A kind of styrene-modified dicyclopentadiene petroleum resin and preparation method thereof

A technology of dicyclopentadiene and petroleum resin, which is applied in the field of petrochemical industry, can solve the problems of petroleum resin solubility and chromaticity difference, and achieve the effect of improving chromaticity, lowering temperature and preventing cross-linking reaction

Active Publication Date: 2017-04-05
安徽同心新材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome adopting styrene compounds to directly mix with crude dicyclopentadiene in the prior art, when carrying out thermopolymerization reaction modification, easily generate a large amount of insoluble polymers, the solubility and chromaticity of gained petroleum resin are comparatively low The shortcoming of the difference provides a kind of styrene-modified dicyclopentadiene petroleum resin and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of preparation method of the styrene-modified dicyclopentadiene petroleum resin of the present embodiment, its step is:

[0034] Step 1, mixing of reaction raw materials:

[0035] Mix high-purity cyclopentadiene monomer, styrene monomer and inert solvent to form a mixed solution. The mass parts of the three components in the mixed solution are: 30 parts of inert solvent, 30 parts of high-purity cyclopentadiene 60 parts of monomers, 25 parts of styrenic monomers; the high-purity cyclopentadiene monomer in the present embodiment is to be the dicyclopentadiene industrial product of commercially available mass percentage about 80% as raw material, it is added to In the bottom of an atmospheric rectification column with a theoretical plate number of 15, and the temperature of the bottom of the tower is heated to 200°C, and the fraction at 41-44°C is collected from the top of the tower at a reflux ratio of 2. The finally obtained high-purity cyclopentadiene monomer in...

Embodiment 2

[0042] A kind of preparation method of the styrene-modified dicyclopentadiene petroleum resin of the present embodiment, its step is:

[0043] Step 1, mixing of reaction raw materials:

[0044] Mix high-purity cyclopentadiene monomer, styrene-based monomer and inert solvent to form a mixed solution. The mass parts of the three components in the mixed solution are respectively: 46 parts of inert solvent, 46 parts of high-purity cyclopentadiene 45 parts of monomers, 18 parts of styrene monomers. The high-purity cyclopentadiene monomer in this example is based on the commercially available C9 industrial product as a raw material, which is added to an atmospheric rectification column with a theoretical plate number of 15, and the application number is CN200510025319 prepared by the process in the Chinese patent. The finally obtained high-purity cyclopentadiene monomer includes the following components in mass percentage: 99.2% cyclopentadiene, 0.71% dicyclopentadiene, and 0.09% ...

Embodiment 3

[0050] A kind of preparation method of the styrene-modified dicyclopentadiene petroleum resin of the present embodiment, its step is:

[0051] Step 1, mixing of reaction raw materials:

[0052] Mix high-purity cyclopentadiene monomer, styrene-based monomer and inert solvent to form a mixed solution. The mass parts of the three components in the mixed solution are respectively: 46 parts of inert solvent, 46 parts of high-purity cyclopentadiene 45 parts of monomers, 18 parts of styrene monomers. The high-purity cyclopentadiene monomer in this example is based on the commercially available C10 industrial product as raw material, which is added to an atmospheric rectification column with a theoretical plate number of 15, and the application number is CN200510025319 prepared by the process in the Chinese patent. The finally obtained high-purity cyclopentadiene monomer includes the following components in mass percentage: 99.7% cyclopentadiene, 0.26% dicyclopentadiene, and 0.04% o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses styrene modified dicyclopentadiene petroleum resin and a preparing method thereof and belongs to the technical field of petrochemical industry. The styrene modified dicyclopentadiene petroleum resin has a softening point 90 DEG C to 130 DEG C, Gardner color scale 4 to 5, weight-average molecular weight 400 to 1000, and molecular weight distribution index 1.5 to 2.5. The preparing method includes the steps of mixing of reaction materials, thermal polymerization reaction of the reaction materials, and purification of the reaction materials. The high-purity cyclopentadiene monomer and the styrene monomer are mixed; by adjusting the ratio of the components and strictly controlling various process parameters of thermal polymerization reaction, cross-linking in the thermal polarization process can be prevented, and the performances, such as solubility, color scale and compatibility with elastomers, of the styrene modified dicyclopentadiene petroleum resin are evidently improved.

Description

technical field [0001] The invention belongs to the field of petrochemical technology, and more specifically relates to a styrene-modified dicyclopentadiene petroleum resin and a preparation method thereof. Background technique [0002] Petroleum resin is a kind of thermoplastic resin polymerized from C5 and C9 fractions produced in the cracking process of ethylene as the main raw material. Among them, dicyclopentadiene petroleum resin is a resin made of dicyclopentadiene in the carbon five fraction as the main raw material. It has the advantages of cheap and easy-to-obtain raw materials, high softening point, strong rigidity, and high brightness, so it is widely used in Rubber mixing, ink additives, paint coatings and adhesives, etc., but its use is limited due to its shortcomings such as deep hue, poor adhesion, and poor compatibility with elastomer materials. scope. Therefore, the modification of dicyclopentadiene petroleum resin has become the focus of general attentio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F240/00C08F8/04
Inventor 郭书成张元张素芳陈洁张泽
Owner 安徽同心新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com