Environmental protection type aqueous release film

A water-based release and environmental-friendly technology, applied in coatings, natural rubber coatings, polyurea/polyurethane coatings, etc., can solve the problems of high cost of solvent-based, low tensile properties, low peel strength, etc., to achieve uniform strength, Effect of improving flexibility, enhancing adhesion and flexibility

Inactive Publication Date: 2015-10-07
JIXIANGBAO TAICANG RELEASE MATERIAL TECH CO LTD
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Solvent type has high cost, high toxicity and serious pollution
Compared with the solvent type, the emulsion type has the characteristics of non-toxic, non-polluting, and low cost, but it also has some defects, such as low peel strength, low tensile properties, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] An environment-friendly water-based release film, comprising a film layer and a release layer positioned above the film layer, the release layer comprises the following components in proportion by weight:

[0040] 35 parts of water-based polyethylene wax emulsion; the water-based polyethylene wax emulsion of commercially available TI-201B can be selected for use;

[0041] 45 parts of water-based polyurethane emulsion; Bayer's U54 water-based polyurethane emulsion can be selected;

[0042] 20 parts of aqueous modified polyvinyl alcohol solution;

[0043] 5 parts of natural latex;

[0044] 3 parts of 3-aminopropyltriethoxysilane coupling agent;

[0045] 0.3 parts of defoamer S12;

[0046] Thickener methyl hydroxyethyl cellulose 0.3 part;

[0047] The weight ratio of the water-based modified polyvinyl alcohol solution includes the following components:

[0048] 100 parts of polyvinyl alcohol;

[0049] 700 parts of deionized water;

[0050] Modified calcium carbonate...

Embodiment 2

[0052] An environment-friendly water-based release film, comprising a film layer and a release layer positioned above the film layer, the release layer comprises the following components in proportion by weight:

[0053] 40 parts of water-based polyethylene wax emulsion; the water-based polyethylene wax emulsion of commercially available TI-201B can be selected for use;

[0054] 50 parts of water-based polyurethane emulsion; you can choose Bayer's U54 water-based polyurethane emulsion;

[0055] 25 parts of water-based modified polyvinyl alcohol solution;

[0056] 7.5 parts of natural latex;

[0057] 4 parts of 3-aminopropyltriethoxysilane coupling agent;

[0058] 0.4 parts of defoamer S12;

[0059] Thickener methyl hydroxyethyl cellulose 0.4 parts;

[0060] The weight ratio of the water-based modified polyvinyl alcohol solution includes the following components:

[0061] 100 parts of polyvinyl alcohol;

[0062] 750 parts of deionized water;

[0063] Modified calcium carbo...

Embodiment 3

[0065] An environment-friendly water-based release film, comprising a film layer and a release layer positioned above the film layer, the release layer comprises the following components in proportion by weight:

[0066] 45 parts of water-based polyethylene wax emulsion; the water-based polyethylene wax emulsion of commercially available TI-201B can be selected for use;

[0067] 55 parts of water-based polyurethane emulsion; you can choose Bayer's U54 water-based polyurethane emulsion;

[0068] 30 parts of aqueous modified polyvinyl alcohol solution;

[0069] 10 parts of natural latex;

[0070] 5 parts of 3-aminopropyltriethoxysilane coupling agent;

[0071] 0.5 parts of defoamer S12;

[0072] Thickener methyl hydroxyethyl cellulose 0.5 part;

[0073] The weight ratio of the water-based modified polyvinyl alcohol solution includes the following components:

[0074] 100 parts of polyvinyl alcohol;

[0075] 800 parts of deionized water;

[0076] Modified calcium carbonate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention provides an environmental protection type aqueous release film, which comprises a thin film layer and a release layer positioned on the thin film layer, wherein the release layer comprises, by weight, 35-45 parts of an aqueous polyethylene wax emulsion, 45-55 parts of an aqueous polyurethane emulsion, 20-30 parts of an aqueous modified polyvinyl alcohol solution, 5-10 parts of natural latex, 3-5 parts of a silane coupling agent, 0.3-0.5 part of a defoamer, and 0.3-0.5 part of a thickener, and the aqueous modified polyvinyl alcohol solution comprises, by weight, 100 parts of polyvinyl alcohol, 700-800 parts of deionized water, and 30-50 parts of modified calcium carbonate. The release film of the present invention is the aqueous environmental protection type release film, has characteristics of good peel strength and good stretching strength, and is the release film having the good comprehensive performance.

Description

technical field [0001] The invention relates to a release film, in particular to an environment-friendly water-based release film. Background technique [0002] Release film, also known as peeling film, isolation film, separation film, barrier film, release film, film, plastic film, hole masking film, silicone oil film, silicone oil paper, anti-adhesive film, slip film, Tianna paper, release film Paper, silliconfilm, release film, release. Usually, in order to increase the release force of the plastic film, the plastic film will be treated with plasma, or coated with fluorine, or coated with silicon (silicone) release agent on the surface of the film material, such as PET, PE, OPP, etc. ;It can show extremely light and stable release force for various organic pressure-sensitive adhesives (such as hot-melt adhesives, acrylic adhesives and rubber-based pressure-sensitive adhesives). [0003] Because the release film has the advantages of isolation, filling, protection, and e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J7/04C09D175/04C09D123/06C09D129/04C09D107/02C09D7/12
Inventor 於险峰
Owner JIXIANGBAO TAICANG RELEASE MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More