A kind of aluminum alloy material and quenching treatment method

A technology of aluminum alloy material and quenching furnace, which is applied in the field of metal materials, can solve the problems of high material cost, impossibility of wide application, limited application range, etc., and achieve the effect of improving surface performance, convenient control of quenching process, and good effect

Active Publication Date: 2016-11-30
佛山市昌美铝业有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the material cost of this patent is high, and the application range is limited due to the high price, so it is impossible to be widely used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] An aluminum alloy material, the main component is aluminum, and the aluminum alloy material includes the following components: nickel, germanium, tin, copper, silicon, manganese, zinc, chromium and iron, and the weight percentages of each component are respectively:

[0050] Nickel: 0.02%, Germanium: 0.001%, Tin: 0.1%, Copper: 0.2%, Silicon: 0.3%, Manganese: 0.2%, Zinc: 0.03%, Chromium: 0.001%, Iron: 1.0%.

Embodiment 2

[0052] An aluminum alloy material, the main component is aluminum, and the aluminum alloy material includes the following components: nickel, germanium, tin, copper, silicon, manganese, zinc, chromium and iron, and the weight percentages of each component are respectively:

[0053] Nickel 0.2%, germanium: 0.01%, tin: 0.4%, copper: 1.5%, silicon 1.0%, manganese: 0.8%, zinc: 0.1%, chromium 0.01%, iron: 2.5%.

Embodiment 3

[0055] An aluminum alloy material, the main component is aluminum, and the aluminum alloy material includes the following components: nickel, germanium, tin, copper, silicon, manganese, zinc, chromium and iron, and the weight percentages of each component are respectively:

[0056] Nickel: 0.02%, Germanium: 0.001%, Tin: 0.1%, Copper: 0.2%, Silicon: 0.3%, Manganese: 0.2%, Zinc: 0.03%, Chromium: 0.001%, Iron: 1.0%.

[0057] The aluminum alloy material also includes gallium, and the weight percentage of the gallium is 0.001%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention relates to an aluminum alloy material and a quenching processing method. The aluminum alloy material uses aluminum as a main component and further comprises nickel, germanium, tin, copper, silicon, manganese, zinc, chromium and iron. The quenching processing method comprises the following steps: (1) preparing a cooling agent; (2) heating the surface of the aluminum alloy material; (3) quenching the surface of the aluminum alloy material; (4) cooling the aluminum alloy material. The aluminum alloy material disclosed by the invention has high flexibility and low rebound resilience and can meet the use requirements of more places; the surface of the aluminum alloy material is quenched, so that the surface performance of the aluminum alloy material is improved and the aluminum alloy material has a longer service life; the quenching method aiming at the aluminum alloy material disclosed by the invention has the advantages of low quenching cost, high convenience for controlling and good quenching effect and is beneficial to wide popularization and application.

Description

technical field [0001] The invention relates to an aluminum alloy material and a quenching treatment method, belonging to the field of metal materials. Background technique [0002] Aluminum is a pure white light metal with ductility, and its products are often made into rods, sheets, foils, powders, ribbons and filaments. In humid air, an oxide film can be formed to prevent metal corrosion. Aluminum powder and foil burn violently when heated in the air, emitting a blinding white flame. Soluble in dilute sulfuric acid, nitric acid, hydrochloric acid, sodium hydroxide and potassium hydroxide solution, insoluble in water. The content of aluminum in the earth's crust is second only to oxygen and silicon, ranking third, and is the most abundant metal element in the earth's crust. The development of the three important industries of aviation, construction, and automobile requires that the material properties have the unique properties of aluminum and its alloys, which greatly ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/00C22C21/02C22C21/18C22F1/04C22F1/043C22F1/057
CPCC22C21/00C22C21/02C22C21/14C22C21/18C22F1/002C22F1/04C22F1/043C22F1/057
Inventor 钱国东
Owner 佛山市昌美铝业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com