Application of volcanic used as titanium dioxide loaded photocatalyst

A photocatalyst, titanium dioxide technology, applied in physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, chemical instruments and methods, etc., to achieve the effect of mild conditions, high carrier strength, and small grains

Active Publication Date: 2015-04-29
山东默锐环境产业股份有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] However, there is currently no report on the application of volcanic rock as a titanium dioxide photocatalyst.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A preparation method of a titanium dioxide photocatalyst supported by volcanic rocks, comprising the steps of:

[0032] (1) Wash the volcanic rock with ultrasonic water at 22°C and ultrasonic frequency of 45kHz for 1h, then soak it in acetone and ethanol for 1h respectively, after filtering, wash the volcanic rock with clean water, dry at 80°C, and then put in 0.3mol / L Soak in NaOH solution for 3 hours, wash with water, and dry at 80°C to obtain a volcanic rock carrier;

[0033] (2) 24g Ti(SO 4 ) 2 Dissolve 24g urea in 1000ml water to prepare loading solution;

[0034] (3) Immerse 100g of the volcanic rock carrier prepared in step (1) in the load solution prepared in step (2), stir and mix evenly, heat to 70°C, and continuously add 0.1mol / L aqueous urea solution to control the reaction system. pH=5~7, keep warm for 2 hours, age for 24 hours, filter, dry at 70°C, then raise the temperature to 200°C at a rate of 2°C / min, keep it for 1 hour, then increase the temperatur...

Embodiment 2

[0037] A preparation method of a titanium dioxide photocatalyst supported by volcanic rocks, comprising the steps of:

[0038] (1) Wash the volcanic rock with ultrasonic water at 18°C ​​and ultrasonic frequency of 35kHz for 1h, then soak it in acetone and ethanol for 3h respectively, after filtering, wash the volcanic rock with clean water, dry at 80°C, and put in 0.1mol / L Soak in NaOH solution for 3 hours, wash with water, and dry at 80°C to obtain a volcanic rock carrier;

[0039] (2) 24g Ti(SO 4 ) 2 Dissolve 48g urea in 1000ml water to prepare loading solution;

[0040] (3) Immerse 100 g of the volcanic rock carrier prepared in step (1) in the loading solution prepared in step (2), stir and mix evenly, heat to 90° C., and continuously add dropwise 0.1mol / L aqueous urea solution to control the reaction system. pH=5~7, keep warm for 4 hours, age for 48 hours, filter, dry at 80°C, then raise the temperature to 200°C at a rate of 2°C / min, keep it for 1 hour, then increase th...

Embodiment 3

[0043] A preparation method of a titanium dioxide photocatalyst supported by volcanic rocks, comprising the steps of:

[0044] (1) Wash the volcanic rock with ultrasonic water at 20°C and ultrasonic frequency 40kHz for 1h, then soak it in acetone and ethanol for 2h respectively, after filtering, wash the volcanic rock with clean water, dry it at 80°C, and then put it into 0.1mol / L Soak in NaOH solution for 3 hours, wash with water, and dry at 80°C to obtain a volcanic rock carrier;

[0045] (2) 24g Ti(SO 4 ) 2 Dissolve 36g urea in 1000ml water to prepare loading solution;

[0046] (3) Immerse 100g of the volcanic rock carrier prepared in step (1) in the load solution prepared in step (2), stir and mix evenly, heat to 80°C, and continuously add 0.1mol / L aqueous urea solution to control the reaction system. pH=5~7, keep warm for 4 hours, age for 24 hours, filter, dry at 80°C, then raise the temperature to 200°C at a rate of 2°C / min, keep it for 1 hour, then increase the tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to application of a volcanic used as a titanium dioxide loaded photocatalyst. The application comprises the following steps: (1) removing impurities on the surface of the volcanic to prepare a volcanic carrier; (2) dissolving Ti(SO4)2 and urea into water according to proportions to prepare load solutions; (3) soaking the volcanic carrier into the load solutions for reacting, adding urea solutions or ammonia water in a reaction process; aging, filtering, drying and baking to prepare the volcanic loaded titanium dioxide photocatalyst. The volcanic is used as a carrier of the titanium dioxide photocatalyst, so that the intensity of the carrier is high, and the performance of the loaded photocatalyst can be improved to a certain extent; in addition, the carrier has a rich honeycomb porous structure, and is high in specific surface area and high in adsorption performance; because of the carrier of the photocatalyst, the load firmness and the photocatalytic performance of the loaded catalyst can be improved.

Description

technical field [0001] The invention relates to the application of volcanic rock as a titanium dioxide photocatalyst load, and belongs to the technical field of semiconductor photocatalytic functional materials. Background technique [0002] Since 1972, A.Fujishima and K.Honda published on n-type semiconductor TiO in Nature magazine 2 Since the article that photo-splitting of water can be carried out, semiconductor photocatalysis technology has become an emerging research discipline. As a new technology of pollution control, semiconductor heterogeneous photocatalysis has been paid more and more attention. [0003] The heterogeneous semiconductor photocatalytic technology can almost completely mineralize various organic and inorganic substances in wastewater into CO 2 、H 2 O and inorganic salts will not produce secondary pollution, achieve the purpose of controlling environmental pollution, and overcome the shortcomings of traditional phase transfer and filtration methods....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J23/889B01J21/06
Inventor 李建业杨建伟姜绍龙王立颖漆伶荣庞丽梅甄冠胜
Owner 山东默锐环境产业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap