperature oxidation pellet weight and a particle size of 0-10mm (its chemical composition is 59.20% fixed carbon and 8.41% ash by mass percentage) %, volatile ...

Embodiment 3

[0062] (1) Take Liaoning Chaoyang grade TFe:70.02% magnetite powder with a fineness of -200 mesh accounting for 80%, mix it with starch syrup with 2.0% iron ore powder weight, moisten and grind, and pelletize. The pellet size is ¢ 8 to ¢16mm, dried in a muffle furnace at 105°C for 4 hours, rapidly raised to 1200°C in an oxidized pellet rotary kiln, and sintered for 18 minutes to obtain 1200°C high-temperature oxidized pellets;

[0063] (2) Get the 1200 ℃ high-temperature oxidation pellet of step (1), add the anthracite (its chemical composition is 69.12% by mass percent of fixed carbon, and ash content is 15.14% of high-temperature oxidation pellet weight 45%), particle size 0-15mm %, volatile matter 12.6%, S 2.14%), mixed and roasted at 1050°C for 20min, added to the rotary kiln for deep reduction of flame-trap type, and carried out deep reduction reaction at 1075°C for 3.0h, took out the pellets, and weighed 45% of the coal powder was added to cover and cool, and the coal ch...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of metallurgy, and in particular relates to a method for producing metallized pellets by direct reduction of sensible heat of high-temperature oxidized pellets. The present invention adopts a single chain grate-rotary kiln method to prepare high-temperature oxidized pellets, uses its sensible heat to directly carry out a reduction reaction with a reducing agent (coal), and then uses normal-temperature reduced coal for heat exchange and cooling, and after magnetic separation and separation, obtains Metallized pellet products and dried reducing agents (including retort coal char). The invention can recycle carbonized coal coke and reuse high-purity coal gas. The recovered carbonized coal coke can be used as a reducing agent again, and high-purity coal gas can be used for oxidation pellet rotary kiln and flame-trap type deep reduction rotary kiln. Energy, no additional heating energy is needed. The patent can reduce coal consumption by 40% to 60%, and the high-purity gas burned can reduce carbon emissions, which is energy-saving and environment-friendly.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, and in particular relates to a method for producing metallized pellets through direct reduction using sensible heat of high-temperature oxidation pellets. Background technique [0002] my country is a big country of iron and steel. In 2014, the steel output exceeded 1.126 billion tons (of which crude steel was 820 million tons), and the annual output of grate-rotary kiln method and sintering machine method oxidized pellets reached more than 2 billion tons; the amount of scrap steel ( Including DRI) there is a gap of 29 million tons per year, while the production of non-coking iron (direct reduced iron) products accounts for less than 1.0% of the world's production, with an annual production scale of less than 600,000 tons. As my country's coking coal reserves become increasingly poor and environmental protection problems become more and more serious, the state has introduced more relevant indus...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B5/10
Inventor 唐竹胜唐佳
Owner 泉州寰锋冶金技术有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products