A technology of anti-rust agent and iron and steel, which is applied in the field of anti-rust agent for iron and steel. It can solve the problems that the anti-rust agent is not very targeted and the anti-rust effect of steel products is not very ideal, and achieve the effect of significant anti-rust effect and strong pertinence
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0015] The iron and steel rust inhibitor is made of the following components: 1.0kg sodium gluconate, 0.3kg ammonium molybdate, 0.5kg boric acid, 0.5kg sodium benzoate, 0.8kg triethanolamine, 0.1kg sodium carbonate, 0.1kg fatty acid, acrylate emulsion 1.5kg and 4.5kg of water.
[0016] The preparation method is as follows: adding sodium gluconate, ammonium molybdate, boric acid, sodium benzoate, triethanolamine, sodium carbonate and fatty acid into water, stirring well, and then adding acrylate emulsion, stirring evenly.
Embodiment 2
[0018] This iron and steel rust inhibitor is made of the following components: 1.5kg sodium gluconate, 0.1kg ammonium molybdate, 0.1kg boric acid, 1.0kg sodium benzoate, 0.5kg triethanolamine, 0.2kg sodium carbonate, 0.05kg fatty acid, acrylate emulsion 2.0kg and water 3.0kg.
[0019] The preparation method is as follows: adding sodium gluconate, ammonium molybdate, boric acid, sodium benzoate, triethanolamine, sodium carbonate and fatty acid into water, stirring well, and then adding acrylate emulsion, stirring evenly.
Embodiment 3
[0021] This iron and steel rust inhibitor is made of the following components: 1.2kg sodium gluconate, 0.2kg ammonium molybdate, 0.4kg boric acid, 0.8kg sodium benzoate, 0.6kg triethanolamine, 0.15kg sodium carbonate, 0.08kg fatty acid, acrylate emulsion 1.6kg and 4.0kg of water.
[0022] The preparation method is as follows: adding sodium gluconate, ammonium molybdate, boric acid, sodium benzoate, triethanolamine, sodium carbonate and fatty acid into water, stirring well, and then adding acrylate emulsion, stirring evenly.
PUM
![No PUM](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com